Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_193_2_1745_wVNgkW.cif"

There are 32 T-atoms per unit cell
There are 64 O-atoms per unit cell

Framework density = 20.80 T-atoms per nm^3
Material density = 2.075 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6212 Angstrom
T1  -- O2  = 1.6216 Angstrom
T1  -- O3  = 1.6207 Angstrom
T1  -- O4  = 1.6215 Angstrom
      mean = 1.6212 Angstrom
        t1 = 0.006994  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000244  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6214 Angstrom
T2  -- O4  = 1.6213 Angstrom
T2  -- O4  = 1.6213 Angstrom
T2  -- O5  = 1.6152 Angstrom
      mean = 1.6198 Angstrom
        t1 = 0.006132  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000705  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6152 A <--> 1.6216 A
          Mean   = 1.6209 A
          StdDev = 0.0015 A

       t1 Range  = 0.0061 <-- 0.0066 --> 0.0070
       t2 Range  = 0.0002 <-- 0.0005 --> 0.0007

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.449 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.539 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.469 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.552 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.421 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.398 deg; O3  -- O4  = 3 A
       109.398 deg <-- 109.471 deg --> 109.552 deg

O4  -- T2  -- O4  = 109.447 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 109.444 deg; O4  -- O4  = 3 A
O4  -- T2  -- O5  = 109.495 deg; O4  -- O5  = 3 A
O4  -- T2  -- O4  = 109.449 deg; O4  -- O4  = 3 A
O4  -- T2  -- O5  = 109.496 deg; O4  -- O5  = 3 A
O4  -- T2  -- O5  = 109.496 deg; O4  -- O5  = 3 A
       109.444 deg <-- 109.471 deg --> 109.496 deg

        O-T-O SUMMARY
          Range  = 109.3980 deg <--> 109.5516 deg
          Mean   = 109.4652 deg
          StdDev = 0.0402 deg

        O--O SUMMARY
          Range  = 2.6430 A <--> 2.6486 A
          Mean   = 2.6460 A
          StdDev = 0.0020 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 115.608 deg; T1  -- T2  = 5.1029 A
T1  - O1  - T1  - O3  - T1  = 120.000 deg; T1  -- T1  = 5.2486 A
T1  - O1  - T1  - O4  - T1  =  90.432 deg; T1  -- T1  = 4.2833 A
T2  - O2  - T1  - O3  - T1  = 115.127 deg; T2  -- T1  = 5.1279 A
T2  - O2  - T1  - O4  - T1  = 121.032 deg; T2  -- T1  = 5.2665 A
T1  - O3  - T1  - O4  - T1  =  89.568 deg; T1  -- T1  = 4.2833 A

T1  - O4  - T2  - O4  - T1  =  95.813 deg; T1  -- T1  = 4.4860 A
T1  - O4  - T2  - O4  - T1  =  95.812 deg; T1  -- T1  = 4.4860 A
T1  - O4  - T2  - O5  - T2  = 121.035 deg; T1  -- T2  = 5.4444 A
T1  - O4  - T2  - O4  - T1  =  95.813 deg; T1  -- T1  = 4.4860 A
T1  - O4  - T2  - O5  - T2  = 121.036 deg; T1  -- T2  = 5.4443 A
T1  - O4  - T2  - O5  - T2  = 121.035 deg; T1  -- T2  = 5.4444 A

        T-T-T SUMMARY
          Range  = 89.5676 deg <--> 121.0363 deg
          Mean   = 107.3280 deg
          StdDev = 13.4615 deg

        T--T SUMMARY
          Range  = 4.2833 A <--> 5.4444 A
          Mean   = 4.8918 A
          StdDev = 0.4795 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 138.024 deg ; T1  -- T1   3.0273 A

T1  -- O2  -- T1  = 136.040 deg ; T1  -- T1   3.0074 A

T1  -- O3  -- T1  = 140.752 deg ; T1  -- T1   3.0531 A

T1  -- O4  -- T2  = 137.533 deg ; T1  -- T2   3.0227 A

T2  -- O5  -- T2  = 180.000 deg ; T2  -- T2   3.2304 A


        T-O-T SUMMARY
          Range  = 136.0403° <--> 180.0000 deg
          Mean   = 141.3112 deg
          StdDev = 11.3424 deg

        T--T SUMMARY
          Range  = 3.0074 A <--> 3.2304 A
          Mean   = 3.0432 A
          StdDev = 0.0566 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 21 39 63 88 113 145 189 240 290 338 390 452 525 605
TD10 = 913
Circuit symbol = 4.6.4.6.6_{2}.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6_{2}
Weight = 19

T2 (Si): multiplicity = 8
Coordination Sequence =
    1 4 12 25 38 55 84 121 158 193 228 274 338 406 468 529 590
TD10 = 919
Circuit symbol = 6_{2}.8_{4}.6_{2}.8_{4}.6_{2}.8_{4}
Weight = 30
Vertex symbol  = 6_{2}.8_{4}.6_{2}.8_{4}.6_{2}.8_{4}
Weight = 30

<TD10> = 914.500
Average ring size = 6.0000