Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_193_2_2142_JGpB8z.cif"

There are 36 T-atoms per unit cell
There are 72 O-atoms per unit cell

Framework density = 20.08 T-atoms per nm^3
Material density = 2.003 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6198 Angstrom
T1  -- O2  = 1.6223 Angstrom
T1  -- O3  = 1.6203 Angstrom
T1  -- O4  = 1.6140 Angstrom
      mean = 1.6191 Angstrom
        t1 = 0.006342  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001850  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6184 Angstrom
T2  -- O4  = 1.6184 Angstrom
T2  -- O5  = 1.6233 Angstrom
T2  -- O5  = 1.6246 Angstrom
      mean = 1.6212 Angstrom
        t1 = 0.007449  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002623  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6140 A <--> 1.6246 A
          Mean   = 1.6198 A
          StdDev = 0.0032 A

       t1 Range  = 0.0063 <-- 0.0069 --> 0.0074
       t2 Range  = 0.0018 <-- 0.0022 --> 0.0026

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.683 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.275 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 108.965 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.654 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.031 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.214 deg; O3  -- O4  = 3 A
       108.965 deg <-- 109.470 deg --> 110.031 deg

O4  -- T2  -- O4  = 109.896 deg; O4  -- O4  = 3 A
O4  -- T2  -- O5  = 110.006 deg; O4  -- O5  = 3 A
O4  -- T2  -- O5  = 109.227 deg; O4  -- O5  = 3 A
O4  -- T2  -- O5  = 110.006 deg; O4  -- O5  = 3 A
O4  -- T2  -- O5  = 109.227 deg; O4  -- O5  = 3 A
O5  -- T2  -- O5  = 108.451 deg; O5  -- O5  = 3 A
       108.451 deg <-- 109.469 deg --> 110.006 deg

        O-T-O SUMMARY
          Range  = 108.4511 deg <--> 110.0306 deg
          Mean   = 109.5103 deg
          StdDev = 0.4558 deg

        O--O SUMMARY
          Range  = 2.6322 A <--> 2.6556 A
          Mean   = 2.6458 A
          StdDev = 0.0078 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 116.060 deg; T1  -- T2  = 5.1676 A
T1  - O1  - T1  - O3  - T1  = 120.000 deg; T1  -- T1  = 5.1584 A
T1  - O1  - T1  - O4  - T1  =  89.687 deg; T1  -- T1  = 4.2901 A
T2  - O2  - T1  - O3  - T1  = 103.759 deg; T2  -- T1  = 4.7662 A
T2  - O2  - T1  - O4  - T1  = 136.662 deg; T2  -- T1  = 5.7472 A
T1  - O3  - T1  - O4  - T1  =  90.313 deg; T1  -- T1  = 4.2901 A

T1  - O4  - T2  - O4  - T1  =  93.204 deg; T1  -- T1  = 4.4992 A
T1  - O4  - T2  - O5  - T2  = 132.904 deg; T1  -- T2  = 5.5538 A
T1  - O4  - T2  - O5  - T2  = 114.881 deg; T1  -- T2  = 5.1064 A
T1  - O4  - T2  - O5  - T2  = 132.904 deg; T1  -- T2  = 5.5538 A
T1  - O4  - T2  - O5  - T2  = 114.881 deg; T1  -- T2  = 5.1064 A
T2  - O5  - T2  - O5  - T2  =  60.000 deg; T2  -- T2  = 2.9619 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 136.6619 deg
          Mean   = 110.5345 deg
          StdDev = 20.5977 deg

        T--T SUMMARY
          Range  = 2.9619 A <--> 5.7472 A
          Mean   = 4.9174 A
          StdDev = 0.6734 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 144.804 deg ; T1  -- T1   3.0881 A

T1  -- O2  -- T1  = 134.758 deg ; T1  -- T1   2.9951 A

T1  -- O3  -- T1  = 132.076 deg ; T1  -- T1   2.9613 A

T1  -- O4  -- T2  = 146.602 deg ; T1  -- T2   3.0961 A

T2  -- O5  -- T2  = 131.549 deg ; T2  -- T2   2.9619 A


        T-O-T SUMMARY
          Range  = 131.5490° <--> 146.6018 deg
          Mean   = 138.6700 deg
          StdDev = 6.4361 deg

        T--T SUMMARY
          Range  = 2.9613 A <--> 3.0961 A
          Mean   = 3.0270 A
          StdDev = 0.0598 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 21 38 62 89 114 143 184 238 294 340 383 441 523 612
TD10 = 904
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 24
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 24

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 24 40 54 80 120 156 196 228 266 330 410 472 524 576
TD10 = 913
Circuit symbol = 3.6_{2}.8_{3}.8_{3}.8_{3}.8_{3}
Weight = 33
Vertex symbol  = 3.6_{2}.8_{3}.8_{3}.8_{3}.8_{3}
Weight = 33

<TD10> = 907.000
Average ring size = 6.2143