Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_194_5_2440654_AfOm4V.cif"

There are 120 T-atoms per unit cell
There are 240 O-atoms per unit cell

Framework density = 16.87 T-atoms per nm^3
Material density = 1.684 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6242 Angstrom
T1  -- O2  = 1.6200 Angstrom
T1  -- O3  = 1.6280 Angstrom
T1  -- O4  = 1.6168 Angstrom
      mean = 1.6222 Angstrom
        t1 = 0.008710  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005040  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6263 Angstrom
T2  -- O5  = 1.6244 Angstrom
T2  -- O6  = 1.6186 Angstrom
T2  -- O7  = 1.6244 Angstrom
      mean = 1.6234 Angstrom
        t1 = 0.008644  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002693  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6168 Angstrom
T3  -- O8  = 1.6152 Angstrom
T3  -- O9  = 1.6168 Angstrom
T3  -- O10 = 1.6178 Angstrom
      mean = 1.6167 Angstrom
        t1 = 0.004536  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001182  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O6  = 1.6175 Angstrom
T4  -- O9  = 1.6177 Angstrom
T4  -- O11 = 1.6192 Angstrom
T4  -- O12 = 1.6180 Angstrom
      mean = 1.6181 Angstrom
        t1 = 0.005273  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001056  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O7  = 1.6224 Angstrom
T5  -- O10 = 1.6177 Angstrom
T5  -- O13 = 1.6241 Angstrom
T5  -- O14 = 1.6201 Angstrom
      mean = 1.6211 Angstrom
        t1 = 0.007177  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002814  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6152 A <--> 1.6280 A
          Mean   = 1.6203 A
          StdDev = 0.0036 A

       t1 Range  = 0.0045 <-- 0.0069 --> 0.0087
       t2 Range  = 0.0011 <-- 0.0026 --> 0.0050

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.256 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.178 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.490 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.659 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.572 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.665 deg; O3  -- O4  = 3 A
       108.490 deg <-- 109.470 deg --> 110.178 deg

O3  -- T2  -- O5  = 109.741 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 108.990 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 109.733 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.640 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.359 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.365 deg; O6  -- O7  = 3 A
       108.990 deg <-- 109.471 deg --> 109.741 deg

O4  -- T3  -- O8  = 109.862 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 109.418 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 109.555 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 109.087 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.816 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.085 deg; O9  -- O10 = 3 A
       109.085 deg <-- 109.471 deg --> 109.862 deg

O6  -- T4  -- O9  = 109.744 deg; O6  -- O9  = 3 A
O6  -- T4  -- O11 = 109.542 deg; O6  -- O11 = 3 A
O6  -- T4  -- O12 = 109.016 deg; O6  -- O12 = 3 A
O9  -- T4  -- O11 = 109.279 deg; O9  -- O11 = 3 A
O9  -- T4  -- O12 = 109.611 deg; O9  -- O12 = 3 A
O11 -- T4  -- O12 = 109.636 deg; O11 -- O12 = 3 A
       109.016 deg <-- 109.471 deg --> 109.744 deg

O7  -- T5  -- O10 = 109.310 deg; O7  -- O10 = 3 A
O7  -- T5  -- O13 = 109.893 deg; O7  -- O13 = 3 A
O7  -- T5  -- O14 = 109.613 deg; O7  -- O14 = 3 A
O10 -- T5  -- O13 = 109.159 deg; O10 -- O13 = 3 A
O10 -- T5  -- O14 = 109.487 deg; O10 -- O14 = 3 A
O13 -- T5  -- O14 = 109.364 deg; O13 -- O14 = 3 A
       109.159 deg <-- 109.471 deg --> 109.893 deg

        O-T-O SUMMARY
          Range  = 108.4898 deg <--> 110.1785 deg
          Mean   = 109.4736 deg
          StdDev = 0.3383 deg

        O--O SUMMARY
          Range  = 2.6301 A <--> 2.6669 A
          Mean   = 2.6459 A
          StdDev = 0.0082 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 107.563 deg; T1  -- T2  = 4.9608 A
T1  - O1  - T1  - O3  - T1  = 145.876 deg; T1  -- T1  = 5.8375 A
T1  - O1  - T1  - O4  - T3  =  90.786 deg; T1  -- T3  = 4.3897 A
T2  - O2  - T1  - O3  - T1  = 102.333 deg; T2  -- T1  = 4.7197 A
T2  - O2  - T1  - O4  - T3  =  84.051 deg; T2  -- T3  = 4.0960 A
T1  - O3  - T1  - O4  - T3  = 108.537 deg; T1  -- T3  = 4.9321 A

T1  - O3  - T2  - O5  - T2  = 146.935 deg; T1  -- T2  = 5.8499 A
T1  - O3  - T2  - O6  - T4  = 111.177 deg; T1  -- T4  = 5.0391 A
T1  - O3  - T2  - O7  - T5  =  92.743 deg; T1  -- T5  = 4.4158 A
T2  - O5  - T2  - O6  - T4  =  89.593 deg; T2  -- T4  = 4.3042 A
T2  - O5  - T2  - O7  - T5  = 108.659 deg; T2  -- T5  = 4.9567 A
T4  - O6  - T2  - O7  - T5  = 101.195 deg; T4  -- T5  = 4.7191 A

