Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_194_3_2666_7h7Z3y.cif"

There are 48 T-atoms per unit cell
There are 96 O-atoms per unit cell

Framework density = 17.85 T-atoms per nm^3
Material density = 1.781 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6178 Angstrom
T1  -- O2  = 1.6118 Angstrom
T1  -- O3  = 1.6134 Angstrom
T1  -- O4  = 1.6263 Angstrom
      mean = 1.6173 Angstrom
        t1 = 0.005873  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002431  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6203 Angstrom
T2  -- O5  = 1.6149 Angstrom
T2  -- O3  = 1.6203 Angstrom
T2  -- O5  = 1.6149 Angstrom
      mean = 1.6176 Angstrom
        t1 = 0.007676  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004253  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6227 Angstrom
T3  -- O4  = 1.6227 Angstrom
T3  -- O6  = 1.6152 Angstrom
T3  -- O7  = 1.6187 Angstrom
      mean = 1.6198 Angstrom
        t1 = 0.006735  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002326  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6118 A <--> 1.6263 A
          Mean   = 1.6180 A
          StdDev = 0.0046 A

       t1 Range  = 0.0059 <-- 0.0068 --> 0.0077
       t2 Range  = 0.0023 <-- 0.0030 --> 0.0043

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.093 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.817 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.689 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.046 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.301 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.875 deg; O3  -- O4  = 3 A
       109.046 deg <-- 109.470 deg --> 109.875 deg

O3  -- T2  -- O5  = 108.688 deg; O3  -- O5  = 3 A
O3  -- T2  -- O3  = 108.722 deg; O3  -- O3  = 3 A
O3  -- T2  -- O5  = 110.858 deg; O3  -- O5  = 3 A
O5  -- T2  -- O3  = 110.858 deg; O5  -- O3  = 3 A
O5  -- T2  -- O5  = 109.032 deg; O5  -- O5  = 3 A
O3  -- T2  -- O5  = 108.688 deg; O3  -- O5  = 3 A
       108.688 deg <-- 109.474 deg --> 110.858 deg

O4  -- T3  -- O4  = 109.826 deg; O4  -- O4  = 3 A
O4  -- T3  -- O6  = 109.184 deg; O4  -- O6  = 3 A
O4  -- T3  -- O7  = 109.735 deg; O4  -- O7  = 3 A
O4  -- T3  -- O6  = 109.184 deg; O4  -- O6  = 3 A
O4  -- T3  -- O7  = 109.735 deg; O4  -- O7  = 3 A
O6  -- T3  -- O7  = 109.158 deg; O6  -- O7  = 3 A
       109.158 deg <-- 109.470 deg --> 109.826 deg

        O-T-O SUMMARY
          Range  = 108.6875 deg <--> 110.8579 deg
          Mean   = 109.5112 deg
          StdDev = 0.6462 deg

        O--O SUMMARY
          Range  = 2.6264 A <--> 2.6639 A
          Mean   = 2.6436 A
          StdDev = 0.0119 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 120.000 deg; T1  -- T1  = 5.5198 A
T1  - O1  - T1  - O3  - T2  = 114.345 deg; T1  -- T2  = 5.2303 A
T1  - O1  - T1  - O4  - T3  = 116.222 deg; T1  -- T3  = 5.2309 A
T1  - O2  - T1  - O3  - T2  =  89.953 deg; T1  -- T2  = 4.4474 A
T1  - O2  - T1  - O4  - T3  =  89.913 deg; T1  -- T3  = 4.4020 A
T2  - O3  - T1  - O4  - T3  = 120.987 deg; T2  -- T3  = 5.2888 A

T1  - O3  - T2  - O5  - T2  = 114.293 deg; T1  -- T2  = 5.2806 A
T1  - O3  - T2  - O3  - T2  =  90.047 deg; T1  -- T2  = 4.4474 A
T1  - O3  - T2  - O5  - T1  = 131.311 deg; T1  -- T1  = 5.5948 A
T2  - O5  - T2  - O3  - T2  = 120.000 deg; T2  -- T2  = 5.5684 A
T2  - O5  - T2  - O5  - T1  =  90.047 deg; T2  -- T1  = 4.4474 A
T2  - O3  - T2  - O5  - T1  = 114.293 deg; T2  -- T1  = 5.2806 A

T1  - O4  - T3  - O4  - T1  = 118.761 deg; T1  -- T1  = 5.1745 A
T1  - O4  - T3  - O6  - T3  = 116.125 deg; T1  -- T3  = 5.1768 A
T1  - O4  - T3  - O7  - T3  =  90.087 deg; T1  -- T3  = 4.4020 A
T1  - O4  - T3  - O6  - T3  = 116.125 deg; T1  -- T3  = 5.1768 A
T1  - O4  - T3  - O7  - T3  =  90.087 deg; T1  -- T3  = 4.4020 A
T3  - O6  - T3  - O7  - T3  = 120.000 deg; T3  -- T3  = 5.4601 A

        T-T-T SUMMARY
          Range  = 89.9134 deg <--> 131.3106 deg
          Mean   = 108.7737 deg
          StdDev = 13.9789 deg

        T--T SUMMARY
          Range  = 4.4020 A <--> 5.5948 A
          Mean   = 5.0125 A
          StdDev = 0.4401 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 154.142 deg ; T1  -- T1   3.1536 A

T1  -- O2  -- T1  = 174.518 deg ; T1  -- T1   3.2200 A

T1  -- O3  -- T2  = 143.427 deg ; T1  -- T2   3.0704 A

T1  -- O4  -- T3  = 135.442 deg ; T1  -- T3   3.0065 A

T2  -- O5  -- T2  = 169.032 deg ; T2  -- T2   3.2149 A

T3  -- O6  -- T3  = 167.410 deg ; T3  -- T3   3.2109 A

T3  -- O7  -- T3  = 145.725 deg ; T3  -- T3   3.0935 A


        T-O-T SUMMARY
          Range  = 135.4419° <--> 174.5178 deg
          Mean   = 154.2931 deg
          StdDev = 14.2851 deg

        T--T SUMMARY
          Range  = 3.0065 A <--> 3.2200 A
          Mean   = 3.1291 A
          StdDev = 0.0801 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 20 34 53 76 103 135 170 208 250 299 355 412 469 530
TD10 = 814
Circuit symbol = 4.6.4.6.6.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6
Weight = 19

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 34 54 78 104 134 168 210 256 302 352 406 470 538
TD10 = 817
Circuit symbol = 4.4.6.6.6.6
Weight = 19
Vertex symbol  = 4.4.6.6.6.6
Weight = 19

T3 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 34 54 78 104 134 168 210 256 302 352 406 470 538
TD10 = 817
Circuit symbol = 4.6.4.6.6.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6
Weight = 19

<TD10> = 815.500
Average ring size = 5.1429