Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_191_5_267582_0TLRt5.cif"

There are 96 T-atoms per unit cell
There are 192 O-atoms per unit cell

Framework density = 25.64 T-atoms per nm^3
Material density = 2.559 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5326 Angstrom
T1  -- O2  = 1.7246 Angstrom
T1  -- O3  = 1.6991 Angstrom
T1  -- O4  = 1.5462 Angstrom
      mean = 1.6256 Angstrom
        t1 = 0.107744  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.080143  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.7916 Angstrom
T2  -- O5  = 1.7260 Angstrom
T2  -- O6  = 1.6730 Angstrom
T2  -- O7  = 1.8551 Angstrom
      mean = 1.7614 Angstrom
        t1 = 0.114461  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.042844  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6391 Angstrom
T3  -- O8  = 1.5529 Angstrom
T3  -- O9  = 1.5102 Angstrom
T3  -- O10 = 1.5753 Angstrom
      mean = 1.5694 Angstrom
        t1 = 0.060244  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.035909  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.7358 Angstrom
T4  -- O7  = 1.7358 Angstrom
T4  -- O11 = 1.5519 Angstrom
T4  -- O12 = 1.5430 Angstrom
      mean = 1.6416 Angstrom
        t1 = 0.121482  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.076676  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.5989 Angstrom
T5  -- O10 = 1.5989 Angstrom
T5  -- O13 = 1.8884 Angstrom
T5  -- O14 = 1.8574 Angstrom
      mean = 1.7359 Angstrom
        t1 = 0.164907  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.092833  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5102 A <--> 1.8884 A
          Mean   = 1.6613 A
          StdDev = 0.1131 A

       t1 Range  = 0.0602 <-- 0.1138 --> 0.1649
       t2 Range  = 0.0359 <-- 0.0657 --> 0.0928

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 100.081 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  =  98.989 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 118.430 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 139.394 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 110.174 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  91.267 deg; O3  -- O4  = 2 A
       91.267 deg <-- 109.722 deg --> 139.394 deg

O3  -- T2  -- O5  = 103.069 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 116.917 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 109.202 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 101.546 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 124.254 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 102.547 deg; O6  -- O7  = 3 A
       101.546 deg <-- 109.589 deg --> 124.254 deg

O4  -- T3  -- O8  = 107.724 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 110.707 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 121.539 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 104.613 deg; O8  -- O9  = 2 A
O8  -- T3  -- O10 = 110.931 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 =  99.952 deg; O9  -- O10 = 2 A
       99.952 deg <-- 109.244 deg --> 121.539 deg

O7  -- T4  -- O7  = 138.309 deg; O7  -- O7  = 3 A
O7  -- T4  -- O11 = 105.960 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 103.596 deg; O7  -- O12 = 3 A
O7  -- T4  -- O11 = 105.960 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 = 103.596 deg; O7  -- O12 = 3 A
O11 -- T4  -- O12 =  88.059 deg; O11 -- O12 = 2 A
       88.059 deg <-- 107.580 deg --> 138.309 deg

O10 -- T5  -- O10 =  81.673 deg; O10 -- O10 = 2 A
O10 -- T5  -- O13 = 107.662 deg; O10 -- O13 = 3 A
O10 -- T5  -- O14 = 104.095 deg; O10 -- O14 = 3 A
O10 -- T5  -- O13 = 107.662 deg; O10 -- O13 = 3 A
O10 -- T5  -- O14 = 104.095 deg; O10 -- O14 = 3 A
O13 -- T5  -- O14 = 137.581 deg; O13 -- O14 = 3 A
       81.673 deg <-- 107.128 deg --> 137.581 deg

        O-T-O SUMMARY
          Range  = 81.6726 deg <--> 139.3940 deg
          Mean   = 108.7863 deg
          StdDev = 12.4411 deg

        O--O SUMMARY
          Range  = 2.0910 A <--> 3.4921 A
          Mean   = 2.6992 A
          StdDev = 0.2740 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 122.645 deg ; T1  -- T1   2.6891 A

