Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_189_5_9550689_9GoAsD.cif"

There are 54 T-atoms per unit cell
There are 108 O-atoms per unit cell

Framework density = 26.54 T-atoms per nm^3
Material density = 2.648 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5449 Angstrom
T1  -- O1  = 1.5179 Angstrom
T1  -- O2  = 1.6663 Angstrom
T1  -- O3  = 1.6634 Angstrom
      mean = 1.5981 Angstrom
        t1 = 0.200969  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.198693  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.7071 Angstrom
T2  -- O4  = 1.6254 Angstrom
T2  -- O5  = 1.7111 Angstrom
T2  -- O6  = 1.6319 Angstrom
      mean = 1.6689 Angstrom
        t1 = 0.061491  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.075299  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O3  = 1.6973 Angstrom
T3  -- O7  = 1.7207 Angstrom
T3  -- O8  = 1.6227 Angstrom
T3  -- O9  = 1.6197 Angstrom
      mean = 1.6651 Angstrom
        t1 = 0.063338  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.035734  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O9  = 1.6004 Angstrom
T4  -- O10 = 1.5747 Angstrom
T4  -- O11 = 1.6071 Angstrom
T4  -- O12 = 1.5480 Angstrom
      mean = 1.5826 Angstrom
        t1 = 0.032641  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.019201  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O12 = 1.5926 Angstrom
T5  -- O12 = 1.5926 Angstrom
T5  -- O13 = 1.5734 Angstrom
T5  -- O13 = 1.5700 Angstrom
      mean = 1.5821 Angstrom
        t1 = 0.043536  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.028356  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5179 A <--> 1.7207 A
          Mean   = 1.6235 A
          StdDev = 0.0593 A

       t1 Range  = 0.0326 <-- 0.0804 --> 0.2010
       t2 Range  = 0.0192 <-- 0.0715 --> 0.1987

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 104.129 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  =  66.342 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  =  64.830 deg; O1  -- O3  = 2 A
O1  -- T1  -- O2  = 113.802 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 113.390 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 117.886 deg; O2  -- O3  = 3 A
       64.830 deg <-- 96.730 deg --> 117.886 deg

O2  -- T2  -- O4  = 106.253 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 123.705 deg; O2  -- O5  = 3 A
O2  -- T2  -- O6  = 105.647 deg; O2  -- O6  = 3 A
O4  -- T2  -- O5  = 106.043 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 106.611 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 107.545 deg; O5  -- O6  = 3 A
       105.647 deg <-- 109.301 deg --> 123.705 deg

O3  -- T3  -- O7  = 123.840 deg; O3  -- O7  = 3 A
O3  -- T3  -- O8  = 106.470 deg; O3  -- O8  = 3 A
O3  -- T3  -- O9  = 101.585 deg; O3  -- O9  = 3 A
O7  -- T3  -- O8  = 107.471 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 108.871 deg; O7  -- O9  = 3 A
O8  -- T3  -- O9  = 107.659 deg; O8  -- O9  = 3 A
       101.585 deg <-- 109.316 deg --> 123.840 deg

O9  -- T4  -- O10 = 108.303 deg; O9  -- O10 = 3 A
O9  -- T4  -- O11 = 109.110 deg; O9  -- O11 = 3 A
O9  -- T4  -- O12 = 114.804 deg; O9  -- O12 = 3 A
O10 -- T4  -- O11 = 113.276 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 102.946 deg; O10 -- O12 = 2 A
O11 -- T4  -- O12 = 108.416 deg; O11 -- O12 = 3 A
       102.946 deg <-- 109.476 deg --> 114.804 deg

O12 -- T5  -- O12 = 122.548 deg; O12 -- O12 = 3 A
O12 -- T5  -- O13 = 106.005 deg; O12 -- O13 = 3 A
O12 -- T5  -- O13 = 104.684 deg; O12 -- O13 = 3 A
O12 -- T5  -- O13 = 106.005 deg; O12 -- O13 = 3 A
O12 -- T5  -- O13 = 104.684 deg; O12 -- O13 = 3 A
O13 -- T5  -- O13 = 113.163 deg; O13 -- O13 = 3 A
       104.684 deg <-- 109.515 deg --> 122.548 deg

