Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_189_5_2912135_HZQo5U.cif"

There are 60 T-atoms per unit cell
There are 120 O-atoms per unit cell

Framework density = 16.86 T-atoms per nm^3
Material density = 1.682 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6263 Angstrom
T1  -- O1  = 1.6254 Angstrom
T1  -- O2  = 1.6215 Angstrom
T1  -- O3  = 1.6228 Angstrom
      mean = 1.6240 Angstrom
        t1 = 0.009200  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002409  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6210 Angstrom
T2  -- O4  = 1.6193 Angstrom
T2  -- O5  = 1.6220 Angstrom
T2  -- O6  = 1.6183 Angstrom
      mean = 1.6201 Angstrom
        t1 = 0.006411  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000911  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O3  = 1.6208 Angstrom
T3  -- O7  = 1.6188 Angstrom
T3  -- O8  = 1.6218 Angstrom
T3  -- O9  = 1.6184 Angstrom
      mean = 1.6199 Angstrom
        t1 = 0.006285  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000797  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O5  = 1.6219 Angstrom
T4  -- O6  = 1.6188 Angstrom
T4  -- O10 = 1.6226 Angstrom
T4  -- O11 = 1.6210 Angstrom
      mean = 1.6211 Angstrom
        t1 = 0.007075  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001212  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O8  = 1.6217 Angstrom
T5  -- O9  = 1.6182 Angstrom
T5  -- O12 = 1.6223 Angstrom
T5  -- O13 = 1.6214 Angstrom
      mean = 1.6209 Angstrom
        t1 = 0.007009  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001374  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6182 A <--> 1.6263 A
          Mean   = 1.6212 A
          StdDev = 0.0022 A

       t1 Range  = 0.0063 <-- 0.0072 --> 0.0092
       t2 Range  = 0.0008 <-- 0.0013 --> 0.0024

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 108.392 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 109.863 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.906 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 109.720 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.656 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 109.291 deg; O2  -- O3  = 3 A
       108.392 deg <-- 109.471 deg --> 109.906 deg

O2  -- T2  -- O4  = 109.603 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.466 deg; O2  -- O5  = 3 A
O2  -- T2  -- O6  = 109.233 deg; O2  -- O6  = 3 A
O4  -- T2  -- O5  = 109.262 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.874 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 109.389 deg; O5  -- O6  = 3 A
       109.233 deg <-- 109.471 deg --> 109.874 deg

O3  -- T3  -- O7  = 109.573 deg; O3  -- O7  = 3 A
O3  -- T3  -- O8  = 109.409 deg; O3  -- O8  = 3 A
O3  -- T3  -- O9  = 109.242 deg; O3  -- O9  = 3 A
O7  -- T3  -- O8  = 109.182 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 109.839 deg; O7  -- O9  = 3 A
O8  -- T3  -- O9  = 109.583 deg; O8  -- O9  = 3 A
       109.182 deg <-- 109.471 deg --> 109.839 deg

O5  -- T4  -- O6  = 109.067 deg; O5  -- O6  = 3 A
O5  -- T4  -- O10 = 109.511 deg; O5  -- O10 = 3 A
O5  -- T4  -- O11 = 109.447 deg; O5  -- O11 = 3 A
O6  -- T4  -- O10 = 109.895 deg; O6  -- O10 = 3 A
O6  -- T4  -- O11 = 109.432 deg; O6  -- O11 = 3 A
O10 -- T4  -- O11 = 109.475 deg; O10 -- O11 = 3 A
       109.067 deg <-- 109.471 deg --> 109.895 deg

O8  -- T5  -- O9  = 108.936 deg; O8  -- O9  = 3 A
O8  -- T5  -- O12 = 109.550 deg; O8  -- O12 = 3 A
O8  -- T5  -- O13 = 109.588 deg; O8  -- O13 = 3 A
O9  -- T5  -- O12 = 109.753 deg; O9  -- O12 = 3 A
O9  -- T5  -- O13 = 109.515 deg; O9  -- O13 = 3 A
O12 -- T5  -- O13 = 109.485 deg; O12 -- O13 = 3 A
       108.936 deg <-- 109.471 deg --> 109.753 deg

        O-T-O SUMMARY
          Range  = 108.3920 deg <--> 109.9058 deg
          Mean   = 109.4708 deg
          StdDev = 0.3197 deg

        O--O SUMMARY
          Range  = 2.6366 A <--> 2.6599 A
          Mean   = 2.6474 A
          StdDev = 0.0056 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T1  =  60.000 deg; T1  -- T1  = 2.9661 A
T1  - O1  - T1  - O2  - T2  = 100.741 deg; T1  -- T2  = 4.6408 A
T1  - O1  - T1  - O3  - T3  = 100.619 deg; T1  -- T3  = 4.6345 A
T1  - O1  - T1  - O2  - T2  = 112.520 deg; T1  -- T2  = 5.0105 A
T1  - O1  - T1  - O3  - T3  = 112.523 deg; T1  -- T3  = 5.0083 A
T2  - O2  - T1  - O3  - T3  = 134.948 deg; T2  -- T3  = 5.6486 A

T1  - O2  - T2  - O4  - T4  =  98.431 deg; T1  -- T4  = 4.5994 A
T1  - O2  - T2  - O5  - T4  = 108.709 deg; T1  -- T4  = 4.9747 A
T1  - O2  - T2  - O6  - T2  = 111.721 deg; T1  -- T2  = 5.1222 A
T4  - O4  - T2  - O5  - T4  =  98.993 deg; T4  -- T4  = 4.6216 A
T4  - O4  - T2  - O6  - T2  = 144.394 deg; T4  -- T2  = 5.8507 A
T4  - O5  - T2  - O6  - T2  =  89.138 deg; T4  -- T2  = 4.3456 A

