Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_189_5_431357__cWJCj.cif"

There are 60 T-atoms per unit cell
There are 120 O-atoms per unit cell

Framework density = 16.70 T-atoms per nm^3
Material density = 1.666 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6249 Angstrom
T1  -- O1  = 1.6252 Angstrom
T1  -- O2  = 1.6248 Angstrom
T1  -- O3  = 1.6267 Angstrom
      mean = 1.6254 Angstrom
        t1 = 0.010691  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003495  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6270 Angstrom
T2  -- O4  = 1.6214 Angstrom
T2  -- O5  = 1.6203 Angstrom
T2  -- O6  = 1.6186 Angstrom
      mean = 1.6218 Angstrom
        t1 = 0.007720  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002038  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O5  = 1.6219 Angstrom
T3  -- O6  = 1.6185 Angstrom
T3  -- O7  = 1.6177 Angstrom
T3  -- O8  = 1.6246 Angstrom
      mean = 1.6207 Angstrom
        t1 = 0.007071  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002996  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O8  = 1.6247 Angstrom
T4  -- O9  = 1.6198 Angstrom
T4  -- O10 = 1.6201 Angstrom
T4  -- O11 = 1.6195 Angstrom
      mean = 1.6210 Angstrom
        t1 = 0.007167  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001366  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O10 = 1.6195 Angstrom
T5  -- O11 = 1.6198 Angstrom
T5  -- O12 = 1.6212 Angstrom
T5  -- O13 = 1.6199 Angstrom
      mean = 1.6201 Angstrom
        t1 = 0.006373  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000734  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6177 A <--> 1.6270 A
          Mean   = 1.6218 A
          StdDev = 0.0029 A

       t1 Range  = 0.0064 <-- 0.0078 --> 0.0107
       t2 Range  = 0.0007 <-- 0.0021 --> 0.0035

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 108.203 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 109.090 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.989 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 109.168 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.789 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 110.558 deg; O2  -- O3  = 3 A
       108.203 deg <-- 109.466 deg --> 110.558 deg

O3  -- T2  -- O4  = 109.689 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 109.649 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.293 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 109.511 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.687 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 108.996 deg; O5  -- O6  = 3 A
       108.996 deg <-- 109.471 deg --> 109.689 deg

O5  -- T3  -- O6  = 109.617 deg; O5  -- O6  = 3 A
O5  -- T3  -- O7  = 108.906 deg; O5  -- O7  = 3 A
O5  -- T3  -- O8  = 109.708 deg; O5  -- O8  = 3 A
O6  -- T3  -- O7  = 109.394 deg; O6  -- O7  = 3 A
O6  -- T3  -- O8  = 109.806 deg; O6  -- O8  = 3 A
O7  -- T3  -- O8  = 109.392 deg; O7  -- O8  = 3 A
       108.906 deg <-- 109.470 deg --> 109.806 deg

O8  -- T4  -- O9  = 109.494 deg; O8  -- O9  = 3 A
O8  -- T4  -- O10 = 109.246 deg; O8  -- O10 = 3 A
O8  -- T4  -- O11 = 110.015 deg; O8  -- O11 = 3 A
O9  -- T4  -- O10 = 109.131 deg; O9  -- O10 = 3 A
O9  -- T4  -- O11 = 109.495 deg; O9  -- O11 = 3 A
O10 -- T4  -- O11 = 109.442 deg; O10 -- O11 = 3 A
       109.131 deg <-- 109.471 deg --> 110.015 deg

O10 -- T5  -- O11 = 109.319 deg; O10 -- O11 = 3 A
O10 -- T5  -- O12 = 109.448 deg; O10 -- O12 = 3 A
O10 -- T5  -- O13 = 109.213 deg; O10 -- O13 = 3 A
O11 -- T5  -- O12 = 109.558 deg; O11 -- O12 = 3 A
O11 -- T5  -- O13 = 109.669 deg; O11 -- O13 = 3 A
O12 -- T5  -- O13 = 109.618 deg; O12 -- O13 = 3 A
       109.213 deg <-- 109.471 deg --> 109.669 deg

        O-T-O SUMMARY
          Range  = 108.2035 deg <--> 110.5581 deg
          Mean   = 109.4673 deg
          StdDev = 0.4086 deg

        O--O SUMMARY
          Range  = 2.6328 A <--> 2.6725 A
          Mean   = 2.6484 A
          StdDev = 0.0082 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T1  =  60.000 deg; T1  -- T1  = 2.9556 A
T1  - O1  - T1  - O2  - T2  = 102.972 deg; T1  -- T2  = 4.6598 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.1318 A
T1  - O1  - T1  - O2  - T2  = 113.788 deg; T1  -- T2  = 4.9885 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.1318 A
T2  - O2  - T1  - O3  - T1  = 156.158 deg; T2  -- T1  = 5.7599 A

T1  - O3  - T2  - O4  - T3  =  97.039 deg; T1  -- T3  = 4.5316 A
T1  - O3  - T2  - O5  - T3  = 106.399 deg; T1  -- T3  = 4.8480 A
T1  - O3  - T2  - O6  - T2  = 112.530 deg; T1  -- T2  = 5.0687 A
T3  - O4  - T2  - O5  - T3  =  97.192 deg; T3  -- T3  = 4.5783 A
T3  - O4  - T2  - O6  - T2  = 146.368 deg; T3  -- T2  = 5.8815 A
T3  - O5  - T2  - O6  - T2  =  89.732 deg; T3  -- T2  = 4.3386 A