T3  - O4  - T3  - O8  - T4  = 131.101 deg; T3  -- T4  = 5.6626 A
T3  - O4  - T3  - O9  - T1  =  89.214 deg; T3  -- T1  = 4.3897 A
T3  - O4  - T3  - O10 - T5  =  89.059 deg; T3  -- T5  = 4.3655 A
T4  - O8  - T3  - O9  - T1  = 107.910 deg; T4  -- T1  = 4.9365 A
T4  - O8  - T3  - O10 - T5  = 133.501 deg; T4  -- T5  = 5.5852 A
T1  - O9  - T3  - O10 - T5  =  92.584 deg; T1  -- T5  = 4.4158 A

T2  - O6  - T4  - O9  - T3  = 103.919 deg; T2  -- T3  = 4.8003 A
T2  - O6  - T4  - O11 - T4  =  90.407 deg; T2  -- T4  = 4.3042 A
T2  - O6  - T4  - O12 - T4  = 127.056 deg; T2  -- T4  = 5.5282 A
T3  - O9  - T4  - O11 - T4  = 138.892 deg; T3  -- T4  = 5.6609 A
T3  - O9  - T4  - O12 - T4  = 109.781 deg; T3  -- T4  = 5.0363 A
T4  - O11 - T4  - O12 - T4  =  90.000 deg; T4  -- T4  = 4.3327 A

T2  - O7  - T5  - O10 - T5  = 128.667 deg; T2  -- T5  = 5.4457 A
T2  - O7  - T5  - O13 - T5  = 107.723 deg; T2  -- T5  = 4.9525 A
T2  - O7  - T5  - O14 - T3  =  84.517 deg; T2  -- T3  = 4.0960 A
T5  - O10 - T5  - O13 - T5  = 120.000 deg; T5  -- T5  = 5.2607 A
T5  - O10 - T5  - O14 - T3  = 111.030 deg; T5  -- T3  = 4.9729 A
T5  - O13 - T5  - O14 - T3  =  90.941 deg; T5  -- T3  = 4.3655 A

        T-T-T SUMMARY
          Range  = 84.0510 deg <--> 146.9347 deg
          Mean   = 108.4736 deg
          StdDev = 18.4567 deg

        T--T SUMMARY
          Range  = 4.0960 A <--> 5.8499 A
          Mean   = 4.8948 A
          StdDev = 0.5283 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 135.639 deg ; T1  -- T1   3.0080 A

T1  -- O2  -- T1  = 145.970 deg ; T1  -- T1   3.0982 A

T1  -- O3  -- T2  = 139.263 deg ; T1  -- T2   3.0508 A

T1  -- O4  -- T3  = 143.130 deg ; T1  -- T3   3.0676 A

T2  -- O5  -- T2  = 139.853 deg ; T2  -- T2   3.0514 A

T2  -- O6  -- T4  = 141.726 deg ; T2  -- T4   3.0573 A

T2  -- O7  -- T5  = 139.892 deg ; T2  -- T5   3.0499 A

T3  -- O8  -- T3  = 160.142 deg ; T3  -- T3   3.1823 A

T3  -- O9  -- T4  = 139.819 deg ; T3  -- T4   3.0377 A

T3  -- O10 -- T5  = 140.069 deg ; T3  -- T5   3.0411 A

T4  -- O11 -- T4  = 136.516 deg ; T4  -- T4   3.0080 A

T4  -- O12 -- T4  = 149.011 deg ; T4  -- T4   3.1184 A

T5  -- O13 -- T5  = 134.169 deg ; T5  -- T5   2.9919 A

T5  -- O14 -- T5  = 144.073 deg ; T5  -- T5   3.0824 A


        T-O-T SUMMARY
          Range  = 134.1689° <--> 160.1416 deg
          Mean   = 142.0908 deg
          StdDev = 6.3139 deg

        T--T SUMMARY
          Range  = 2.9919 A <--> 3.1823 A
          Mean   = 3.0604 A
          StdDev = 0.0475 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 19 34 55 78 104 132 163 201 245 294 349 409 476 538
TD10 = 801
Circuit symbol = 4.5.4.7.5.6_{3}
Weight = 13
Vertex symbol  = 4.5.4.12_{2}.5.6_{2}
Weight = 29

T2 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 20 34 50 73 102 131 165 207 253 300 348 399 462 536
TD10 = 797
Circuit symbol = 4.4.5.8_{6}.6.7
Weight = 22
Vertex symbol  = 4.4.5.8_{4}.6.8_{2}
Weight = 23

T3 (Si): multiplicity = 24
Coordination Sequence =
    1 4 9 18 32 49 70 95 126 169 213 254 297 342 398 463 534
TD10 = 786
Circuit symbol = 4.5.4.6.4.7
Weight = 13
Vertex symbol  = 4.5.4.6.4.8
Weight = 18

T4 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 19 30 47 71 100 133 168 210 259 305 347 397 458 526
TD10 = 793
Circuit symbol = 4.5.4.6.6_{2}.7
Weight = 15
Vertex symbol  = 4.5.4.6.6.8
Weight = 20

T5 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 20 32 47 66 92 128 169 212 254 301 355 407 453 505
TD10 = 781
Circuit symbol = 4.6.4.6.6.6_{3}
Weight = 18
Vertex symbol  = 4.6.4.6.6.6_{2}
Weight = 18

<TD10> = 791.600
Average ring size = 5.4815