Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_191_5_207852_VDnUyM.cif"

There are 88 T-atoms per unit cell
There are 176 O-atoms per unit cell

Framework density = 15.55 T-atoms per nm^3
Material density = 1.552 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6223 Angstrom
T1  -- O2  = 1.6182 Angstrom
T1  -- O3  = 1.6217 Angstrom
T1  -- O4  = 1.6183 Angstrom
      mean = 1.6201 Angstrom
        t1 = 0.006534  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001338  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6209 Angstrom
T2  -- O5  = 1.6279 Angstrom
T2  -- O6  = 1.6187 Angstrom
T2  -- O7  = 1.6346 Angstrom
      mean = 1.6255 Angstrom
        t1 = 0.011105  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.006521  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6174 Angstrom
T3  -- O8  = 1.6191 Angstrom
T3  -- O9  = 1.6206 Angstrom
T3  -- O10 = 1.6209 Angstrom
      mean = 1.6195 Angstrom
        t1 = 0.005995  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000646  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O11 = 1.6119 Angstrom
T4  -- O12 = 1.6170 Angstrom
T4  -- O12 = 1.6170 Angstrom
T4  -- O12 = 1.6171 Angstrom
      mean = 1.6158 Angstrom
        t1 = 0.004264  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002106  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O7  = 1.6234 Angstrom
T5  -- O7  = 1.6232 Angstrom
T5  -- O12 = 1.6018 Angstrom
T5  -- O13 = 1.6195 Angstrom
      mean = 1.6170 Angstrom
        t1 = 0.009816  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008878  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6018 A <--> 1.6346 A
          Mean   = 1.6208 A
          StdDev = 0.0058 A

       t1 Range  = 0.0043 <-- 0.0075 --> 0.0111
       t2 Range  = 0.0006 <-- 0.0039 --> 0.0089

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.534 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.465 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.740 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.665 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.083 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.341 deg; O3  -- O4  = 3 A
       109.083 deg <-- 109.471 deg --> 109.740 deg

O4  -- T2  -- O5  = 109.336 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 108.624 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 109.476 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 109.583 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 110.519 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.272 deg; O6  -- O7  = 3 A
       108.624 deg <-- 109.468 deg --> 110.519 deg

O6  -- T3  -- O8  = 109.244 deg; O6  -- O8  = 3 A
O6  -- T3  -- O9  = 109.537 deg; O6  -- O9  = 3 A
O6  -- T3  -- O10 = 109.509 deg; O6  -- O10 = 3 A
O8  -- T3  -- O9  = 109.570 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.518 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.449 deg; O9  -- O10 = 3 A
       109.244 deg <-- 109.471 deg --> 109.570 deg

O11 -- T4  -- O12 = 109.981 deg; O11 -- O12 = 3 A
O11 -- T4  -- O12 = 109.981 deg; O11 -- O12 = 3 A
O11 -- T4  -- O12 = 109.978 deg; O11 -- O12 = 3 A
O12 -- T4  -- O12 = 108.964 deg; O12 -- O12 = 3 A
O12 -- T4  -- O12 = 108.955 deg; O12 -- O12 = 3 A
O12 -- T4  -- O12 = 108.955 deg; O12 -- O12 = 3 A
       108.955 deg <-- 109.469 deg --> 109.981 deg

O7  -- T5  -- O7  = 110.985 deg; O7  -- O7  = 3 A
O7  -- T5  -- O12 = 108.136 deg; O7  -- O12 = 3 A
O7  -- T5  -- O13 = 109.798 deg; O7  -- O13 = 3 A
O7  -- T5  -- O12 = 108.145 deg; O7  -- O12 = 3 A
O7  -- T5  -- O13 = 109.807 deg; O7  -- O13 = 3 A
O12 -- T5  -- O13 = 109.934 deg; O12 -- O13 = 3 A
       108.136 deg <-- 109.468 deg --> 110.985 deg

        O-T-O SUMMARY
          Range  = 108.1364 deg <--> 110.9847 deg
          Mean   = 109.4515 deg
          StdDev = 0.6243 deg

        O--O SUMMARY
          Range  = 2.6115 A <--> 2.6809 A
          Mean   = 2.6453 A
          StdDev = 0.0154 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  = 120.000 deg; T1  -- T1  = 5.2320 A
T1  - O1  - T1  - O3  - T2  = 113.509 deg; T1  -- T2  = 5.0830 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.2790 A
T1  - O2  - T1  - O3  - T2  =  90.410 deg; T1  -- T2  = 4.2593 A
T1  - O2  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.2252 A
T2  - O3  - T1  - O4  - T1  = 152.304 deg; T2  -- T1  = 5.8370 A

T1  - O4  - T2  - O5  - T2  =  89.590 deg; T1  -- T2  = 4.2593 A
T1  - O4  - T2  - O6  - T3  = 144.336 deg; T1  -- T3  = 5.7946 A
T1  - O4  - T2  - O7  - T5  =  89.463 deg; T1  -- T5  = 4.2597 A
T2  - O5  - T2  - O6  - T3  =  89.954 deg; T2  -- T3  = 4.3073 A
T2  - O5  - T2  - O7  - T5  = 111.416 deg; T2  -- T5  = 5.0061 A
T3  - O6  - T2  - O7  - T5  = 123.554 deg; T3  -- T5  = 5.3758 A

