Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_194_5_2502379_MHIj4H.cif"

There are 120 T-atoms per unit cell
There are 240 O-atoms per unit cell

Framework density = 18.03 T-atoms per nm^3
Material density = 1.799 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6226 Angstrom
T1  -- O3  = 1.6181 Angstrom
T1  -- O2  = 1.6223 Angstrom
T1  -- O4  = 1.6198 Angstrom
      mean = 1.6207 Angstrom
        t1 = 0.006957  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002040  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6193 Angstrom
T2  -- O5  = 1.6217 Angstrom
T2  -- O6  = 1.6197 Angstrom
T2  -- O7  = 1.6190 Angstrom
      mean = 1.6199 Angstrom
        t1 = 0.006256  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000729  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6200 Angstrom
T3  -- O8  = 1.6172 Angstrom
T3  -- O9  = 1.6174 Angstrom
T3  -- O10 = 1.6228 Angstrom
      mean = 1.6194 Angstrom
        t1 = 0.006029  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001275  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O6  = 1.6207 Angstrom
T4  -- O10 = 1.6229 Angstrom
T4  -- O11 = 1.6206 Angstrom
T4  -- O12 = 1.6197 Angstrom
      mean = 1.6210 Angstrom
        t1 = 0.006931  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000824  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O7  = 1.6206 Angstrom
T5  -- O13 = 1.6219 Angstrom
T5  -- O14 = 1.6220 Angstrom
T5  -- O15 = 1.6178 Angstrom
      mean = 1.6206 Angstrom
        t1 = 0.006753  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001022  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6172 A <--> 1.6229 A
          Mean   = 1.6203 A
          StdDev = 0.0018 A

       t1 Range  = 0.0060 <-- 0.0066 --> 0.0070
       t2 Range  = 0.0007 <-- 0.0012 --> 0.0020

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O3  = 109.331 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 109.699 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 109.333 deg; O1  -- O4  = 3 A
O3  -- T1  -- O2  = 109.698 deg; O3  -- O2  = 3 A
O3  -- T1  -- O4  = 109.058 deg; O3  -- O4  = 3 A
O2  -- T1  -- O4  = 109.705 deg; O2  -- O4  = 3 A
       109.058 deg <-- 109.471 deg --> 109.705 deg

O3  -- T2  -- O5  = 109.232 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.584 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 109.767 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.596 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.234 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.414 deg; O6  -- O7  = 3 A
       109.232 deg <-- 109.471 deg --> 109.767 deg

O4  -- T3  -- O8  = 109.387 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 109.733 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 109.382 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 109.169 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.498 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.658 deg; O9  -- O10 = 3 A
       109.169 deg <-- 109.471 deg --> 109.733 deg

O6  -- T4  -- O10 = 109.696 deg; O6  -- O10 = 3 A
O6  -- T4  -- O11 = 109.489 deg; O6  -- O11 = 3 A
O6  -- T4  -- O12 = 109.146 deg; O6  -- O12 = 3 A
O10 -- T4  -- O11 = 109.485 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 109.450 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 109.561 deg; O11 -- O12 = 3 A
       109.146 deg <-- 109.471 deg --> 109.696 deg

O7  -- T5  -- O13 = 109.652 deg; O7  -- O13 = 3 A
O7  -- T5  -- O14 = 109.432 deg; O7  -- O14 = 3 A
O7  -- T5  -- O15 = 109.067 deg; O7  -- O15 = 3 A
O13 -- T5  -- O14 = 109.484 deg; O13 -- O14 = 3 A
O13 -- T5  -- O15 = 109.494 deg; O13 -- O15 = 3 A
O14 -- T5  -- O15 = 109.697 deg; O14 -- O15 = 3 A
       109.067 deg <-- 109.471 deg --> 109.697 deg

        O-T-O SUMMARY
          Range  = 109.0583 deg <--> 109.7669 deg
          Mean   = 109.4659 deg
          StdDev = 0.2040 deg

        O--O SUMMARY
          Range  = 2.6361 A <--> 2.6532 A
          Mean   = 2.6459 A
          StdDev = 0.0041 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O3  - T2  =  89.065 deg; T1  -- T2  = 4.2916 A
T1  - O1  - T1  - O2  - T1  = 148.709 deg; T1  -- T1  = 5.8267 A
T1  - O1  - T1  - O4  - T3  =  91.391 deg; T1  -- T3  = 4.3697 A
T2  - O3  - T1  - O2  - T1  =  98.859 deg; T2  -- T1  = 4.6061 A
T2  - O3  - T1  - O4  - T3  = 140.139 deg; T2  -- T3  = 5.7523 A
T1  - O2  - T1  - O4  - T3  = 101.085 deg; T1  -- T3  = 4.6715 A

T1  - O3  - T2  - O5  - T2  =  90.935 deg; T1  -- T2  = 4.2916 A
T1  - O3  - T2  - O6  - T4  = 108.509 deg; T1  -- T4  = 4.9496 A
T1  - O3  - T2  - O7  - T5  = 113.038 deg; T1  -- T5  = 5.0633 A
T2  - O5  - T2  - O6  - T4  = 154.548 deg; T2  -- T4  = 5.8385 A
T2  - O5  - T2  - O7  - T5  =  90.447 deg; T2  -- T5  = 4.2293 A
T4  - O6  - T2  - O7  - T5  =  96.528 deg; T4  -- T5  = 4.5048 A

