Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_191_5_114046_zf72DP.cif"

There are 108 T-atoms per unit cell
There are 216 O-atoms per unit cell

Framework density = 19.85 T-atoms per nm^3
Material density = 1.980 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6279 Angstrom
T1  -- O2  = 1.6212 Angstrom
T1  -- O3  = 1.6221 Angstrom
T1  -- O4  = 1.6310 Angstrom
      mean = 1.6255 Angstrom
        t1 = 0.010702  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003664  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6196 Angstrom
T2  -- O5  = 1.6194 Angstrom
T2  -- O6  = 1.6236 Angstrom
T2  -- O7  = 1.6205 Angstrom
      mean = 1.6207 Angstrom
        t1 = 0.007035  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002018  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O7  = 1.6177 Angstrom
T3  -- O8  = 1.6202 Angstrom
T3  -- O9  = 1.6227 Angstrom
T3  -- O10 = 1.6199 Angstrom
      mean = 1.6201 Angstrom
        t1 = 0.006394  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001581  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O10 = 1.6169 Angstrom
T4  -- O11 = 1.6179 Angstrom
T4  -- O12 = 1.6192 Angstrom
T4  -- O13 = 1.6194 Angstrom
      mean = 1.6184 Angstrom
        t1 = 0.005386  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001030  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O4  = 1.6245 Angstrom
T5  -- O4  = 1.6245 Angstrom
T5  -- O14 = 1.6123 Angstrom
T5  -- O15 = 1.6175 Angstrom
      mean = 1.6197 Angstrom
        t1 = 0.008316  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004198  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6123 A <--> 1.6310 A
          Mean   = 1.6210 A
          StdDev = 0.0038 A

       t1 Range  = 0.0054 <-- 0.0076 --> 0.0107
       t2 Range  = 0.0010 <-- 0.0025 --> 0.0042

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.496 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.953 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 110.655 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.151 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 109.436 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.126 deg; O3  -- O4  = 3 A
       108.953 deg <-- 109.469 deg --> 110.655 deg

O3  -- T2  -- O5  = 109.037 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.756 deg; O3  -- O6  = 3 A
O3  -- T2  -- O7  = 109.603 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 109.451 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 109.190 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 109.785 deg; O6  -- O7  = 3 A
       109.037 deg <-- 109.471 deg --> 109.785 deg

O7  -- T3  -- O8  = 109.339 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 109.821 deg; O7  -- O9  = 3 A
O7  -- T3  -- O10 = 109.547 deg; O7  -- O10 = 3 A
O8  -- T3  -- O9  = 109.367 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 109.334 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.417 deg; O9  -- O10 = 3 A
       109.334 deg <-- 109.471 deg --> 109.821 deg

O10 -- T4  -- O11 = 109.081 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 109.632 deg; O10 -- O12 = 3 A
O10 -- T4  -- O13 = 109.518 deg; O10 -- O13 = 3 A
O11 -- T4  -- O12 = 109.662 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 109.566 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 109.368 deg; O12 -- O13 = 3 A
       109.081 deg <-- 109.471 deg --> 109.662 deg

O4  -- T5  -- O4  = 110.815 deg; O4  -- O4  = 3 A
O4  -- T5  -- O14 = 109.047 deg; O4  -- O14 = 3 A
O4  -- T5  -- O15 = 109.511 deg; O4  -- O15 = 3 A
O4  -- T5  -- O14 = 109.047 deg; O4  -- O14 = 3 A
O4  -- T5  -- O15 = 109.511 deg; O4  -- O15 = 3 A
O14 -- T5  -- O15 = 108.878 deg; O14 -- O15 = 3 A
       108.878 deg <-- 109.468 deg --> 110.815 deg

        O-T-O SUMMARY
          Range  = 108.8783 deg <--> 110.8147 deg
          Mean   = 109.4853 deg
          StdDev = 0.4364 deg

        O--O SUMMARY
          Range  = 2.6275 A <--> 2.6802 A
          Mean   = 2.6475 A
          StdDev = 0.0103 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 129.335 deg; T1  -- T2  = 5.5372 A
T1  - O1  - T1  - O3  - T5  =  91.110 deg; T1  -- T5  = 4.3850 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.2835 A
T2  - O2  - T1  - O3  - T5  =  97.302 deg; T2  -- T5  = 4.5444 A
T2  - O2  - T1  - O4  - T1  = 108.928 deg; T2  -- T1  = 4.8561 A
T5  - O3  - T1  - O4  - T1  = 144.805 deg; T5  -- T1  = 5.7031 A

T1  - O3  - T2  - O5  - T2  = 108.928 deg; T1  -- T2  = 4.8988 A
T1  - O3  - T2  - O6  - T3  =  95.282 deg; T1  -- T3  = 4.4934 A
T1  - O3  - T2  - O7  - T2  = 134.600 deg; T1  -- T2  = 5.5702 A
T2  - O5  - T2  - O6  - T3  = 108.283 deg; T2  -- T3  = 4.9139 A
T2  - O5  - T2  - O7  - T2  =  90.000 deg; T2  -- T2  = 4.2569 A
T3  - O6  - T2  - O7  - T2  = 117.980 deg; T3  -- T2  = 5.2118 A