T1  - O3  - T3  - O7  - T5  =  98.179 deg; T1  -- T5  = 4.5881 A
T1  - O3  - T3  - O8  - T5  = 108.675 deg; T1  -- T5  = 4.9685 A
T1  - O3  - T3  - O9  - T3  = 111.766 deg; T1  -- T3  = 5.1193 A
T5  - O7  - T3  - O8  - T5  =  99.682 deg; T5  -- T5  = 4.6422 A
T5  - O7  - T3  - O9  - T3  = 144.315 deg; T5  -- T3  = 5.8466 A
T5  - O8  - T3  - O9  - T3  =  89.001 deg; T5  -- T3  = 4.3363 A

T2  - O5  - T4  - O6  - T2  = 104.987 deg; T2  -- T2  = 4.8217 A
T2  - O5  - T4  - O10 - T4  = 137.090 deg; T2  -- T4  = 5.6332 A
T2  - O5  - T4  - O11 - T4  = 116.374 deg; T2  -- T4  = 5.1109 A
T2  - O6  - T4  - O10 - T4  =  90.862 deg; T2  -- T4  = 4.3456 A
T2  - O6  - T4  - O11 - T4  = 115.937 deg; T2  -- T4  = 5.1389 A
T4  - O10 - T4  - O11 - T4  =  90.000 deg; T4  -- T4  = 4.2684 A

T3  - O8  - T5  - O9  - T3  = 104.921 deg; T3  -- T3  = 4.8163 A
T3  - O8  - T5  - O12 - T5  = 116.111 deg; T3  -- T5  = 5.1023 A
T3  - O8  - T5  - O13 - T5  = 137.534 deg; T3  -- T5  = 5.6255 A
T3  - O9  - T5  - O12 - T5  = 115.705 deg; T3  -- T5  = 5.1287 A
T3  - O9  - T5  - O13 - T5  =  90.999 deg; T3  -- T5  = 4.3363 A
T5  - O12 - T5  - O13 - T5  =  90.000 deg; T5  -- T5  = 4.2558 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 144.3944 deg
          Mean   = 108.4440 deg
          StdDev = 18.4113 deg

        T--T SUMMARY
          Range  = 2.9661 A <--> 5.8507 A
          Mean   = 4.8705 A
          StdDev = 0.5763 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 131.608 deg ; T1  -- T1   2.9661 A

T1  -- O2  -- T2  = 141.254 deg ; T1  -- T2   3.0590 A

T1  -- O3  -- T3  = 140.861 deg ; T1  -- T3   3.0562 A

T2  -- O4  -- T2  = 150.165 deg ; T2  -- T2   3.1294 A

T2  -- O5  -- T4  = 136.732 deg ; T2  -- T4   3.0154 A

T2  -- O6  -- T4  = 142.205 deg ; T2  -- T4   3.0626 A

T3  -- O7  -- T3  = 149.977 deg ; T3  -- T3   3.1271 A

T3  -- O8  -- T5  = 136.705 deg ; T3  -- T5   3.0148 A

T3  -- O9  -- T5  = 141.887 deg ; T3  -- T5   3.0592 A

T4  -- O10 -- T4  = 135.077 deg ; T4  -- T4   2.9990 A

T4  -- O11 -- T4  = 139.062 deg ; T4  -- T4   3.0372 A

T5  -- O12 -- T5  = 135.052 deg ; T5  -- T5   2.9981 A

T5  -- O13 -- T5  = 137.316 deg ; T5  -- T5   3.0204 A


        T-O-T SUMMARY
          Range  = 131.6080° <--> 150.1647 deg
          Mean   = 139.8386 deg
          StdDev = 5.2942 deg

        T--T SUMMARY
          Range  = 2.9661 A <--> 3.1294 A
          Mean   = 3.0419 A
          StdDev = 0.0462 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 17 32 52 70 103 136 162 204 250 294 347 406 458 514
TD10 = 791
Circuit symbol = 3.6.5.5.5.5
Weight = 16
Vertex symbol  = 3.6.5.5.5.5
Weight = 16

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 11 20 33 52 74 102 134 167 206 251 299 346 399 463 526
TD10 = 804
Circuit symbol = 4.5.5.8_{5}.6.6_{2}
Weight = 21
Vertex symbol  = 4.5.5.8_{2}.6.6_{2}
Weight = 21

T3 (Si): multiplicity = 12
Coordination Sequence =
    1 4 11 20 33 52 74 102 134 167 206 251 299 346 399 463 526
TD10 = 804
Circuit symbol = 4.5.5.8_{5}.6.6_{2}
Weight = 21
Vertex symbol  = 4.5.5.8_{2}.6.6_{2}
Weight = 21

T4 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 33 50 73 101 133 168 207 250 296 348 403 457 521
TD10 = 800
Circuit symbol = 4.5.4.6.6_{2}.7
Weight = 15
Vertex symbol  = 4.5.4.6.6.10
Weight = 21

T5 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 33 50 73 101 133 168 207 250 296 348 403 457 521
TD10 = 800
Circuit symbol = 4.5.4.6.6_{2}.7
Weight = 15
Vertex symbol  = 4.5.4.6.6.10
Weight = 21

<TD10> = 799.800
Average ring size = 5.3403