Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_192_2_238385_6v5_la.cif"

There are 36 T-atoms per unit cell
There are 72 O-atoms per unit cell

Framework density = 18.70 T-atoms per nm^3
Material density = 1.866 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6173 Angstrom
T1  -- O1  = 1.6176 Angstrom
T1  -- O2  = 1.6155 Angstrom
T1  -- O3  = 1.6140 Angstrom
      mean = 1.6161 Angstrom
        t1 = 0.003999  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001231  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6196 Angstrom
T2  -- O4  = 1.6245 Angstrom
T2  -- O4  = 1.6249 Angstrom
T2  -- O3  = 1.6196 Angstrom
      mean = 1.6222 Angstrom
        t1 = 0.008569  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002616  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6140 A <--> 1.6249 A
          Mean   = 1.6181 A
          StdDev = 0.0034 A

       t1 Range  = 0.0040 <-- 0.0063 --> 0.0086
       t2 Range  = 0.0012 <-- 0.0019 --> 0.0026

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 109.333 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 109.687 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.360 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 109.692 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.405 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 109.350 deg; O2  -- O3  = 3 A
       109.333 deg <-- 109.471 deg --> 109.692 deg

O3  -- T2  -- O4  = 109.342 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 109.406 deg; O3  -- O4  = 3 A
O3  -- T2  -- O3  = 111.043 deg; O3  -- O3  = 3 A
O4  -- T2  -- O4  = 108.252 deg; O4  -- O4  = 3 A
O4  -- T2  -- O3  = 109.342 deg; O4  -- O3  = 3 A
O4  -- T2  -- O3  = 109.406 deg; O4  -- O3  = 3 A
       108.252 deg <-- 109.465 deg --> 111.043 deg

        O-T-O SUMMARY
          Range  = 108.2521 deg <--> 111.0430 deg
          Mean   = 109.5211 deg
          StdDev = 0.5426 deg

        O--O SUMMARY
          Range  = 2.6330 A <--> 2.6702 A
          Mean   = 2.6445 A
          StdDev = 0.0093 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T1  =  90.002 deg; T1  -- T1  = 4.4587 A
T1  - O1  - T1  - O2  - T2  = 112.777 deg; T1  -- T2  = 5.1503 A
T1  - O1  - T1  - O3  - T1  = 120.000 deg; T1  -- T1  = 5.3338 A
T1  - O1  - T1  - O2  - T2  = 129.318 deg; T1  -- T2  = 5.7203 A
T1  - O1  - T1  - O3  - T1  =  89.998 deg; T1  -- T1  = 4.4586 A
T2  - O2  - T1  - O3  - T1  = 112.736 deg; T2  -- T1  = 5.1491 A

T1  - O3  - T2  - O4  - T2  = 132.099 deg; T1  -- T2  = 5.5479 A
T1  - O3  - T2  - O4  - T2  = 132.034 deg; T1  -- T2  = 5.5465 A
T1  - O3  - T2  - O3  - T1  =  78.636 deg; T1  -- T1  = 3.9345 A
T2  - O4  - T2  - O4  - T2  =  60.000 deg; T2  -- T2  = 2.9656 A
T2  - O4  - T2  - O3  - T1  = 132.099 deg; T2  -- T1  = 5.5479 A
T2  - O4  - T2  - O3  - T1  = 132.034 deg; T2  -- T1  = 5.5465 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 132.0988 deg
          Mean   = 112.3247 deg
          StdDev = 21.7242 deg

        T--T SUMMARY
          Range  = 2.9656 A <--> 5.7203 A
          Mean   = 5.0328 A
          StdDev = 0.7023 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 144.326 deg ; T1  -- T1   3.0795 A

T1  -- O2  -- T1  = 172.586 deg ; T1  -- T1   3.2243 A

T1  -- O3  -- T2  = 147.535 deg ; T1  -- T2   3.1047 A

T2  -- O4  -- T2  = 131.748 deg ; T2  -- T2   2.9656 A


        T-O-T SUMMARY
          Range  = 131.7479° <--> 172.5860 deg
          Mean   = 151.5204 deg
          StdDev = 14.2968 deg

        T--T SUMMARY
          Range  = 2.9656 A <--> 3.2243 A
          Mean   = 3.1118 A
          StdDev = 0.0841 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 21 38 62 89 114 143 184 238 294 340 383 441 523 612
TD10 = 904
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 24
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 24

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 24 40 54 80 120 156 196 228 266 330 410 472 524 576
TD10 = 913
Circuit symbol = 3.6_{2}.8_{3}.8_{3}.8_{3}.8_{3}
Weight = 33
Vertex symbol  = 3.6_{2}.8_{3}.8_{3}.8_{3}.8_{3}
Weight = 33

<TD10> = 907.000
Average ring size = 6.2143