Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_189_5_15504738_QmMh5P.cif"

There are 40 T-atoms per unit cell
There are 80 O-atoms per unit cell

Framework density = 20.99 T-atoms per nm^3
Material density = 2.094 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6183 Angstrom
T1  -- O2  = 1.6330 Angstrom
T1  -- O3  = 1.6486 Angstrom
T1  -- O4  = 1.6876 Angstrom
      mean = 1.6469 Angstrom
        t1 = 0.034706  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.019576  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6607 Angstrom
T2  -- O6  = 1.6340 Angstrom
T2  -- O7  = 1.6287 Angstrom
T2  -- O8  = 1.6648 Angstrom
      mean = 1.6471 Angstrom
        t1 = 0.041076  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.022181  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O7  = 1.6209 Angstrom
T3  -- O7  = 1.6209 Angstrom
T3  -- O7  = 1.6210 Angstrom
T3  -- O9  = 1.5325 Angstrom
      mean = 1.5988 Angstrom
        t1 = 0.059218  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.052489  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O4  = 1.6403 Angstrom
T4  -- O4  = 1.6403 Angstrom
T4  -- O10 = 1.5859 Angstrom
T4  -- O11 = 1.6344 Angstrom
      mean = 1.6252 Angstrom
        t1 = 0.046835  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037181  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O8  = 1.6301 Angstrom
T5  -- O11 = 1.6381 Angstrom
T5  -- O12 = 1.6581 Angstrom
T5  -- O8  = 1.6301 Angstrom
      mean = 1.6391 Angstrom
        t1 = 0.046408  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037546  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5325 A <--> 1.6876 A
          Mean   = 1.6377 A
          StdDev = 0.0274 A

       t1 Range  = 0.0347 <-- 0.0456 --> 0.0592
       t2 Range  = 0.0196 <-- 0.0338 --> 0.0525

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.766 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 107.975 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 106.532 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 109.560 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 107.019 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 116.744 deg; O3  -- O4  = 3 A
       106.532 deg <-- 109.433 deg --> 116.744 deg

O5  -- T2  -- O6  = 106.921 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 111.067 deg; O5  -- O7  = 3 A
O5  -- T2  -- O8  = 117.230 deg; O5  -- O8  = 3 A
O6  -- T2  -- O7  = 113.189 deg; O6  -- O7  = 3 A
O6  -- T2  -- O8  = 107.780 deg; O6  -- O8  = 3 A
O7  -- T2  -- O8  = 100.757 deg; O7  -- O8  = 3 A
       100.757 deg <-- 109.490 deg --> 117.230 deg

O7  -- T3  -- O7  = 116.044 deg; O7  -- O7  = 3 A
O7  -- T3  -- O7  = 116.038 deg; O7  -- O7  = 3 A
O7  -- T3  -- O9  = 101.636 deg; O7  -- O9  = 2 A
O7  -- T3  -- O7  = 116.036 deg; O7  -- O7  = 3 A
O7  -- T3  -- O9  = 101.635 deg; O7  -- O9  = 2 A
O7  -- T3  -- O9  = 101.635 deg; O7  -- O9  = 2 A
       101.635 deg <-- 108.837 deg --> 116.044 deg

O4  -- T4  -- O4  = 107.052 deg; O4  -- O4  = 3 A
O4  -- T4  -- O10 = 104.365 deg; O4  -- O10 = 3 A
O4  -- T4  -- O11 = 118.178 deg; O4  -- O11 = 3 A
O4  -- T4  -- O10 = 104.365 deg; O4  -- O10 = 3 A
O4  -- T4  -- O11 = 118.178 deg; O4  -- O11 = 3 A
O10 -- T4  -- O11 = 102.739 deg; O10 -- O11 = 3 A
       102.739 deg <-- 109.146 deg --> 118.178 deg