T2  - O7  - T3  - O8  - T3  = 144.992 deg; T2  -- T3  = 5.7770 A
T2  - O7  - T3  - O9  - T4  = 111.051 deg; T2  -- T4  = 5.0130 A
T2  - O7  - T3  - O10 - T3  = 108.283 deg; T2  -- T3  = 4.9017 A
T3  - O8  - T3  - O9  - T4  =  90.147 deg; T3  -- T4  = 4.2585 A
T3  - O8  - T3  - O10 - T3  =  90.000 deg; T3  -- T3  = 4.2296 A
T4  - O9  - T3  - O10 - T3  = 107.818 deg; T4  -- T3  = 4.8526 A

T3  - O10 - T4  - O11 - T4  = 107.818 deg; T3  -- T4  = 4.9242 A
T3  - O10 - T4  - O12 - T4  =  89.853 deg; T3  -- T4  = 4.2585 A
T3  - O10 - T4  - O13 - T4  = 118.570 deg; T3  -- T4  = 5.1785 A
T4  - O11 - T4  - O12 - T4  =  90.000 deg; T4  -- T4  = 4.3034 A
T4  - O11 - T4  - O13 - T4  =  90.000 deg; T4  -- T4  = 4.2987 A
T4  - O12 - T4  - O13 - T4  = 150.000 deg; T4  -- T4  = 5.8105 A

T1  - O4  - T5  - O4  - T1  = 109.611 deg; T1  -- T1  = 4.9596 A
T1  - O4  - T5  - O14 - T5  =  88.890 deg; T1  -- T5  = 4.3850 A
T1  - O4  - T5  - O15 - T5  = 120.567 deg; T1  -- T5  = 5.3863 A
T1  - O4  - T5  - O14 - T5  =  88.890 deg; T1  -- T5  = 4.3850 A
T1  - O4  - T5  - O15 - T5  = 120.567 deg; T1  -- T5  = 5.3863 A
T5  - O14 - T5  - O15 - T5  = 120.000 deg; T5  -- T5  = 5.5355 A

        T-T-T SUMMARY
          Range  = 88.8903 deg <--> 150.0000 deg
          Mean   = 108.3705 deg
          StdDev = 17.6776 deg

        T--T SUMMARY
          Range  = 4.2296 A <--> 5.8105 A
          Mean   = 4.8680 A
          StdDev = 0.4992 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 129.807 deg ; T1  -- T1   2.9485 A

T1  -- O2  -- T1  = 146.798 deg ; T1  -- T1   3.1072 A

T1  -- O3  -- T2  = 137.268 deg ; T1  -- T2   3.0189 A

T1  -- O4  -- T5  = 137.538 deg ; T1  -- T5   3.0345 A

T2  -- O5  -- T2  = 135.835 deg ; T2  -- T2   3.0011 A

T2  -- O6  -- T2  = 136.791 deg ; T2  -- T2   3.0190 A

T2  -- O7  -- T3  = 142.013 deg ; T2  -- T3   3.0618 A

T3  -- O8  -- T3  = 134.280 deg ; T3  -- T3   2.9859 A

T3  -- O9  -- T3  = 134.744 deg ; T3  -- T3   2.9956 A

T3  -- O10 -- T4  = 137.731 deg ; T3  -- T4   3.0191 A

T4  -- O11 -- T4  = 143.666 deg ; T4  -- T4   3.0745 A

T4  -- O12 -- T4  = 136.785 deg ; T4  -- T4   3.0111 A

T4  -- O13 -- T4  = 136.131 deg ; T4  -- T4   3.0044 A

T5  -- O14 -- T5  = 178.751 deg ; T5  -- T5   3.2248 A

T5  -- O15 -- T5  = 156.505 deg ; T5  -- T5   3.1670 A


        T-O-T SUMMARY
          Range  = 129.8067° <--> 178.7510 deg
          Mean   = 139.7867 deg
          StdDev = 9.2177 deg

        T--T SUMMARY
          Range  = 2.9485 A <--> 3.2248 A
          Mean   = 3.0341 A
          StdDev = 0.0593 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 22 41 63 88 120 157 197 241 292 349 406 470 547 624
TD10 = 944
Circuit symbol = 4.5.4.6.6.7_{2}
Weight = 13
Vertex symbol  = 4.5.4.6.8.8
Weight = 22

T2 (Si): multiplicity = 24
Coordination Sequence =
    1 4 11 23 38 58 84 114 152 197 241 287 342 404 471 543 616
TD10 = 923
Circuit symbol = 4.6.5.6.6.7
Weight = 16
Vertex symbol  = 4.6.5.6.6.8_{3}
Weight = 24

T3 (Si): multiplicity = 24
Coordination Sequence =
    1 4 10 21 35 51 75 108 143 180 226 280 336 394 459 531 605
TD10 = 854
Circuit symbol = 4.6.4.6_{2}.6.8_{7}
Weight = 23
Vertex symbol  = 4.6.4.6_{2}.8_{2}.8_{3}
Weight = 27

T4 (Si): multiplicity = 24
Coordination Sequence =
    1 4 9 17 30 48 69 95 130 171 215 265 323 386 451 520 595
TD10 = 789
Circuit symbol = 4.4.4.6.6.6_{2}
Weight = 13
Vertex symbol  = 4.4.4.6.6.12
Weight = 22

T5 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 21 40 65 93 123 157 196 243 296 352 415 479 544 622
TD10 = 953
Circuit symbol = 4.8_{3}.4.8_{3}.5.6
Weight = 28
Vertex symbol  = 4.8_{2}.4.8_{2}.5.6
Weight = 28

<TD10> = 885.889
Average ring size = 5.7465