Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_194_5_2821578__25Ppo.cif"

There are 120 T-atoms per unit cell
There are 240 O-atoms per unit cell

Framework density = 17.83 T-atoms per nm^3
Material density = 1.779 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6295 Angstrom
T1  -- O2  = 1.6019 Angstrom
T1  -- O3  = 1.6331 Angstrom
T1  -- O4  = 1.6383 Angstrom
      mean = 1.6257 Angstrom
        t1 = 0.018829  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.010214  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6350 Angstrom
T2  -- O5  = 1.6298 Angstrom
T2  -- O6  = 1.6327 Angstrom
T2  -- O7  = 1.6124 Angstrom
      mean = 1.6275 Angstrom
        t1 = 0.015195  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.009868  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6279 Angstrom
T3  -- O8  = 1.6096 Angstrom
T3  -- O9  = 1.6041 Angstrom
T3  -- O10 = 1.6392 Angstrom
      mean = 1.6202 Angstrom
        t1 = 0.018599  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.016468  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6231 Angstrom
T4  -- O9  = 1.5967 Angstrom
T4  -- O11 = 1.6213 Angstrom
T4  -- O12 = 1.5856 Angstrom
      mean = 1.6067 Angstrom
        t1 = 0.012424  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.010489  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O12 = 1.5925 Angstrom
T5  -- O13 = 1.6277 Angstrom
T5  -- O14 = 1.6245 Angstrom
T5  -- O10 = 1.6415 Angstrom
      mean = 1.6216 Angstrom
        t1 = 0.012177  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008246  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5856 A <--> 1.6415 A
          Mean   = 1.6203 A
          StdDev = 0.0163 A

       t1 Range  = 0.0122 <-- 0.0154 --> 0.0188
       t2 Range  = 0.0082 <-- 0.0111 --> 0.0165

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.494 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.107 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 111.598 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 107.557 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 107.583 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 112.341 deg; O3  -- O4  = 3 A
       107.557 deg <-- 109.447 deg --> 112.341 deg

O3  -- T2  -- O5  = 110.372 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 110.677 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 106.701 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 110.269 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.686 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.059 deg; O6  -- O7  = 3 A
       106.701 deg <-- 109.461 deg --> 110.677 deg

O4  -- T3  -- O8  = 109.158 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 106.759 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 112.591 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 107.418 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 108.805 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 111.950 deg; O9  -- O10 = 3 A
       106.759 deg <-- 109.447 deg --> 112.591 deg

O7  -- T4  -- O9  = 111.134 deg; O7  -- O9  = 3 A
O7  -- T4  -- O11 = 109.702 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 108.734 deg; O7  -- O12 = 3 A
O9  -- T4  -- O11 = 110.346 deg; O9  -- O11 = 3 A
O9  -- T4  -- O12 = 107.254 deg; O9  -- O12 = 3 A
O11 -- T4  -- O12 = 109.618 deg; O11 -- O12 = 3 A
       107.254 deg <-- 109.464 deg --> 111.134 deg

O12 -- T5  -- O13 = 111.495 deg; O12 -- O13 = 3 A
O12 -- T5  -- O14 = 109.369 deg; O12 -- O14 = 3 A
O12 -- T5  -- O10 = 107.006 deg; O12 -- O10 = 3 A
O13 -- T5  -- O14 = 109.919 deg; O13 -- O14 = 3 A
O13 -- T5  -- O10 = 109.504 deg; O13 -- O10 = 3 A
O14 -- T5  -- O10 = 109.489 deg; O14 -- O10 = 3 A
       107.006 deg <-- 109.464 deg --> 111.495 deg

        O-T-O SUMMARY
          Range  = 106.7011 deg <--> 112.5912 deg
          Mean   = 109.4510 deg
          StdDev = 1.6598 deg

        O--O SUMMARY
          Range  = 2.5623 A <--> 2.7179 A
          Mean   = 2.6451 A
          StdDev = 0.0385 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.2707 A
T1  - O1  - T1  - O3  - T2  = 105.175 deg; T1  -- T2  = 4.6326 A
T1  - O1  - T1  - O4  - T3  = 154.411 deg; T1  -- T3  = 5.7380 A
T1  - O2  - T1  - O3  - T2  =  89.639 deg; T1  -- T2  = 4.3676 A
T1  - O2  - T1  - O4  - T3  = 109.989 deg; T1  -- T3  = 5.1166 A
T2  - O3  - T1  - O4  - T3  =  91.195 deg; T2  -- T3  = 4.3212 A

T1  - O3  - T2  - O5  - T2  =  90.361 deg; T1  -- T2  = 4.3676 A
T1  - O3  - T2  - O6  - T2  = 146.373 deg; T1  -- T2  = 5.8156 A
T1  - O3  - T2  - O7  - T4  =  88.970 deg; T1  -- T4  = 4.1406 A
T2  - O5  - T2  - O6  - T2  = 120.000 deg; T2  -- T2  = 5.4000 A
T2  - O5  - T2  - O7  - T4  = 119.113 deg; T2  -- T4  = 5.2332 A
T2  - O6  - T2  - O7  - T4  =  88.122 deg; T2  -- T4  = 4.1662 A

