Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_191_2_33_bq3Yij.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 19.14 T-atoms per nm^3
Material density = 1.910 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6248 Angstrom
T1  -- O1  = 1.6247 Angstrom
T1  -- O2  = 1.6098 Angstrom
T1  -- O2  = 1.6098 Angstrom
      mean = 1.6173 Angstrom
        t1 = 0.004847  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001363  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6098 Angstrom
T2  -- O2  = 1.6098 Angstrom
T2  -- O3  = 1.6106 Angstrom
T2  -- O3  = 1.6107 Angstrom
      mean = 1.6102 Angstrom
        t1 = 0.001824  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001273  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6098 A <--> 1.6248 A
          Mean   = 1.6138 A
          StdDev = 0.0064 A

       t1 Range  = 0.0018 <-- 0.0033 --> 0.0048
       t2 Range  = 0.0013 <-- 0.0013 --> 0.0014

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 108.501 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 109.663 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 109.663 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 109.662 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 109.662 deg; O1  -- O2  = 3 A
O2  -- T1  -- O2  = 109.673 deg; O2  -- O2  = 3 A
       108.501 deg <-- 109.470 deg --> 109.673 deg

O2  -- T2  -- O2  = 109.610 deg; O2  -- O2  = 3 A
O2  -- T2  -- O3  = 109.613 deg; O2  -- O3  = 3 A
O2  -- T2  -- O3  = 109.608 deg; O2  -- O3  = 3 A
O2  -- T2  -- O3  = 109.613 deg; O2  -- O3  = 3 A
O2  -- T2  -- O3  = 109.608 deg; O2  -- O3  = 3 A
O3  -- T2  -- O3  = 108.774 deg; O3  -- O3  = 3 A
       108.774 deg <-- 109.471 deg --> 109.613 deg

        O-T-O SUMMARY
          Range  = 108.5012 deg <--> 109.6727 deg
          Mean   = 109.5463 deg
          StdDev = 0.2926 deg

        O--O SUMMARY
          Range  = 2.6188 A <--> 2.6442 A
          Mean   = 2.6359 A
          StdDev = 0.0069 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T1  =  60.000 deg; T1  -- T1  = 2.9627 A
T1  - O1  - T1  - O2  - T2  = 119.930 deg; T1  -- T2  = 5.3537 A
T1  - O1  - T1  - O2  - T2  = 119.930 deg; T1  -- T2  = 5.3537 A
T1  - O1  - T1  - O2  - T2  = 119.931 deg; T1  -- T2  = 5.3538 A
T1  - O1  - T1  - O2  - T2  = 119.931 deg; T1  -- T2  = 5.3538 A
T2  - O2  - T1  - O2  - T2  = 109.641 deg; T2  -- T2  = 5.2632 A

T1  - O2  - T2  - O2  - T2  = 106.741 deg; T1  -- T2  = 5.1566 A
T1  - O2  - T2  - O3  - T2  = 106.744 deg; T1  -- T2  = 5.1567 A
T1  - O2  - T2  - O3  - T1  = 109.641 deg; T1  -- T1  = 5.2632 A
T2  - O2  - T2  - O3  - T2  = 120.000 deg; T2  -- T2  = 5.5527 A
T2  - O2  - T2  - O3  - T1  = 106.741 deg; T2  -- T1  = 5.1566 A
T2  - O3  - T2  - O3  - T1  = 106.744 deg; T2  -- T1  = 5.1567 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 120.0000 deg
          Mean   = 111.1457 deg
          StdDev = 12.7241 deg

        T--T SUMMARY
          Range  = 2.9627 A <--> 5.5527 A
          Mean   = 5.1840 A
          StdDev = 0.5004 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 131.499 deg ; T1  -- T1   2.9627 A

T1  -- O2  -- T2  = 179.968 deg ; T1  -- T2   3.2197 A

T2  -- O3  -- T2  = 168.774 deg ; T2  -- T2   3.2059 A


        T-O-T SUMMARY
          Range  = 131.4988° <--> 179.9684 deg
          Mean   = 160.0803 deg
          StdDev = 21.3212 deg

        T--T SUMMARY
          Range  = 2.9627 A <--> 3.2197 A
          Mean   = 3.1294 A
          StdDev = 0.1214 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 24 44 64 100 122 164 214 264 322 362 432 512 600 672
TD10 = 1011
Circuit symbol = 3.6_{2}.6.6.6.6
Weight = 21
Vertex symbol  = 3.6_{2}.6.6.6.6
Weight = 21

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 12 25 42 66 94 131 170 208 258 312 382 447 502 578 658
TD10 = 1011
Circuit symbol = 6.6.6.6.6.6_{2}
Weight = 24
Vertex symbol  = 6.6.6.6.6.6_{2}
Weight = 24

<TD10> = 1011.000
Average ring size = 5.6000