T1  -- O2  -- T1  = 104.171 deg ; T1  -- T1   2.7212 A

T1  -- O3  -- T2  = 131.937 deg ; T1  -- T2   3.1884 A

T1  -- O4  -- T3  =  91.455 deg ; T1  -- T3   2.2817 A

T2  -- O5  -- T2  = 126.278 deg ; T2  -- T2   3.0796 A

T2  -- O6  -- T2  = 133.266 deg ; T2  -- T2   3.0715 A

T2  -- O7  -- T4  = 168.398 deg ; T2  -- T4   3.5726 A

T3  -- O8  -- T3  = 128.883 deg ; T3  -- T3   2.8018 A

T3  -- O9  -- T3  = 135.239 deg ; T3  -- T3   2.7929 A

T3  -- O10 -- T5  = 136.146 deg ; T3  -- T5   2.9446 A

T4  -- O11 -- T4  = 118.233 deg ; T4  -- T4   2.6637 A

T4  -- O12 -- T4  = 117.889 deg ; T4  -- T4   2.6439 A

T5  -- O13 -- T5  = 164.997 deg ; T5  -- T5   3.7444 A

T5  -- O14 -- T5  = 170.166 deg ; T5  -- T5   3.7012 A


        T-O-T SUMMARY
          Range  = 91.4551° <--> 170.1658 deg
          Mean   = 130.3384 deg
          StdDev = 21.1245 deg

        T--T SUMMARY
          Range  = 2.2817 A <--> 3.7444 A
          Mean   = 2.9600 A
          StdDev = 0.3852 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O10 -- O10 = 2.0910 A
O11 -- O12 = 2.1510 A
O11 -- O12 = 2.1513 A

T-T-T analysis was not conducted.
T1  -- T1  = 2.7212 Angstrom
T1  -- T3  = 2.2817 Angstrom
T1  -- T1  = 2.6891 Angstrom

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T2  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 3.1884 Angstrom
  T2  -- T3  = 3.1497 Angstrom
  T2  -- T5  = 3.3027 Angstrom
  T2  -- T2  = 3.0715 Angstrom
  T2  -- T2  = 3.0796 Angstrom
T3  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T3  -- T1  = 2.2817 Angstrom
  T3  -- T2  = 3.1497 Angstrom
  T3  -- T3  = 2.8018 Angstrom
  T3  -- T5  = 2.9446 Angstrom
  T3  -- T3  = 2.7929 Angstrom
T4  has only 3 neighboring T-atoms within 3.50 A, but 4 bridging O-atoms
  T4  -- T4  = 2.6439 Angstrom
  T4  -- T5  = 2.0653 Angstrom
  T4  -- T4  = 2.6637 Angstrom
T5  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T5  -- T2  = 3.3027 Angstrom
  T5  -- T2  = 3.3027 Angstrom
  T5  -- T3  = 2.9446 Angstrom
  T5  -- T3  = 2.9446 Angstrom
  T5  -- T4  = 2.0653 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 24
Coordination Sequence =
    1 4 9 17 30 52 85 125 168 210 250 299 372 474 596 721 837
TD10 = 951
Circuit symbol = 4.4.4.6.6.6
Weight = 11
Vertex symbol  = 4.4.4.6.8_{2}.8_{2}
Weight = 19

T2 (Si): multiplicity = 24
Coordination Sequence =
    1 4 9 18 33 54 84 125 170 213 258 313 387 484 595 706 812
TD10 = 969
Circuit symbol = 4.4.4.8_{3}.6.6_{2}
Weight = 15
Vertex symbol  = 4.4.4.8.6.8
Weight = 20

T3 (Si): multiplicity = 24
Coordination Sequence =
    1 4 9 17 30 52 85 124 164 204 248 308 393 498 611 720 816
TD10 = 938
Circuit symbol = 4.4.4.8_{4}.6_{2}.6_{2}
Weight = 17
Vertex symbol  = 4.4.4.8.6.6
Weight = 17

T4 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 22 41 64 89 120 164 220 283 359 449 537 615 690 770
TD10 = 1018
Circuit symbol = 4.8.4.8.6.10_{6}
Weight = 21
Vertex symbol  = 4.8.4.8.8.12
Weight = 31

T5 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 21 38 60 85 118 166 225 292 371 457 538 614 701 810
TD10 = 1020
Circuit symbol = 4.10_{2}.4.10_{2}.6_{2}.12_{13}
Weight = 36
Vertex symbol  = 4.10_{2}.4.10_{2}.6.12
Weight = 31

<TD10> = 969.250
Average ring size = 5.5718