Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_193_2_1971_EjJOBy.cif"

There are 36 T-atoms per unit cell
There are 72 O-atoms per unit cell

Framework density = 18.75 T-atoms per nm^3
Material density = 1.871 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6158 Angstrom
T1  -- O2  = 1.6195 Angstrom
T1  -- O3  = 1.6193 Angstrom
T1  -- O4  = 1.6137 Angstrom
      mean = 1.6171 Angstrom
        t1 = 0.004632  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001000  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6194 Angstrom
T2  -- O5  = 1.6243 Angstrom
T2  -- O5  = 1.6243 Angstrom
T2  -- O4  = 1.6194 Angstrom
      mean = 1.6218 Angstrom
        t1 = 0.008202  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002371  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6137 A <--> 1.6243 A
          Mean   = 1.6187 A
          StdDev = 0.0033 A

       t1 Range  = 0.0046 <-- 0.0064 --> 0.0082
       t2 Range  = 0.0010 <-- 0.0017 --> 0.0024

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.525 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.523 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.220 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.509 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.528 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.522 deg; O3  -- O4  = 3 A
       109.220 deg <-- 109.471 deg --> 109.528 deg

O4  -- T2  -- O5  = 109.406 deg; O4  -- O5  = 3 A
O4  -- T2  -- O5  = 109.406 deg; O4  -- O5  = 3 A
O4  -- T2  -- O4  = 110.874 deg; O4  -- O4  = 3 A
O5  -- T2  -- O5  = 108.299 deg; O5  -- O5  = 3 A
O5  -- T2  -- O4  = 109.406 deg; O5  -- O4  = 3 A
O5  -- T2  -- O4  = 109.406 deg; O5  -- O4  = 3 A
       108.299 deg <-- 109.466 deg --> 110.874 deg

        O-T-O SUMMARY
          Range  = 108.2990 deg <--> 110.8744 deg
          Mean   = 109.5196 deg
          StdDev = 0.5228 deg

        O--O SUMMARY
          Range  = 2.6327 A <--> 2.6671 A
          Mean   = 2.6452 A
          StdDev = 0.0088 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.4604 A
T1  - O1  - T1  - O3  - T2  = 128.919 deg; T1  -- T2  = 5.7080 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.4624 A
T1  - O2  - T1  - O3  - T2  = 112.908 deg; T1  -- T2  = 5.1495 A
T1  - O2  - T1  - O4  - T1  = 120.000 deg; T1  -- T1  = 5.3364 A
T2  - O3  - T1  - O4  - T1  = 112.879 deg; T2  -- T1  = 5.1510 A

T1  - O4  - T2  - O5  - T2  = 132.371 deg; T1  -- T2  = 5.5474 A
T1  - O4  - T2  - O5  - T2  = 132.351 deg; T1  -- T2  = 5.5470 A
T1  - O4  - T2  - O4  - T1  =  77.837 deg; T1  -- T1  = 3.8938 A
T2  - O5  - T2  - O5  - T2  =  60.000 deg; T2  -- T2  = 2.9643 A
T2  - O5  - T2  - O4  - T1  = 132.351 deg; T2  -- T1  = 5.5470 A
T2  - O5  - T2  - O4  - T1  = 132.371 deg; T2  -- T1  = 5.5474 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 132.3712 deg
          Mean   = 112.6074 deg
          StdDev = 22.6481 deg

        T--T SUMMARY
          Range  = 2.9643 A <--> 5.7080 A
          Mean   = 5.0174 A
          StdDev = 0.7311 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 173.755 deg ; T1  -- T1   3.2268 A

T1  -- O2  -- T1  = 143.885 deg ; T1  -- T1   3.0795 A

T1  -- O3  -- T1  = 144.257 deg ; T1  -- T1   3.0823 A

T1  -- O4  -- T2  = 146.903 deg ; T1  -- T2   3.0991 A

T2  -- O5  -- T2  = 131.701 deg ; T2  -- T2   2.9643 A


        T-O-T SUMMARY
          Range  = 131.7010° <--> 173.7554 deg
          Mean   = 149.9225 deg
          StdDev = 13.4930 deg

        T--T SUMMARY
          Range  = 2.9643 A <--> 3.2268 A
          Mean   = 3.1044 A
          StdDev = 0.0763 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 21 38 62 89 114 143 184 238 294 340 383 441 523 612
TD10 = 904
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 24
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 24

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 24 40 54 80 120 156 196 228 266 330 410 472 524 576
TD10 = 913
Circuit symbol = 3.6_{2}.8_{3}.8_{3}.8_{3}.8_{3}
Weight = 33
Vertex symbol  = 3.6_{2}.8_{3}.8_{3}.8_{3}.8_{3}
Weight = 33

<TD10> = 907.000
Average ring size = 6.2143