Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_193_2_129_zVrnpI.cif"

There are 48 T-atoms per unit cell
There are 96 O-atoms per unit cell

Framework density = 15.23 T-atoms per nm^3
Material density = 1.520 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6252 Angstrom
T1  -- O1  = 1.6252 Angstrom
T1  -- O2  = 1.6239 Angstrom
T1  -- O3  = 1.6211 Angstrom
      mean = 1.6238 Angstrom
        t1 = 0.009197  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002143  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6222 Angstrom
T2  -- O4  = 1.6214 Angstrom
T2  -- O5  = 1.6215 Angstrom
T2  -- O6  = 1.6217 Angstrom
      mean = 1.6217 Angstrom
        t1 = 0.007276  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000396  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6211 A <--> 1.6252 A
          Mean   = 1.6228 A
          StdDev = 0.0016 A

       t1 Range  = 0.0073 <-- 0.0082 --> 0.0092
       t2 Range  = 0.0004 <-- 0.0013 --> 0.0021

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 108.244 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 109.336 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.824 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 109.327 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.835 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 110.241 deg; O2  -- O3  = 3 A
       108.244 deg <-- 109.468 deg --> 110.241 deg

O3  -- T2  -- O4  = 109.461 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.365 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.469 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 109.519 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.524 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 109.490 deg; O5  -- O6  = 3 A
       109.365 deg <-- 109.471 deg --> 109.524 deg

        O-T-O SUMMARY
          Range  = 108.2438 deg <--> 110.2411 deg
          Mean   = 109.4636 deg
          StdDev = 0.4799 deg

        O--O SUMMARY
          Range  = 2.6336 A <--> 2.6620 A
          Mean   = 2.6501 A
          StdDev = 0.0070 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T1  =  60.000 deg; T1  -- T1  = 2.9462 A
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.1581 A
T1  - O1  - T1  - O3  - T2  = 109.276 deg; T1  -- T2  = 4.8547 A
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.1581 A
T1  - O1  - T1  - O3  - T2  = 109.171 deg; T1  -- T2  = 4.8516 A
T1  - O2  - T1  - O3  - T2  = 157.654 deg; T1  -- T2  = 5.8283 A

T1  - O3  - T2  - O4  - T2  = 109.250 deg; T1  -- T2  = 4.9226 A
T1  - O3  - T2  - O5  - T2  =  98.823 deg; T1  -- T2  = 4.5973 A
T1  - O3  - T2  - O6  - T2  =  98.768 deg; T1  -- T2  = 4.5923 A
T2  - O4  - T2  - O5  - T2  =  90.000 deg; T2  -- T2  = 4.2975 A
T2  - O4  - T2  - O6  - T2  = 143.977 deg; T2  -- T2  = 5.7760 A
T2  - O5  - T2  - O6  - T2  = 107.970 deg; T2  -- T2  = 4.9261 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 157.6540 deg
          Mean   = 104.1825 deg
          StdDev = 24.4416 deg

        T--T SUMMARY
          Range  = 2.9462 A <--> 5.8283 A
          Mean   = 4.6104 A
          StdDev = 0.7354 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 130.030 deg ; T1  -- T1   2.9462 A

T1  -- O2  -- T1  = 129.232 deg ; T1  -- T1   2.9342 A

T1  -- O3  -- T2  = 135.958 deg ; T1  -- T2   3.0066 A

T2  -- O4  -- T2  = 139.968 deg ; T2  -- T2   3.0471 A

T2  -- O5  -- T2  = 139.555 deg ; T2  -- T2   3.0431 A

T2  -- O6  -- T2  = 138.254 deg ; T2  -- T2   3.0305 A


        T-O-T SUMMARY
          Range  = 129.2322° <--> 139.9677 deg
          Mean   = 135.4993 deg
          StdDev = 4.3626 deg

        T--T SUMMARY
          Range  = 2.9342 A <--> 3.0471 A
          Mean   = 3.0013 A
          StdDev = 0.0454 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 24
Coordination Sequence =
    1 4 8 14 26 44 62 91 121 144 181 222 272 326 368 410 469
TD10 = 696
Circuit symbol = 3.7_{2}.4.5.4.5
Weight = 11
Vertex symbol  = 3.8.4.5.4.5
Weight = 16

T2 (Si): multiplicity = 24
Coordination Sequence =
    1 4 11 19 29 47 67 91 121 153 188 227 271 317 367 426 481
TD10 = 731
Circuit symbol = 4.5.5.7.5.7
Weight = 12
Vertex symbol  = 4.5.5.8.5.12_{2}
Weight = 33

<TD10> = 713.500
Average ring size = 5.2000