O8  -- T5  -- O11 = 109.129 deg; O8  -- O11 = 3 A
O8  -- T5  -- O12 = 115.472 deg; O8  -- O12 = 3 A
O8  -- T5  -- O8  =  96.852 deg; O8  -- O8  = 2 A
O11 -- T5  -- O12 = 110.008 deg; O11 -- O12 = 3 A
O11 -- T5  -- O8  = 109.129 deg; O11 -- O8  = 3 A
O12 -- T5  -- O8  = 115.472 deg; O12 -- O8  = 3 A
       96.852 deg <-- 109.344 deg --> 115.472 deg

        O-T-O SUMMARY
          Range  = 96.8516 deg <--> 118.1782 deg
          Mean   = 109.4266 deg
          StdDev = 6.1106 deg

        O--O SUMMARY
          Range  = 2.4389 A <--> 2.8408 A
          Mean   = 2.6599 A
          StdDev = 0.1233 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T4  =  57.247 deg; T1  -- T4  = 2.7453 A
T1  - O1  - T1  - O3  - T1  = 120.000 deg; T1  -- T1  = 4.9892 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.2706 A
T4  - O2  - T1  - O3  - T1  = 177.246 deg; T4  -- T1  = 5.5333 A
T4  - O2  - T1  - O4  - T1  =  89.925 deg; T4  -- T1  = 4.1144 A
T1  - O3  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.1467 A

T2  - O5  - T2  - O6  - T3  =  91.740 deg; T2  -- T3  = 4.0963 A
T2  - O5  - T2  - O7  - T5  = 147.992 deg; T2  -- T5  = 5.4114 A
T2  - O5  - T2  - O8  - T2  =  90.000 deg; T2  -- T2  = 3.9923 A
T3  - O6  - T2  - O7  - T5  = 119.659 deg; T3  -- T5  = 4.7962 A
T3  - O6  - T2  - O8  - T2  = 172.016 deg; T3  -- T2  = 5.5487 A
T5  - O7  - T2  - O8  - T2  =  59.823 deg; T5  -- T2  = 2.7352 A

T2  - O7  - T3  - O7  - T2  = 119.911 deg; T2  -- T2  = 4.8689 A
T2  - O7  - T3  - O7  - T2  = 119.907 deg; T2  -- T2  = 4.8689 A
T2  - O7  - T3  - O9  - T3  =  88.260 deg; T2  -- T3  = 4.0963 A
T2  - O7  - T3  - O7  - T2  = 119.907 deg; T2  -- T2  = 4.8689 A
T2  - O7  - T3  - O9  - T3  =  88.260 deg; T2  -- T3  = 4.0963 A
T2  - O7  - T3  - O9  - T3  =  88.260 deg; T2  -- T3  = 4.0964 A

T1  - O4  - T4  - O4  - T1  =  65.506 deg; T1  -- T1  = 2.9705 A
T1  - O4  - T4  - O10 - T5  = 147.247 deg; T1  -- T5  = 5.7726 A
T1  - O4  - T4  - O11 - T4  =  90.075 deg; T1  -- T4  = 4.1144 A
T1  - O4  - T4  - O10 - T5  = 147.247 deg; T1  -- T5  = 5.7726 A
T1  - O4  - T4  - O11 - T4  =  90.075 deg; T1  -- T4  = 4.1144 A
T5  - O10 - T4  - O11 - T4  =  90.024 deg; T5  -- T4  = 4.4796 A

T2  - O8  - T5  - O11 - T4  =  80.344 deg; T2  -- T4  = 3.8949 A
T2  - O8  - T5  - O12 - T2  =  60.355 deg; T2  -- T2  = 2.7499 A
T2  - O8  - T5  - O8  - T5  = 147.992 deg; T2  -- T5  = 5.5749 A
T4  - O11 - T5  - O12 - T2  =  80.344 deg; T4  -- T2  = 3.8949 A
T4  - O11 - T5  - O8  - T5  =  89.976 deg; T4  -- T5  = 4.4796 A
T2  - O12 - T5  - O8  - T5  = 147.992 deg; T2  -- T5  = 5.5749 A