T2  - O5  - T3  - O6  - T2  = 107.655 deg; T2  -- T2  = 4.9273 A
T2  - O5  - T3  - O7  - T3  = 135.551 deg; T2  -- T3  = 5.6613 A
T2  - O5  - T3  - O8  - T4  = 115.691 deg; T2  -- T4  = 5.1030 A
T2  - O6  - T3  - O7  - T3  =  90.268 deg; T2  -- T3  = 4.3386 A
T2  - O6  - T3  - O8  - T4  = 115.725 deg; T2  -- T4  = 5.1088 A
T3  - O7  - T3  - O8  - T4  =  90.045 deg; T3  -- T4  = 4.2765 A

T3  - O8  - T4  - O9  - T4  =  89.955 deg; T3  -- T4  = 4.2765 A
T3  - O8  - T4  - O10 - T5  = 115.490 deg; T3  -- T5  = 5.0923 A
T3  - O8  - T4  - O11 - T5  = 115.409 deg; T3  -- T5  = 5.0896 A
T4  - O9  - T4  - O10 - T5  = 135.791 deg; T4  -- T5  = 5.6650 A
T4  - O9  - T4  - O11 - T5  =  90.183 deg; T4  -- T5  = 4.3301 A
T5  - O10 - T4  - O11 - T5  = 108.014 deg; T5  -- T5  = 4.9239 A

T4  - O10 - T5  - O11 - T4  =  97.511 deg; T4  -- T4  = 4.5759 A
T4  - O10 - T5  - O12 - T5  = 115.436 deg; T4  -- T5  = 5.1581 A
T4  - O10 - T5  - O13 - T5  = 146.523 deg; T4  -- T5  = 5.8740 A
T4  - O11 - T5  - O12 - T5  = 115.440 deg; T4  -- T5  = 5.1578 A
T4  - O11 - T5  - O13 - T5  =  89.817 deg; T4  -- T5  = 4.3301 A
T5  - O12 - T5  - O13 - T5  =  90.000 deg; T5  -- T5  = 4.3479 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 156.1578 deg
          Mean   = 107.8536 deg
          StdDev = 20.7238 deg

        T--T SUMMARY
          Range  = 2.9556 A <--> 5.8815 A
          Mean   = 4.8114 A
          StdDev = 0.6249 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 130.843 deg ; T1  -- T1   2.9556 A

T1  -- O2  -- T1  = 125.369 deg ; T1  -- T1   2.8872 A

T1  -- O3  -- T2  = 134.412 deg ; T1  -- T2   2.9996 A

T2  -- O4  -- T2  = 145.288 deg ; T2  -- T2   3.0952 A

T2  -- O5  -- T3  = 140.242 deg ; T2  -- T3   3.0490 A

T2  -- O6  -- T3  = 141.360 deg ; T2  -- T3   3.0548 A

T3  -- O7  -- T3  = 142.824 deg ; T3  -- T3   3.0666 A

T3  -- O8  -- T4  = 132.866 deg ; T3  -- T4   2.9783 A

T4  -- O9  -- T4  = 142.895 deg ; T4  -- T4   3.0712 A

T4  -- O10 -- T5  = 139.890 deg ; T4  -- T5   3.0431 A

T4  -- O11 -- T5  = 139.856 deg ; T4  -- T5   3.0426 A

T5  -- O12 -- T5  = 141.176 deg ; T5  -- T5   3.0580 A

T5  -- O13 -- T5  = 145.094 deg ; T5  -- T5   3.0907 A


        T-O-T SUMMARY
          Range  = 125.3686° <--> 145.2876 deg
          Mean   = 138.6242 deg
          StdDev = 5.7633 deg

        T--T SUMMARY
          Range  = 2.8872 A <--> 3.0952 A
          Mean   = 3.0301 A
          StdDev = 0.0574 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 8 14 27 46 65 96 129 154 192 234 274 325 380 426 481
TD10 = 736
Circuit symbol = 3.7_{2}.4.5.4.5
Weight = 11
Vertex symbol  = 3.8.4.5.4.5
Weight = 16

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 11 19 30 50 70 94 129 161 194 237 283 325 374 436 495
TD10 = 763
Circuit symbol = 4.5.5.8_{5}.6_{2}.7
Weight = 18
Vertex symbol  = 4.5.5.8_{2}.6_{2}.8
Weight = 23

T3 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 32 47 70 97 123 158 199 233 276 332 382 433 499
TD10 = 761
Circuit symbol = 4.5.4.6.6_{2}.7
Weight = 15
Vertex symbol  = 4.5.4.6.6.12_{2}
Weight = 31

T4 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 33 49 69 96 127 155 189 236 283 326 382 446 499
TD10 = 753
Circuit symbol = 4.6.4.6_{2}.6_{2}.8_{6}
Weight = 21
Vertex symbol  = 4.6.4.6_{2}.6.8_{2}
Weight = 21

T5 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 33 50 73 97 121 155 194 232 281 337 386 435 500
TD10 = 758
Circuit symbol = 4.6.4.6_{2}.6_{2}.8_{6}
Weight = 21
Vertex symbol  = 4.6.4.6_{2}.6.8_{2}
Weight = 21

<TD10> = 754.200
Average ring size = 5.4815