Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_191_3_1326_QsOdrj.cif"

There are 36 T-atoms per unit cell
There are 72 O-atoms per unit cell

Framework density = 18.60 T-atoms per nm^3
Material density = 1.855 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6242 Angstrom
T1  -- O1  = 1.6243 Angstrom
T1  -- O2  = 1.6197 Angstrom
T1  -- O3  = 1.6193 Angstrom
      mean = 1.6219 Angstrom
        t1 = 0.007934  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001904  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6179 Angstrom
T2  -- O4  = 1.6173 Angstrom
T2  -- O4  = 1.6173 Angstrom
T2  -- O5  = 1.6158 Angstrom
      mean = 1.6171 Angstrom
        t1 = 0.004585  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000982  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O3  = 1.6171 Angstrom
T3  -- O6  = 1.6178 Angstrom
T3  -- O6  = 1.6178 Angstrom
T3  -- O7  = 1.6156 Angstrom
      mean = 1.6171 Angstrom
        t1 = 0.004510  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000803  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6156 A <--> 1.6243 A
          Mean   = 1.6187 A
          StdDev = 0.0027 A

       t1 Range  = 0.0045 <-- 0.0057 --> 0.0079
       t2 Range  = 0.0008 <-- 0.0012 --> 0.0019

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 108.341 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 109.501 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.485 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 109.498 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.486 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 110.495 deg; O2  -- O3  = 3 A
       108.341 deg <-- 109.468 deg --> 110.495 deg

O2  -- T2  -- O4  = 109.280 deg; O2  -- O4  = 3 A
O2  -- T2  -- O4  = 109.276 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.387 deg; O2  -- O5  = 3 A
O4  -- T2  -- O4  = 109.257 deg; O4  -- O4  = 3 A
O4  -- T2  -- O5  = 109.813 deg; O4  -- O5  = 3 A
O4  -- T2  -- O5  = 109.813 deg; O4  -- O5  = 3 A
       109.257 deg <-- 109.471 deg --> 109.813 deg

O3  -- T3  -- O6  = 109.315 deg; O3  -- O6  = 3 A
O3  -- T3  -- O6  = 109.315 deg; O3  -- O6  = 3 A
O3  -- T3  -- O7  = 109.423 deg; O3  -- O7  = 3 A
O6  -- T3  -- O6  = 109.276 deg; O6  -- O6  = 3 A
O6  -- T3  -- O7  = 109.749 deg; O6  -- O7  = 3 A
O6  -- T3  -- O7  = 109.749 deg; O6  -- O7  = 3 A
       109.276 deg <-- 109.471 deg --> 109.749 deg

        O-T-O SUMMARY
          Range  = 108.3415 deg <--> 110.4947 deg
          Mean   = 109.4698 deg
          StdDev = 0.4044 deg

        O--O SUMMARY
          Range  = 2.6338 A <--> 2.6612 A
          Mean   = 2.6433 A
          StdDev = 0.0064 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T1  =  60.000 deg; T1  -- T1  = 2.9637 A
T1  - O1  - T1  - O2  - T2  = 131.620 deg; T1  -- T2  = 5.5536 A
T1  - O1  - T1  - O3  - T3  = 132.138 deg; T1  -- T3  = 5.5507 A
T1  - O1  - T1  - O2  - T2  = 131.620 deg; T1  -- T2  = 5.5536 A
T1  - O1  - T1  - O3  - T3  = 132.138 deg; T1  -- T3  = 5.5507 A
T2  - O2  - T1  - O3  - T3  =  79.141 deg; T2  -- T3  = 3.9704 A

T1  - O2  - T2  - O4  - T2  = 112.549 deg; T1  -- T2  = 5.1688 A
T1  - O2  - T2  - O4  - T2  = 112.549 deg; T1  -- T2  = 5.1688 A
T1  - O2  - T2  - O5  - T2  = 129.920 deg; T1  -- T2  = 5.7460 A
T2  - O4  - T2  - O4  - T2  = 120.000 deg; T2  -- T2  = 5.3531 A
T2  - O4  - T2  - O5  - T2  =  90.000 deg; T2  -- T2  = 4.4617 A
T2  - O4  - T2  - O5  - T2  =  90.000 deg; T2  -- T2  = 4.4617 A

T1  - O3  - T3  - O6  - T3  = 112.790 deg; T1  -- T3  = 5.1530 A
T1  - O3  - T3  - O6  - T3  = 129.221 deg; T1  -- T3  = 5.7219 A
T1  - O3  - T3  - O7  - T3  = 112.790 deg; T1  -- T3  = 5.1530 A
T3  - O6  - T3  - O6  - T3  =  90.000 deg; T3  -- T3  = 4.4581 A
T3  - O6  - T3  - O7  - T3  = 120.000 deg; T3  -- T3  = 5.3318 A
T3  - O6  - T3  - O7  - T3  =  90.000 deg; T3  -- T3  = 4.4581 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 132.1381 deg
          Mean   = 109.8043 deg
          StdDev = 21.0799 deg

        T--T SUMMARY
          Range  = 2.9637 A <--> 5.7460 A
          Mean   = 4.9877 A
          StdDev = 0.7090 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 131.658 deg ; T1  -- T1   2.9637 A

T1  -- O2  -- T2  = 149.563 deg ; T1  -- T2   3.1241 A

T1  -- O3  -- T3  = 147.690 deg ; T1  -- T3   3.1086 A

T2  -- O4  -- T2  = 145.675 deg ; T2  -- T2   3.0906 A

T2  -- O5  -- T2  = 169.388 deg ; T2  -- T2   3.2178 A

T3  -- O6  -- T3  = 144.133 deg ; T3  -- T3   3.0783 A

T3  -- O7  -- T3  = 172.736 deg ; T3  -- T3   3.2247 A


        T-O-T SUMMARY
          Range  = 131.6583° <--> 172.7356 deg
          Mean   = 151.5490 deg
          StdDev = 13.5562 deg

        T--T SUMMARY
          Range  = 2.9637 A <--> 3.2247 A
          Mean   = 3.1154 A
          StdDev = 0.0829 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 24 40 54 80 120 156 196 228 266 330 410 472 524 576
TD10 = 913
Circuit symbol = 3.6_{2}.8_{3}.8_{3}.8_{3}.8_{3}
Weight = 33
Vertex symbol  = 3.6_{2}.8_{3}.8_{3}.8_{3}.8_{3}
Weight = 33

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 21 38 62 89 114 143 184 238 294 340 383 441 523 612
TD10 = 904
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 24
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 24

T3 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 21 38 62 89 114 143 184 238 294 340 383 441 523 612
TD10 = 904
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 24
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 24

<TD10> = 907.000
Average ring size = 6.2143