Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_189_5_16660488_C4IjqU.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 20.06 T-atoms per nm^3
Material density = 2.001 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5612 Angstrom
T1  -- O2  = 1.6083 Angstrom
T1  -- O2  = 1.6083 Angstrom
T1  -- O2  = 1.6083 Angstrom
      mean = 1.5966 Angstrom
        t1 = 0.029725  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.025475  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6427 Angstrom
T2  -- O4  = 1.6138 Angstrom
T2  -- O4  = 1.6138 Angstrom
T2  -- O4  = 1.6139 Angstrom
      mean = 1.6210 Angstrom
        t1 = 0.017433  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.014332  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O5  = 1.6179 Angstrom
T3  -- O6  = 1.6149 Angstrom
T3  -- O6  = 1.6149 Angstrom
T3  -- O7  = 1.6096 Angstrom
      mean = 1.6143 Angstrom
        t1 = 0.005563  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003088  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O2  = 1.5523 Angstrom
T4  -- O4  = 1.6083 Angstrom
T4  -- O8  = 1.6170 Angstrom
T4  -- O4  = 1.6083 Angstrom
      mean = 1.5965 Angstrom
        t1 = 0.020875  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.021696  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O6  = 1.6152 Angstrom
T5  -- O7  = 1.6124 Angstrom
T5  -- O8  = 1.6078 Angstrom
T5  -- O6  = 1.6152 Angstrom
      mean = 1.6126 Angstrom
        t1 = 0.010155  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.007749  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5523 A <--> 1.6427 A
          Mean   = 1.6091 A
          StdDev = 0.0179 A

       t1 Range  = 0.0056 <-- 0.0168 --> 0.0297
       t2 Range  = 0.0031 <-- 0.0145 --> 0.0255

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 105.932 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 105.932 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 105.932 deg; O1  -- O2  = 3 A
O2  -- T1  -- O2  = 112.766 deg; O2  -- O2  = 3 A
O2  -- T1  -- O2  = 112.766 deg; O2  -- O2  = 3 A
O2  -- T1  -- O2  = 112.766 deg; O2  -- O2  = 3 A
       105.932 deg <-- 109.349 deg --> 112.766 deg

O3  -- T2  -- O4  = 111.313 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 111.313 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 111.312 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  = 107.570 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 107.566 deg; O4  -- O4  = 3 A
O4  -- T2  -- O4  = 107.568 deg; O4  -- O4  = 3 A
       107.566 deg <-- 109.441 deg --> 111.313 deg

O5  -- T3  -- O6  = 109.238 deg; O5  -- O6  = 3 A
O5  -- T3  -- O6  = 109.238 deg; O5  -- O6  = 3 A
O5  -- T3  -- O7  = 108.623 deg; O5  -- O7  = 3 A
O6  -- T3  -- O6  = 111.063 deg; O6  -- O6  = 3 A
O6  -- T3  -- O7  = 109.319 deg; O6  -- O7  = 3 A
O6  -- T3  -- O7  = 109.319 deg; O6  -- O7  = 3 A
       108.623 deg <-- 109.467 deg --> 111.063 deg

O2  -- T4  -- O4  = 109.150 deg; O2  -- O4  = 3 A
O2  -- T4  -- O8  = 106.084 deg; O2  -- O8  = 3 A
O2  -- T4  -- O4  = 109.150 deg; O2  -- O4  = 3 A
O4  -- T4  -- O8  = 111.620 deg; O4  -- O8  = 3 A
O4  -- T4  -- O4  = 109.131 deg; O4  -- O4  = 3 A
O8  -- T4  -- O4  = 111.620 deg; O8  -- O4  = 3 A
       106.084 deg <-- 109.459 deg --> 111.620 deg

O6  -- T5  -- O7  = 110.281 deg; O6  -- O7  = 3 A
O6  -- T5  -- O8  = 110.730 deg; O6  -- O8  = 3 A
O6  -- T5  -- O6  = 108.328 deg; O6  -- O6  = 3 A
O7  -- T5  -- O8  = 106.498 deg; O7  -- O8  = 3 A
O7  -- T5  -- O6  = 110.281 deg; O7  -- O6  = 3 A
O8  -- T5  -- O6  = 110.730 deg; O8  -- O6  = 3 A
       106.498 deg <-- 109.475 deg --> 110.730 deg

        O-T-O SUMMARY
          Range  = 105.9322 deg <--> 112.7664 deg
          Mean   = 109.5880 deg
          StdDev = 1.8213 deg

        O--O SUMMARY
          Range  = 2.5304 A <--> 2.6889 A
          Mean   = 2.6307 A
          StdDev = 0.0437 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T4  - O1  - T1  - O2  - T4  = 107.951 deg; T4  -- T4  = 5.0921 A
T4  - O1  - T1  - O2  - T4  = 107.951 deg; T4  -- T4  = 5.0921 A
T4  - O1  - T1  - O2  - T1  = 110.951 deg; T4  -- T1  = 5.1662 A
T4  - O2  - T1  - O2  - T4  = 107.951 deg; T4  -- T4  = 5.0921 A
T4  - O2  - T1  - O2  - T1  = 110.951 deg; T4  -- T1  = 5.1662 A
T4  - O2  - T1  - O2  - T1  = 110.951 deg; T4  -- T1  = 5.1662 A

