Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_193_2_1747_UanBts.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 20.74 T-atoms per nm^3
Material density = 2.070 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6211 Angstrom
T1  -- O2  = 1.6209 Angstrom
T1  -- O3  = 1.6211 Angstrom
T1  -- O4  = 1.6211 Angstrom
      mean = 1.6211 Angstrom
        t1 = 0.006875  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000354  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6213 Angstrom
T2  -- O4  = 1.6212 Angstrom
T2  -- O4  = 1.6213 Angstrom
T2  -- O5  = 1.6162 Angstrom
      mean = 1.6200 Angstrom
        t1 = 0.006228  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000423  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6162 A <--> 1.6213 A
          Mean   = 1.6208 A
          StdDev = 0.0012 A

       t1 Range  = 0.0062 <-- 0.0066 --> 0.0069
       t2 Range  = 0.0004 <-- 0.0004 --> 0.0004

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.486 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.545 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.482 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.452 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.413 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.450 deg; O3  -- O4  = 3 A
       109.413 deg <-- 109.471 deg --> 109.545 deg

O4  -- T2  -- O4  = 109.423 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 109.418 deg; O4  -- O4  = 3 A
O4  -- T2  -- O5  = 109.522 deg; O4  -- O5  = 3 A
O4  -- T2  -- O4  = 109.421 deg; O4  -- O4  = 3 A
O4  -- T2  -- O5  = 109.522 deg; O4  -- O5  = 3 A
O4  -- T2  -- O5  = 109.521 deg; O4  -- O5  = 3 A
       109.418 deg <-- 109.471 deg --> 109.522 deg

        O-T-O SUMMARY
          Range  = 109.4128 deg <--> 109.5448 deg
          Mean   = 109.4679 deg
          StdDev = 0.0461 deg

        O--O SUMMARY
          Range  = 2.6442 A <--> 2.6485 A
          Mean   = 2.6461 A
          StdDev = 0.0013 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.2863 A
T1  - O1  - T1  - O3  - T2  = 120.369 deg; T1  -- T2  = 5.2512 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.2907 A
T1  - O2  - T1  - O3  - T2  = 115.590 deg; T1  -- T2  = 5.1246 A
T1  - O2  - T1  - O4  - T1  = 120.000 deg; T1  -- T1  = 5.2584 A
T2  - O3  - T1  - O4  - T1  = 115.522 deg; T2  -- T1  = 5.1280 A

T1  - O4  - T2  - O4  - T1  =  96.696 deg; T1  -- T1  = 4.5183 A
T1  - O4  - T2  - O4  - T1  =  96.695 deg; T1  -- T1  = 4.5183 A
T1  - O4  - T2  - O5  - T2  = 120.369 deg; T1  -- T2  = 5.4288 A
T1  - O4  - T2  - O4  - T1  =  96.696 deg; T1  -- T1  = 4.5183 A
T1  - O4  - T2  - O5  - T2  = 120.370 deg; T1  -- T2  = 5.4287 A
T1  - O4  - T2  - O5  - T2  = 120.369 deg; T1  -- T2  = 5.4288 A

        T-T-T SUMMARY
          Range  = 90.0000 deg <--> 120.3699 deg
          Mean   = 108.5425 deg
          StdDev = 12.4887 deg

        T--T SUMMARY
          Range  = 4.2863 A <--> 5.4288 A
          Mean   = 4.9380 A
          StdDev = 0.4468 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 138.198 deg ; T1  -- T1   3.0289 A

T1  -- O2  -- T1  = 138.624 deg ; T1  -- T1   3.0328 A

T1  -- O3  -- T1  = 139.217 deg ; T1  -- T1   3.0391 A

T1  -- O4  -- T2  = 137.658 deg ; T1  -- T2   3.0235 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2324 A


        T-O-T SUMMARY
          Range  = 137.6581° <--> 180.0000 deg
          Mean   = 141.6224 deg
          StdDev = 11.1460 deg

        T--T SUMMARY
          Range  = 3.0235 A <--> 3.2324 A
          Mean   = 3.0466 A
          StdDev = 0.0542 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 21 39 63 88 113 145 189 240 290 338 390 452 525 605
TD10 = 913
Circuit symbol = 4.6.4.6.6_{2}.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6_{2}
Weight = 19

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 25 38 55 84 121 158 193 228 274 338 406 468 529 590
TD10 = 919
Circuit symbol = 6_{2}.8_{4}.6_{2}.8_{4}.6_{2}.8_{4}
Weight = 30
Vertex symbol  = 6_{2}.8_{4}.6_{2}.8_{4}.6_{2}.8_{4}
Weight = 30

<TD10> = 914.500
Average ring size = 6.0000