Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_194_3_2006_xDsjdk.cif"

There are 60 T-atoms per unit cell
There are 120 O-atoms per unit cell

Framework density = 18.88 T-atoms per nm^3
Material density = 1.884 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6035 Angstrom
T1  -- O2  = 1.6365 Angstrom
T1  -- O3  = 1.6189 Angstrom
T1  -- O4  = 1.6063 Angstrom
      mean = 1.6163 Angstrom
        t1 = 0.036052  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.023479  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6136 Angstrom
T2  -- O5  = 1.6213 Angstrom
T2  -- O6  = 1.6145 Angstrom
T2  -- O7  = 1.6671 Angstrom
      mean = 1.6291 Angstrom
        t1 = 0.026785  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.027279  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O7  = 1.6379 Angstrom
T3  -- O7  = 1.6379 Angstrom
T3  -- O8  = 1.6570 Angstrom
T3  -- O9  = 1.6348 Angstrom
      mean = 1.6419 Angstrom
        t1 = 0.022122  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.009934  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6035 A <--> 1.6671 A
          Mean   = 1.6266 A
          StdDev = 0.0193 A

       t1 Range  = 0.0221 <-- 0.0283 --> 0.0361
       t2 Range  = 0.0099 <-- 0.0202 --> 0.0273

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 113.868 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 111.296 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  98.370 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 111.522 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.964 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 111.136 deg; O3  -- O4  = 3 A
       98.370 deg <-- 109.359 deg --> 113.868 deg

O4  -- T2  -- O5  = 107.153 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 105.171 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 114.442 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 110.032 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 110.351 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.525 deg; O6  -- O7  = 3 A
       105.171 deg <-- 109.446 deg --> 114.442 deg

O7  -- T3  -- O7  = 109.007 deg; O7  -- O7  = 3 A
O7  -- T3  -- O8  = 110.903 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 108.222 deg; O7  -- O9  = 3 A
O7  -- T3  -- O8  = 110.903 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 108.222 deg; O7  -- O9  = 3 A
O8  -- T3  -- O9  = 109.505 deg; O8  -- O9  = 3 A
       108.222 deg <-- 109.460 deg --> 110.903 deg

        O-T-O SUMMARY
          Range  = 98.3700 deg <--> 114.4416 deg
          Mean   = 109.1215 deg
          StdDev = 3.5785 deg

        O--O SUMMARY
          Range  = 2.4293 A <--> 2.7585 A
          Mean   = 2.6544 A
          StdDev = 0.0748 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.0130 A
T1  - O1  - T1  - O3  - T1  = 150.000 deg; T1  -- T1  = 5.4280 A
T1  - O1  - T1  - O4  - T2  =  90.567 deg; T1  -- T2  = 4.1936 A
T1  - O2  - T1  - O3  - T1  = 120.000 deg; T1  -- T1  = 5.1167 A
T1  - O2  - T1  - O4  - T2  =  89.559 deg; T1  -- T2  = 4.3484 A
T1  - O3  - T1  - O4  - T2  =  89.730 deg; T1  -- T2  = 4.3219 A

T1  - O4  - T2  - O5  - T2  =  90.441 deg; T1  -- T2  = 4.3484 A
T1  - O4  - T2  - O6  - T2  =  90.270 deg; T1  -- T2  = 4.3219 A
T1  - O4  - T2  - O7  - T3  = 126.099 deg; T1  -- T3  = 5.5919 A
T2  - O5  - T2  - O6  - T2  = 120.000 deg; T2  -- T2  = 5.0480 A
T2  - O5  - T2  - O7  - T3  = 132.493 deg; T2  -- T3  = 5.5021 A
T2  - O6  - T2  - O7  - T3  =  92.007 deg; T2  -- T3  = 4.3047 A

T2  - O7  - T3  - O7  - T2  =  73.552 deg; T2  -- T2  = 3.6900 A
T2  - O7  - T3  - O8  - T3  =  87.993 deg; T2  -- T3  = 4.3047 A
T2  - O7  - T3  - O9  - T3  = 135.277 deg; T2  -- T3  = 5.8911 A
T2  - O7  - T3  - O8  - T3  =  87.993 deg; T2  -- T3  = 4.3047 A
T2  - O7  - T3  - O9  - T3  = 135.277 deg; T2  -- T3  = 5.8911 A
T3  - O8  - T3  - O9  - T3  = 120.000 deg; T3  -- T3  = 5.5461 A

        T-T-T SUMMARY
          Range  = 73.5524 deg <--> 150.0000 deg
          Mean   = 104.3448 deg
          StdDev = 21.8776 deg

        T--T SUMMARY
          Range  = 3.6900 A <--> 5.8911 A
          Mean   = 4.7347 A
          StdDev = 0.6958 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 113.983 deg ; T1  -- T1   2.6894 A

T1  -- O2  -- T1  = 131.006 deg ; T1  -- T1   2.9784 A

T1  -- O3  -- T1  = 129.600 deg ; T1  -- T1   2.9297 A

T1  -- O4  -- T2  = 164.708 deg ; T1  -- T2   3.1913 A

T2  -- O5  -- T2  = 129.206 deg ; T2  -- T2   2.9293 A

T2  -- O6  -- T2  = 127.796 deg ; T2  -- T2   2.8996 A

T2  -- O7  -- T3  = 137.629 deg ; T2  -- T3   3.0817 A

T3  -- O8  -- T3  = 165.663 deg ; T3  -- T3   3.2879 A

T3  -- O9  -- T3  = 144.673 deg ; T3  -- T3   3.1154 A


        T-O-T SUMMARY
          Range  = 113.9834° <--> 165.6631 deg
          Mean   = 136.1370 deg
          StdDev = 15.7265 deg

        T--T SUMMARY
          Range  = 2.6894 A <--> 3.2879 A
          Mean   = 2.9876 A
          StdDev = 0.1613 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.6894 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 24
Coordination Sequence =
    1 4 9 17 29 46 68 93 120 150 185 224 265 309 358 413 473
TD10 = 722
Circuit symbol = 4.4.4.8_{3}.6.6_{2}
Weight = 16
Vertex symbol  = 4.4.4.8.6.8
Weight = 21

T2 (Si): multiplicity = 24
Coordination Sequence =
    1 4 9 17 30 49 71 91 113 146 190 233 265 299 353 423 488
TD10 = 721
Circuit symbol = 4.4.4.6.6.6_{2}
Weight = 14
Vertex symbol  = 4.4.4.6.6.8
Weight = 19

T3 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 32 46 64 88 118 148 178 216 266 322 370 410 460
TD10 = 709
Circuit symbol = 4.8_{2}.4.8_{2}.6.6_{2}
Weight = 23
Vertex symbol  = 4.8.4.8.6.6
Weight = 23

<TD10> = 719.000
Average ring size = 5.1429