T4  - O3  - T2  - O4  - T4  = 110.009 deg; T4  -- T4  = 5.2743 A
T4  - O3  - T2  - O4  - T2  = 108.927 deg; T4  -- T2  = 5.2932 A
T4  - O3  - T2  - O4  - T4  = 110.011 deg; T4  -- T4  = 5.2743 A
T4  - O4  - T2  - O4  - T2  = 108.926 deg; T4  -- T2  = 5.2933 A
T4  - O4  - T2  - O4  - T4  = 110.010 deg; T4  -- T4  = 5.2743 A
T2  - O4  - T2  - O4  - T4  = 108.927 deg; T2  -- T4  = 5.2932 A

T3  - O5  - T3  - O6  - T5  = 108.875 deg; T3  -- T5  = 5.1703 A
T3  - O5  - T3  - O6  - T5  = 108.875 deg; T3  -- T5  = 5.1703 A
T3  - O5  - T3  - O7  - T5  = 109.291 deg; T3  -- T5  = 5.1292 A
T5  - O6  - T3  - O6  - T5  = 104.826 deg; T5  -- T5  = 5.0853 A
T5  - O6  - T3  - O7  - T5  = 112.408 deg; T5  -- T5  = 5.2777 A
T5  - O6  - T3  - O7  - T5  = 112.408 deg; T5  -- T5  = 5.2777 A

T1  - O2  - T4  - O4  - T2  = 109.926 deg; T1  -- T2  = 5.2135 A
T1  - O2  - T4  - O8  - T5  = 110.881 deg; T1  -- T5  = 5.2077 A
T1  - O2  - T4  - O4  - T2  = 109.925 deg; T1  -- T2  = 5.2134 A
T2  - O4  - T4  - O8  - T5  = 108.963 deg; T2  -- T5  = 5.2048 A
T2  - O4  - T4  - O4  - T2  = 108.125 deg; T2  -- T2  = 5.2128 A
T5  - O8  - T4  - O4  - T2  = 108.963 deg; T5  -- T2  = 5.2048 A

T3  - O6  - T5  - O7  - T3  = 107.266 deg; T3  -- T3  = 5.1140 A
T3  - O6  - T5  - O8  - T4  = 108.907 deg; T3  -- T4  = 5.1945 A
T3  - O6  - T5  - O6  - T3  = 115.139 deg; T3  -- T3  = 5.4166 A
T3  - O7  - T5  - O8  - T4  = 109.221 deg; T3  -- T4  = 5.1503 A
T3  - O7  - T5  - O6  - T3  = 107.266 deg; T3  -- T3  = 5.1140 A
T4  - O8  - T5  - O6  - T3  = 108.907 deg; T4  -- T3  = 5.1945 A

        T-T-T SUMMARY
          Range  = 104.8260 deg <--> 115.1387 deg
          Mean   = 109.4369 deg
          StdDev = 1.9260 deg

        T--T SUMMARY
          Range  = 5.0853 A <--> 5.4166 A
          Mean   = 5.2117 A
          StdDev = 0.0772 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.1224 A

T1  -- O2  -- T4  = 169.779 deg ; T1  -- T4   3.1480 A

T2  -- O3  -- T2  = 180.000 deg ; T2  -- T2   3.2855 A

T2  -- O4  -- T4  = 175.052 deg ; T2  -- T4   3.2191 A

T3  -- O5  -- T3  = 153.061 deg ; T3  -- T3   3.1468 A

T3  -- O6  -- T5  = 166.812 deg ; T3  -- T5   3.2087 A

T3  -- O7  -- T5  = 154.419 deg ; T3  -- T5   3.1421 A

T4  -- O8  -- T5  = 159.945 deg ; T4  -- T5   3.1755 A


        T-O-T SUMMARY
          Range  = 153.0606° <--> 180.0000 deg
          Mean   = 165.5811 deg
          StdDev = 9.6008 deg

        T--T SUMMARY
          Range  = 3.1224 A <--> 3.2855 A
          Mean   = 3.1816 A
          StdDev = 0.0460 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 2
Coordination Sequence =
    1 4 12 24 42 66 96 130 170 214 264 318 378 444 516 592 674
TD10 = 1023
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 24 42 66 96 130 170 214 264 318 378 444 516 592 674
TD10 = 1023
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29

T3 (Si): multiplicity = 6
Coordination Sequence =
    1 4 12 24 42 66 96 130 170 214 264 318 378 444 516 592 674
TD10 = 1023
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29

T4 (Si): multiplicity = 6
Coordination Sequence =
    1 4 12 25 44 67 96 130 170 214 264 319 380 445 516 592 674
TD10 = 1027
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27

T5 (Si): multiplicity = 6
Coordination Sequence =
    1 4 12 25 44 67 96 130 170 214 264 319 380 445 516 592 674
TD10 = 1027
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27

<TD10> = 1025.000
Average ring size = 6.0000