T1  - O4  - T3  - O8  - T3  = 113.550 deg; T1  -- T3  = 5.0871 A
T1  - O4  - T3  - O9  - T4  =  85.503 deg; T1  -- T4  = 4.1406 A
T1  - O4  - T3  - O10 - T5  = 137.552 deg; T1  -- T5  = 5.7215 A
T3  - O8  - T3  - O9  - T4  = 142.310 deg; T3  -- T4  = 5.7541 A
T3  - O8  - T3  - O10 - T5  =  89.907 deg; T3  -- T5  = 4.3229 A
T4  - O9  - T3  - O10 - T5  =  96.993 deg; T4  -- T5  = 4.5959 A

T2  - O7  - T4  - O9  - T3  =  92.914 deg; T2  -- T3  = 4.3212 A
T2  - O7  - T4  - O11 - T4  =  91.878 deg; T2  -- T4  = 4.1662 A
T2  - O7  - T4  - O12 - T5  = 110.048 deg; T2  -- T5  = 4.7402 A
T3  - O9  - T4  - O11 - T4  = 155.174 deg; T3  -- T4  = 5.7974 A
T3  - O9  - T4  - O12 - T5  = 109.753 deg; T3  -- T5  = 4.8459 A
T4  - O11 - T4  - O12 - T5  =  91.334 deg; T4  -- T5  = 4.1209 A

T4  - O12 - T5  - O13 - T5  = 122.178 deg; T4  -- T5  = 5.0796 A
T4  - O12 - T5  - O14 - T5  =  88.666 deg; T4  -- T5  = 4.1209 A
T4  - O12 - T5  - O10 - T3  = 116.849 deg; T4  -- T3  = 5.0803 A
T5  - O13 - T5  - O14 - T5  = 120.000 deg; T5  -- T5  = 5.1524 A
T5  - O13 - T5  - O10 - T3  = 112.393 deg; T5  -- T3  = 4.9997 A
T5  - O14 - T5  - O10 - T3  =  90.093 deg; T5  -- T3  = 4.3229 A

        T-T-T SUMMARY
          Range  = 85.5033 deg <--> 155.1744 deg
          Mean   = 108.6120 deg
          StdDev = 21.1849 deg

        T--T SUMMARY
          Range  = 4.1209 A <--> 5.8156 A
          Mean   = 4.7904 A
          StdDev = 0.5799 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 120.783 deg ; T1  -- T1   2.8334 A

T1  -- O2  -- T1  = 171.746 deg ; T1  -- T1   3.1954 A

T1  -- O3  -- T2  = 133.054 deg ; T1  -- T2   2.9977 A

T1  -- O4  -- T3  = 138.111 deg ; T1  -- T3   3.0504 A

T2  -- O5  -- T2  = 151.244 deg ; T2  -- T2   3.1576 A

T2  -- O6  -- T2  = 140.956 deg ; T2  -- T2   3.0776 A

T2  -- O7  -- T4  = 128.209 deg ; T2  -- T4   2.9107 A

T3  -- O8  -- T3  = 140.573 deg ; T3  -- T3   3.0308 A

T3  -- O9  -- T4  = 144.600 deg ; T3  -- T4   3.0492 A

T3  -- O10 -- T5  = 140.465 deg ; T3  -- T5   3.0874 A

T4  -- O11 -- T4  = 125.816 deg ; T4  -- T4   2.8868 A

T4  -- O12 -- T5  = 129.480 deg ; T4  -- T5   2.8743 A

T5  -- O13 -- T5  = 128.211 deg ; T5  -- T5   2.9285 A

T5  -- O14 -- T5  = 136.796 deg ; T5  -- T5   3.0207 A


        T-O-T SUMMARY
          Range  = 120.7832° <--> 171.7462 deg
          Mean   = 137.8603 deg
          StdDev = 12.3065 deg

        T--T SUMMARY
          Range  = 2.8334 A <--> 3.1954 A
          Mean   = 3.0072 A
          StdDev = 0.1043 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 24
Coordination Sequence =
    1 4 9 18 32 47 63 87 119 153 190 231 271 310 357 418 486
TD10 = 723
Circuit symbol = 4.4.4.8_{3}.6.6_{2}
Weight = 16
Vertex symbol  = 4.4.4.8.6.8
Weight = 21

T2 (Si): multiplicity = 24
Coordination Sequence =
    1 4 9 16 26 42 66 96 128 158 184 212 253 311 379 443 493
TD10 = 730
Circuit symbol = 4.4.4.6.6.6_{2}
Weight = 14
Vertex symbol  = 4.4.4.6.6.8
Weight = 19

T3 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 20 32 48 69 89 114 152 195 235 273 314 360 411 471
TD10 = 734
Circuit symbol = 4.4.6.8_{2}.6.8_{2}
Weight = 19
Vertex symbol  = 4.4.6.8.6.12
Weight = 27

T4 (Si): multiplicity = 24
Coordination Sequence =
    1 4 9 18 31 46 66 94 125 152 182 224 272 321 370 418 470
TD10 = 728
Circuit symbol = 4.4.4.6.6.6_{2}
Weight = 14
Vertex symbol  = 4.4.4.6.6.12
Weight = 23

T5 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 19 30 46 70 100 130 156 181 211 252 308 376 444 500
TD10 = 747
Circuit symbol = 4.6.4.6.6.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6
Weight = 19

<TD10> = 732.400
Average ring size = 5.2174