Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_189_5_1477290_U2Huo3.cif"

There are 60 T-atoms per unit cell
There are 120 O-atoms per unit cell

Framework density = 20.32 T-atoms per nm^3
Material density = 2.027 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6134 Angstrom
T1  -- O1  = 1.6038 Angstrom
T1  -- O2  = 1.6335 Angstrom
T1  -- O3  = 1.6160 Angstrom
      mean = 1.6167 Angstrom
        t1 = 0.032608  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.020521  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6412 Angstrom
T2  -- O4  = 1.5919 Angstrom
T2  -- O5  = 1.6730 Angstrom
T2  -- O6  = 1.6210 Angstrom
      mean = 1.6318 Angstrom
        t1 = 0.039974  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.049996  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O5  = 1.6968 Angstrom
T3  -- O7  = 1.6517 Angstrom
T3  -- O8  = 1.6485 Angstrom
T3  -- O9  = 1.6424 Angstrom
      mean = 1.6598 Angstrom
        t1 = 0.033393  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.009881  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O6  = 1.6251 Angstrom
T4  -- O10 = 1.6175 Angstrom
T4  -- O11 = 1.5870 Angstrom
T4  -- O12 = 1.6184 Angstrom
      mean = 1.6120 Angstrom
        t1 = 0.010145  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008109  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O9  = 1.6438 Angstrom
T5  -- O11 = 1.5949 Angstrom
T5  -- O12 = 1.6133 Angstrom
T5  -- O13 = 1.6262 Angstrom
      mean = 1.6196 Angstrom
        t1 = 0.018646  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.014348  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5870 A <--> 1.6968 A
          Mean   = 1.6280 A
          StdDev = 0.0264 A

       t1 Range  = 0.0101 <-- 0.0270 --> 0.0400
       t2 Range  = 0.0081 <-- 0.0206 --> 0.0500

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 108.697 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 108.687 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  99.741 deg; O1  -- O3  = 2 A
O1  -- T1  -- O2  = 109.596 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 115.097 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 114.323 deg; O2  -- O3  = 3 A
       99.741 deg <-- 109.357 deg --> 115.097 deg

O3  -- T2  -- O4  = 108.116 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 118.328 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 108.046 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 103.937 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 105.458 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 112.079 deg; O5  -- O6  = 3 A
       103.937 deg <-- 109.327 deg --> 118.328 deg

O5  -- T3  -- O7  = 111.549 deg; O5  -- O7  = 3 A
O5  -- T3  -- O8  = 109.757 deg; O5  -- O8  = 3 A
O5  -- T3  -- O9  = 107.893 deg; O5  -- O9  = 3 A
O7  -- T3  -- O8  = 110.189 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 108.708 deg; O7  -- O9  = 3 A
O8  -- T3  -- O9  = 108.666 deg; O8  -- O9  = 3 A
       107.893 deg <-- 109.460 deg --> 111.549 deg

O6  -- T4  -- O10 = 110.639 deg; O6  -- O10 = 3 A
O6  -- T4  -- O11 = 111.371 deg; O6  -- O11 = 3 A
O6  -- T4  -- O12 = 107.014 deg; O6  -- O12 = 3 A
O10 -- T4  -- O11 = 108.198 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 110.151 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 109.468 deg; O11 -- O12 = 3 A
       107.014 deg <-- 109.473 deg --> 111.371 deg

O9  -- T5  -- O11 = 110.752 deg; O9  -- O11 = 3 A
O9  -- T5  -- O12 = 110.847 deg; O9  -- O12 = 3 A
O9  -- T5  -- O13 = 111.053 deg; O9  -- O13 = 3 A
O11 -- T5  -- O12 = 105.470 deg; O11 -- O12 = 3 A
O11 -- T5  -- O13 = 109.379 deg; O11 -- O13 = 3 A
O12 -- T5  -- O13 = 109.176 deg; O12 -- O13 = 3 A
       105.470 deg <-- 109.446 deg --> 111.053 deg

        O-T-O SUMMARY
          Range  = 99.7414 deg <--> 118.3278 deg
          Mean   = 109.3997 deg
          StdDev = 3.3513 deg

        O--O SUMMARY
          Range  = 2.4691 A <--> 2.8457 A
          Mean   = 2.6558 A
          StdDev = 0.0717 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T1  =  60.000 deg; T1  -- T1  = 2.9298 A
T1  - O1  - T1  - O2  - T2  = 115.493 deg; T1  -- T2  = 5.0387 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.0322 A
T1  - O1  - T1  - O2  - T2  =  91.310 deg; T1  -- T2  = 4.2612 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.0322 A
T2  - O2  - T1  - O3  - T1  = 151.032 deg; T2  -- T1  = 5.6144 A

T1  - O3  - T2  - O4  - T3  = 127.960 deg; T1  -- T3  = 5.3682 A
T1  - O3  - T2  - O5  - T4  = 126.826 deg; T1  -- T4  = 5.2522 A
T1  - O3  - T2  - O6  - T2  = 105.170 deg; T1  -- T2  = 4.7583 A
T3  - O4  - T2  - O5  - T4  = 101.129 deg; T3  -- T4  = 4.4725 A
T3  - O4  - T2  - O6  - T2  =  92.493 deg; T3  -- T2  = 4.2678 A
T4  - O5  - T2  - O6  - T2  =  89.866 deg; T4  -- T2  = 4.1025 A

