Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_194_2_58p_ceHIxF.cif"

There are 36 T-atoms per unit cell
There are 72 O-atoms per unit cell

Framework density = 16.11 T-atoms per nm^3
Material density = 1.607 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6156 Angstrom
T1  -- O2  = 1.6203 Angstrom
T1  -- O3  = 1.6204 Angstrom
T1  -- O4  = 1.6151 Angstrom
      mean = 1.6179 Angstrom
        t1 = 0.005942  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002297  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6153 Angstrom
T2  -- O4  = 1.6153 Angstrom
T2  -- O5  = 1.6126 Angstrom
T2  -- O6  = 1.6215 Angstrom
      mean = 1.6162 Angstrom
        t1 = 0.006200  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005307  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6126 A <--> 1.6215 A
          Mean   = 1.6173 A
          StdDev = 0.0029 A

       t1 Range  = 0.0059 <-- 0.0061 --> 0.0062
       t2 Range  = 0.0023 <-- 0.0038 --> 0.0053

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.810 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.666 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.551 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.630 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.796 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.369 deg; O3  -- O4  = 3 A
       108.551 deg <-- 109.470 deg --> 109.810 deg

O4  -- T2  -- O4  = 109.983 deg; O4  -- O4  = 3 A
O4  -- T2  -- O5  = 108.586 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.913 deg; O4  -- O6  = 3 A
O4  -- T2  -- O5  = 108.586 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.913 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 109.830 deg; O5  -- O6  = 3 A
       108.586 deg <-- 109.469 deg --> 109.983 deg

        O-T-O SUMMARY
          Range  = 108.5510 deg <--> 109.9828 deg
          Mean   = 109.4061 deg
          StdDev = 0.5796 deg

        O--O SUMMARY
          Range  = 2.6211 A <--> 2.6501 A
          Mean   = 2.6391 A
          StdDev = 0.0119 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  90.096 deg; T1  -- T2  = 4.3562 A
T1  - O1  - T1  - O3  - T1  = 120.000 deg; T1  -- T1  = 5.2578 A
T1  - O1  - T1  - O4  - T1  =  90.155 deg; T1  -- T1  = 4.3522 A
T2  - O2  - T1  - O3  - T1  = 127.902 deg; T2  -- T1  = 5.5448 A
T2  - O2  - T1  - O4  - T1  = 134.829 deg; T2  -- T1  = 5.7673 A
T1  - O3  - T1  - O4  - T1  =  89.845 deg; T1  -- T1  = 4.3522 A

T1  - O4  - T2  - O4  - T1  =  89.479 deg; T1  -- T1  = 4.4028 A
T1  - O4  - T2  - O5  - T2  = 128.024 deg; T1  -- T2  = 5.6634 A
T1  - O4  - T2  - O6  - T2  =  89.904 deg; T1  -- T2  = 4.3562 A
T1  - O4  - T2  - O5  - T2  = 128.024 deg; T1  -- T2  = 5.6634 A
T1  - O4  - T2  - O6  - T2  =  89.904 deg; T1  -- T2  = 4.3562 A
T2  - O5  - T2  - O6  - T2  = 120.000 deg; T2  -- T2  = 5.3789 A

        T-T-T SUMMARY
          Range  = 89.4790 deg <--> 134.8285 deg
          Mean   = 106.5807 deg
          StdDev = 19.2949 deg

        T--T SUMMARY
          Range  = 4.3522 A <--> 5.7673 A
          Mean   = 4.9064 A
          StdDev = 0.6284 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 149.675 deg ; T1  -- T1   3.1188 A

T1  -- O2  -- T1  = 138.189 deg ; T1  -- T1   3.0271 A

T1  -- O3  -- T1  = 139.869 deg ; T1  -- T1   3.0440 A

T1  -- O4  -- T2  = 150.997 deg ; T1  -- T2   3.1275 A

T2  -- O5  -- T2  = 159.335 deg ; T2  -- T2   3.1729 A

T2  -- O6  -- T2  = 138.996 deg ; T2  -- T2   3.0376 A


        T-O-T SUMMARY
          Range  = 138.1895° <--> 159.3354 deg
          Mean   = 145.5794 deg
          StdDev = 7.0955 deg

        T--T SUMMARY
          Range  = 3.0271 A <--> 3.1729 A
          Mean   = 3.0845 A
          StdDev = 0.0511 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 24
Coordination Sequence =
    1 4 9 17 30 50 75 98 118 144 185 238 288 326 360 408 479
TD10 = 731
Circuit symbol = 4.4.4.6.6.6_{2}
Weight = 14
Vertex symbol  = 4.4.4.6.6.8
Weight = 19

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 32 46 64 90 126 164 196 222 258 316 384 444 488
TD10 = 753
Circuit symbol = 4.8_{2}.4.8_{2}.6.6_{2}
Weight = 23
Vertex symbol  = 4.8.4.8.6.6
Weight = 23

<TD10> = 738.333
Average ring size = 5.1429