        O-T-O SUMMARY
          Range  = 64.8296 deg <--> 123.8396 deg
          Mean   = 106.6284 deg
          StdDev = 13.1004 deg

        O--O SUMMARY
          Range  = 1.7227 A <--> 3.0157 A
          Mean   = 2.5807 A
          StdDev = 0.2761 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 135.833 deg ; T1  -- T1   2.8381 A

T1  -- O2  -- T2  = 142.133 deg ; T1  -- T2   3.1910 A

T1  -- O3  -- T3  = 145.434 deg ; T1  -- T3   3.2090 A

T2  -- O4  -- T2  = 163.817 deg ; T2  -- T2   3.2184 A

T2  -- O5  -- T2  = 132.958 deg ; T2  -- T2   3.1379 A

T2  -- O6  -- T2  = 126.307 deg ; T2  -- T2   2.9121 A

T3  -- O7  -- T3  = 136.056 deg ; T3  -- T3   3.1915 A

T3  -- O8  -- T3  = 125.427 deg ; T3  -- T3   2.8842 A

T3  -- O9  -- T4  = 139.588 deg ; T3  -- T4   3.0220 A

T4  -- O10 -- T4  = 121.933 deg ; T4  -- T4   2.7537 A

T4  -- O11 -- T4  = 115.368 deg ; T4  -- T4   2.7163 A

T4  -- O12 -- T5  = 149.640 deg ; T4  -- T5   3.0310 A

T5  -- O13 -- T5  = 126.837 deg ; T5  -- T5   2.8111 A


        T-O-T SUMMARY
          Range  = 115.3678° <--> 163.8168 deg
          Mean   = 135.8330 deg
          StdDev = 12.6264 deg

        T--T SUMMARY
          Range  = 2.7163 A <--> 3.2184 A
          Mean   = 3.0009 A
          StdDev = 0.1775 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 1.7599 A
O1  -- O3  = 1.7227 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 7 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T1  = 2.8381 Angstrom
  T1  -- T1  = 2.8381 Angstrom
  T1  -- T1  = 2.5951 Angstrom
  T1  -- T2  = 3.2484 Angstrom
  T1  -- T2  = 3.1910 Angstrom
  T1  -- T3  = 3.2864 Angstrom
  T1  -- T3  = 3.2090 Angstrom
T2  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 3.2484 Angstrom
  T2  -- T1  = 3.1910 Angstrom
  T2  -- T2  = 3.1379 Angstrom
  T2  -- T2  = 2.9121 Angstrom
  T2  -- T2  = 3.2184 Angstrom
T3  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T3  -- T1  = 3.2864 Angstrom
  T3  -- T1  = 3.2090 Angstrom
  T3  -- T3  = 3.1915 Angstrom
  T3  -- T4  = 3.0220 Angstrom
  T3  -- T3  = 2.8842 Angstrom
T4  -- T4  = 2.7537 Angstrom
T4  -- T4  = 2.7163 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 24 40 54 80 120 156 196 228 266 330 410 472 524 576
TD10 = 913
Circuit symbol = 3.6_{2}.8_{3}.8_{3}.8_{3}.8_{3}
Weight = 33
Vertex symbol  = 3.6_{2}.8_{3}.8_{3}.8_{3}.8_{3}
Weight = 33

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 21 38 62 89 114 143 184 238 294 340 383 441 523 612
TD10 = 904
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 24
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 24

T3 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 21 38 62 89 114 143 184 238 294 340 383 441 523 612
TD10 = 904
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 24
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 24

T4 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 21 38 62 89 114 143 184 238 294 340 383 441 523 612
TD10 = 904
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 24
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 24

T5 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 24 40 54 80 120 156 196 228 266 330 410 472 524 576
TD10 = 913
Circuit symbol = 3.6_{2}.8_{3}.8_{3}.8_{3}.8_{3}
Weight = 33
Vertex symbol  = 3.6_{2}.8_{3}.8_{3}.8_{3}.8_{3}
Weight = 33

<TD10> = 907.000
Average ring size = 6.2143