T2  - O5  - T3  - O7  - T3  = 148.794 deg; T2  -- T3  = 5.9565 A
T2  - O5  - T3  - O8  - T5  =  77.833 deg; T2  -- T5  = 3.8642 A
T2  - O5  - T3  - O9  - T3  =  87.507 deg; T2  -- T3  = 4.2678 A
T3  - O7  - T3  - O8  - T5  = 107.282 deg; T3  -- T5  = 5.1832 A
T3  - O7  - T3  - O9  - T3  = 120.000 deg; T3  -- T3  = 5.5922 A
T5  - O8  - T3  - O9  - T3  = 102.423 deg; T5  -- T3  = 5.0017 A

T2  - O6  - T4  - O10 - T4  =  90.134 deg; T2  -- T4  = 4.1025 A
T2  - O6  - T4  - O11 - T5  = 132.923 deg; T2  -- T5  = 5.4203 A
T2  - O6  - T4  - O12 - T5  =  84.225 deg; T2  -- T5  = 3.8642 A
T4  - O10 - T4  - O11 - T5  = 110.907 deg; T4  -- T5  = 4.9559 A
T4  - O10 - T4  - O12 - T5  = 106.380 deg; T4  -- T5  = 4.6971 A
T5  - O11 - T4  - O12 - T5  = 125.227 deg; T5  -- T5  = 5.3139 A

T3  - O9  - T5  - O11 - T4  =  89.170 deg; T3  -- T4  = 4.3986 A
T3  - O9  - T5  - O12 - T4  =  93.892 deg; T3  -- T4  = 4.4725 A
T3  - O9  - T5  - O13 - T5  = 149.044 deg; T3  -- T5  = 5.9166 A
T4  - O11 - T5  - O12 - T4  =  92.236 deg; T4  -- T4  = 4.3144 A
T4  - O11 - T5  - O13 - T5  = 108.818 deg; T4  -- T5  = 4.8860 A
T4  - O12 - T5  - O13 - T5  = 109.822 deg; T4  -- T5  = 4.7936 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 151.0320 deg
          Mean   = 105.9069 deg
          StdDev = 21.7064 deg

        T--T SUMMARY
          Range  = 2.9298 A <--> 5.9565 A
          Mean   = 4.6962 A
          StdDev = 0.6854 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 131.196 deg ; T1  -- T1   2.9298 A

T1  -- O2  -- T1  = 115.985 deg ; T1  -- T1   2.7704 A

T1  -- O3  -- T2  = 136.749 deg ; T1  -- T2   3.0279 A

T2  -- O4  -- T2  = 137.043 deg ; T2  -- T2   2.9628 A

T2  -- O5  -- T3  = 121.881 deg ; T2  -- T3   2.9456 A

T2  -- O6  -- T4  = 122.403 deg ; T2  -- T4   2.8446 A

T3  -- O7  -- T3  = 157.215 deg ; T3  -- T3   3.2383 A

T3  -- O8  -- T3  = 155.035 deg ; T3  -- T3   3.2190 A

T3  -- O9  -- T5  = 153.361 deg ; T3  -- T5   3.1978 A

T4  -- O10 -- T4  = 131.492 deg ; T4  -- T4   2.9494 A

T4  -- O11 -- T5  = 149.094 deg ; T4  -- T5   3.0668 A

T4  -- O12 -- T5  = 129.036 deg ; T4  -- T5   2.9173 A

T5  -- O13 -- T5  = 129.438 deg ; T5  -- T5   2.9410 A


        T-O-T SUMMARY
          Range  = 115.9850° <--> 157.2148 deg
          Mean   = 136.1483 deg
          StdDev = 13.0697 deg

        T--T SUMMARY
          Range  = 2.7704 A <--> 3.2383 A
          Mean   = 3.0008 A
          StdDev = 0.1386 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.7704 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 8 17 31 50 78 112 148 174 202 252 309 376 450 514 573
TD10 = 825
Circuit symbol = 3.8.4.7_{2}.4.7_{2}
Weight = 21
Vertex symbol  = 3.8.4.7_{2}.4.7_{2}
Weight = 21

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 9 19 34 54 80 105 138 182 217 257 316 375 439 508 573
TD10 = 843
Circuit symbol = 4.7.4.7_{3}.4.8
Weight = 21
Vertex symbol  = 4.7.4.7_{3}.4.8
Weight = 21

T3 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 22 39 57 77 101 135 182 235 284 322 366 426 499 586
TD10 = 863
Circuit symbol = 4.6.4.6.6_{3}.8_{2}
Weight = 15
Vertex symbol  = 4.6.4.6.6_{2}.12_{2}
Weight = 28

T4 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 22 36 51 76 106 137 174 218 262 308 377 443 489 549
TD10 = 835
Circuit symbol = 4.6.4.6_{2}.6_{3}.7_{2}
Weight = 21
Vertex symbol  = 4.6.4.6_{2}.6_{2}.7_{2}
Weight = 21

T5 (Si): multiplicity = 12
Coordination Sequence =
    1 4 11 22 35 53 77 105 140 178 216 269 331 380 434 497 554
TD10 = 842
Circuit symbol = 4.6.6.6.6.8_{5}
Weight = 25
Vertex symbol  = 4.6.6.6.6.8_{4}
Weight = 25

<TD10> = 841.600
Average ring size = 5.7180