T3  - O4  - T3  - O8  - T3  = 120.000 deg; T3  -- T3  = 5.5709 A
T3  - O4  - T3  - O9  - T4  =  88.466 deg; T3  -- T4  = 4.3673 A
T3  - O4  - T3  - O10 - T1  = 126.604 deg; T3  -- T1  = 5.6144 A
T3  - O8  - T3  - O9  - T4  = 124.195 deg; T3  -- T4  = 5.5043 A
T3  - O8  - T3  - O10 - T1  =  88.609 deg; T3  -- T1  = 4.3697 A
T4  - O9  - T3  - O10 - T1  = 112.719 deg; T4  -- T1  = 5.0608 A

T2  - O6  - T4  - O10 - T3  =  97.451 deg; T2  -- T3  = 4.5533 A
T2  - O6  - T4  - O11 - T4  = 110.127 deg; T2  -- T4  = 4.9705 A
T2  - O6  - T4  - O12 - T4  = 132.410 deg; T2  -- T4  = 5.5828 A
T3  - O10 - T4  - O11 - T4  = 140.649 deg; T3  -- T4  = 5.7033 A
T3  - O10 - T4  - O12 - T4  =  91.534 deg; T3  -- T4  = 4.3673 A
T4  - O11 - T4  - O12 - T4  =  90.000 deg; T4  -- T4  = 4.3134 A

T2  - O7  - T5  - O13 - T5  = 110.485 deg; T2  -- T5  = 4.9453 A
T2  - O7  - T5  - O14 - T5  =  89.553 deg; T2  -- T5  = 4.2293 A
T2  - O7  - T5  - O15 - T5  = 144.601 deg; T2  -- T5  = 5.8068 A
T5  - O13 - T5  - O14 - T5  =  90.000 deg; T5  -- T5  = 4.2533 A
T5  - O13 - T5  - O15 - T5  =  90.000 deg; T5  -- T5  = 4.3177 A
T5  - O14 - T5  - O15 - T5  = 120.000 deg; T5  -- T5  = 5.2751 A

        T-T-T SUMMARY
          Range  = 88.4661 deg <--> 154.5477 deg
          Mean   = 109.6002 deg
          StdDev = 20.3603 deg

        T--T SUMMARY
          Range  = 4.2293 A <--> 5.8385 A
          Mean   = 4.9057 A
          StdDev = 0.5772 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 134.937 deg ; T1  -- T1   2.9975 A

T1  -- O2  -- T1  = 140.467 deg ; T1  -- T1   3.0533 A

T1  -- O3  -- T2  = 142.551 deg ; T1  -- T2   3.0660 A

T1  -- O4  -- T3  = 140.867 deg ; T1  -- T3   3.0527 A

T2  -- O5  -- T2  = 131.179 deg ; T2  -- T2   2.9532 A

T2  -- O6  -- T4  = 138.710 deg ; T2  -- T4   3.0323 A

T2  -- O7  -- T5  = 136.067 deg ; T2  -- T5   3.0044 A

T3  -- O8  -- T3  = 174.755 deg ; T3  -- T3   3.2311 A

T3  -- O9  -- T3  = 163.558 deg ; T3  -- T3   3.2016 A

T3  -- O10 -- T4  = 137.609 deg ; T3  -- T4   3.0261 A

T4  -- O11 -- T4  = 138.491 deg ; T4  -- T4   3.0309 A

T4  -- O12 -- T4  = 142.680 deg ; T4  -- T4   3.0691 A

T5  -- O13 -- T5  = 136.704 deg ; T5  -- T5   3.0149 A

T5  -- O14 -- T5  = 135.283 deg ; T5  -- T5   3.0001 A

T5  -- O15 -- T5  = 145.604 deg ; T5  -- T5   3.0908 A


        T-O-T SUMMARY
          Range  = 131.1790° <--> 174.7553 deg
          Mean   = 142.6309 deg
          StdDev = 11.1715 deg

        T--T SUMMARY
          Range  = 2.9532 A <--> 3.2311 A
          Mean   = 3.0549 A
          StdDev = 0.0717 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 20 35 55 80 107 141 182 223 267 315 369 429 500 578
TD10 = 858
Circuit symbol = 4.5.4.5.6.7_{2}
Weight = 11
Vertex symbol  = 4.5.4.5.8.8
Weight = 19

T2 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 20 34 53 78 106 140 182 223 264 310 363 427 497 571
TD10 = 851
Circuit symbol = 4.5.4.6.6.7
Weight = 12
Vertex symbol  = 4.5.4.6.8.8_{2}
Weight = 20

T3 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 21 37 58 83 111 142 176 217 268 324 383 443 501 562
TD10 = 860
Circuit symbol = 4.4.5.6.7.7
Weight = 12
Vertex symbol  = 4.4.5.6.8_{2}.8_{2}
Weight = 28

T4 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 21 36 55 80 108 140 177 216 264 323 380 433 495 564
TD10 = 848
Circuit symbol = 4.5.4.6.6.7
Weight = 12
Vertex symbol  = 4.5.4.6.8.8
Weight = 21

T5 (Si): multiplicity = 24
Coordination Sequence =
    1 4 9 17 29 47 73 105 141 179 219 263 311 366 429 496 564
TD10 = 824
Circuit symbol = 4.4.4.8_{5}.6_{2}.6_{2}
Weight = 22
Vertex symbol  = 4.4.4.8_{2}.6.6
Weight = 22

<TD10> = 848.200
Average ring size = 5.4765