        T-T-T SUMMARY
          Range  = 57.2470 deg <--> 177.2460 deg
          Mean   = 105.8899 deg
          StdDev = 31.9336 deg

        T--T SUMMARY
          Range  = 2.7352 A <--> 5.7726 A
          Mean   = 4.4370 A
          StdDev = 0.8744 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 142.874 deg ; T1  -- T1   3.0682 A

T1  -- O2  -- T1  = 130.881 deg ; T1  -- T1   2.9705 A

T1  -- O3  -- T1  = 115.563 deg ; T1  -- T1   2.7896 A

T1  -- O4  -- T4  = 111.154 deg ; T1  -- T4   2.7453 A

T2  -- O5  -- T2  = 121.232 deg ; T2  -- T2   2.8942 A

T2  -- O6  -- T2  = 114.590 deg ; T2  -- T2   2.7499 A

T2  -- O7  -- T3  = 119.867 deg ; T2  -- T3   2.8123 A

T2  -- O8  -- T5  = 112.224 deg ; T2  -- T5   2.7352 A

T3  -- O9  -- T3  = 180.000 deg ; T3  -- T3   3.0650 A

T4  -- O10 -- T4  = 149.625 deg ; T4  -- T4   3.0610 A

T4  -- O11 -- T5  = 175.060 deg ; T4  -- T5   3.2694 A

T5  -- O12 -- T5  = 135.000 deg ; T5  -- T5   3.0637 A


        T-O-T SUMMARY
          Range  = 111.1543° <--> 180.0000 deg
          Mean   = 127.9554 deg
          StdDev = 18.8805 deg

        T--T SUMMARY
          Range  = 2.7352 A <--> 3.2694 A
          Mean   = 2.8967 A
          StdDev = 0.1537 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T4  = 2.7453 Angstrom
T1  -- T1  = 2.7896 Angstrom
T2  -- T5  = 2.7352 Angstrom
T2  -- T2  = 2.7499 Angstrom
T4  -- T1  = 2.7453 Angstrom
T4  -- T1  = 2.7453 Angstrom
T5  -- T2  = 2.7352 Angstrom
T5  -- T2  = 2.7352 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 7 9 12 20 37 59 88 131 180 221 256 299 359 435 502
TD10 = 548
Circuit symbol = 3.4.4.6.4.6_{2}
Weight = 11
Vertex symbol  = 3.4.4.6.4.12
Weight = 20

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 8 16 29 49 73 94 120 159 204 249 289 344 415 469 530
TD10 = 757
Circuit symbol = 3.4.4.7.5.6
Weight = 7
Vertex symbol  = 3.4.4.10_{2}.12.16
Weight = 38

T3 (Si): multiplicity = 4
Coordination Sequence =
    1 4 9 15 30 55 80 100 123 166 218 253 300 364 413 478 558
TD10 = 801
Circuit symbol = 4.6.4.6.4.6
Weight = 8
Vertex symbol  = 4.10.4.10.4.10
Weight = 18

T4 (Si): multiplicity = 6
Coordination Sequence =
    1 4 7 12 17 27 45 69 106 141 174 220 267 319 380 433 506
TD10 = 603
Circuit symbol = 3.4.4.6.4.6
Weight = 8
Vertex symbol  = 3.4.4.12.4.12
Weight = 26

T5 (Si): multiplicity = 6
Coordination Sequence =
    1 4 9 15 27 41 61 97 130 157 190 236 299 361 404 467 546
TD10 = 732
Circuit symbol = 3.4.10_{2}.12_{3}.10_{2}.12_{3}
Weight = 42
Vertex symbol  = 3.4.10_{2}.12.10_{2}.12
Weight = 42

<TD10> = 671.850
Average ring size = 5.4154