T2  - O6  - T3  - O8  - T3  = 116.645 deg; T2  -- T3  = 5.2044 A
T2  - O6  - T3  - O9  - T3  =  90.046 deg; T2  -- T3  = 4.3073 A
T2  - O6  - T3  - O10 - T3  = 116.500 deg; T2  -- T3  = 5.1790 A
T3  - O8  - T3  - O9  - T3  =  90.000 deg; T3  -- T3  = 4.2913 A
T3  - O8  - T3  - O10 - T3  =  90.000 deg; T3  -- T3  = 4.2923 A
T3  - O9  - T3  - O10 - T3  = 150.000 deg; T3  -- T3  = 5.8377 A

T4  - O11 - T4  - O12 - T5  =  90.145 deg; T4  -- T5  = 4.4270 A
T4  - O11 - T4  - O12 - T5  =  90.145 deg; T4  -- T5  = 4.4270 A
T4  - O11 - T4  - O12 - T5  =  90.145 deg; T4  -- T5  = 4.4271 A
T5  - O12 - T4  - O12 - T5  = 120.003 deg; T5  -- T5  = 5.2411 A
T5  - O12 - T4  - O12 - T5  = 119.997 deg; T5  -- T5  = 5.2411 A
T5  - O12 - T4  - O12 - T5  = 119.997 deg; T5  -- T5  = 5.2411 A

T2  - O7  - T5  - O7  - T2  = 128.633 deg; T2  -- T2  = 5.4671 A
T2  - O7  - T5  - O12 - T4  =  95.725 deg; T2  -- T4  = 4.4931 A
T2  - O7  - T5  - O13 - T5  = 114.957 deg; T2  -- T5  = 5.2900 A
T2  - O7  - T5  - O12 - T4  =  95.725 deg; T2  -- T4  = 4.4930 A
T2  - O7  - T5  - O13 - T5  = 114.967 deg; T2  -- T5  = 5.2901 A
T4  - O12 - T5  - O13 - T5  =  89.855 deg; T4  -- T5  = 4.4270 A

        T-T-T SUMMARY
          Range  = 89.4630 deg <--> 152.3038 deg
          Mean   = 108.1242 deg
          StdDev = 19.3602 deg

        T--T SUMMARY
          Range  = 4.2252 A <--> 5.8377 A
          Mean   = 4.8630 A
          StdDev = 0.5495 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 134.537 deg ; T1  -- T1   2.9925 A

T1  -- O2  -- T1  = 141.832 deg ; T1  -- T1   3.0585 A

T1  -- O3  -- T1  = 133.744 deg ; T1  -- T1   2.9828 A

T1  -- O4  -- T2  = 137.523 deg ; T1  -- T2   3.0192 A

T2  -- O5  -- T2  = 136.711 deg ; T2  -- T2   3.0260 A

T2  -- O6  -- T3  = 142.876 deg ; T2  -- T3   3.0678 A

T2  -- O7  -- T5  = 137.196 deg ; T2  -- T5   3.0333 A

T3  -- O8  -- T3  = 140.501 deg ; T3  -- T3   3.0477 A

T3  -- O9  -- T3  = 137.526 deg ; T3  -- T3   3.0211 A

T3  -- O10 -- T3  = 137.604 deg ; T3  -- T3   3.0225 A

T4  -- O11 -- T4  = 180.000 deg ; T4  -- T4   3.2238 A

T4  -- O12 -- T5  = 140.132 deg ; T4  -- T5   3.0259 A

T5  -- O13 -- T5  = 179.908 deg ; T5  -- T5   3.2391 A


        T-O-T SUMMARY
          Range  = 133.7442° <--> 180.0000 deg
          Mean   = 140.6031 deg
          StdDev = 10.2835 deg

        T--T SUMMARY
          Range  = 2.9828 A <--> 3.2391 A
          Mean   = 3.0395 A
          StdDev = 0.0549 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 24
Coordination Sequence =
    1 4 9 16 25 38 57 82 114 157 207 251 281 301 326 372 444
TD10 = 710
Circuit symbol = 4.4.4.5.6.6_{2}
Weight = 13
Vertex symbol  = 4.4.4.5.6.12
Weight = 22

T2 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 18 27 41 61 86 119 155 193 233 272 307 347 403 469
TD10 = 715
Circuit symbol = 4.5.4.6.5.6
Weight = 14
Vertex symbol  = 4.5.4.6.5.12
Weight = 23

T3 (Si): multiplicity = 24
Coordination Sequence =
    1 4 9 18 33 52 72 93 117 144 174 213 266 326 384 438 489
TD10 = 717
Circuit symbol = 4.4.4.8_{2}.6.6_{2}
Weight = 11
Vertex symbol  = 4.4.4.10.6.12
Weight = 26

T4 (Si): multiplicity = 4
Coordination Sequence =
    1 4 9 18 24 30 48 79 116 154 201 240 270 289 323 385 459
TD10 = 684
Circuit symbol = 4.5.4.5.4.5
Weight = 14
Vertex symbol  = 4.5.4.5.4.5
Weight = 14

T5 (Si): multiplicity = 12
Coordination Sequence =
    1 4 11 18 24 34 55 84 116 157 201 238 265 298 339 392 464
TD10 = 705
Circuit symbol = 4.5.5.6.5.6
Weight = 18
Vertex symbol  = 4.5.5.6.5.6
Weight = 18

<TD10> = 711.409
Average ring size = 5.1562