Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_189_5_1408918_6ds8qN.cif"

There are 60 T-atoms per unit cell
There are 120 O-atoms per unit cell

Framework density = 24.17 T-atoms per nm^3
Material density = 2.411 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5263 Angstrom
T1  -- O1  = 1.5203 Angstrom
T1  -- O2  = 1.6189 Angstrom
T1  -- O3  = 1.7542 Angstrom
      mean = 1.6049 Angstrom
        t1 = 0.233883  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.156530  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.7911 Angstrom
T2  -- O4  = 1.7450 Angstrom
T2  -- O5  = 1.5717 Angstrom
T2  -- O6  = 1.6702 Angstrom
      mean = 1.6945 Angstrom
        t1 = 0.099723  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.061278  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O5  = 1.5905 Angstrom
T3  -- O7  = 1.6153 Angstrom
T3  -- O8  = 1.5798 Angstrom
T3  -- O9  = 1.6019 Angstrom
      mean = 1.5969 Angstrom
        t1 = 0.019730  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.018549  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O6  = 1.6236 Angstrom
T4  -- O10 = 1.6054 Angstrom
T4  -- O11 = 1.6052 Angstrom
T4  -- O12 = 1.6084 Angstrom
      mean = 1.6106 Angstrom
        t1 = 0.014061  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.017709  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O9  = 1.6043 Angstrom
T5  -- O11 = 1.5852 Angstrom
T5  -- O12 = 1.6181 Angstrom
T5  -- O13 = 1.6172 Angstrom
      mean = 1.6062 Angstrom
        t1 = 0.015249  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.011278  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5203 A <--> 1.7911 A
          Mean   = 1.6226 A
          StdDev = 0.0677 A

       t1 Range  = 0.0141 <-- 0.0765 --> 0.2339
       t2 Range  = 0.0113 <-- 0.0531 --> 0.1565

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  =  73.264 deg; O1  -- O1  = 2 A
O1  -- T1  -- O2  = 107.468 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 122.413 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 115.130 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  49.534 deg; O1  -- O3  = 1 A
O2  -- T1  -- O3  = 102.667 deg; O2  -- O3  = 3 A
       49.534 deg <-- 95.080 deg --> 122.413 deg

O3  -- T2  -- O4  = 127.154 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 102.178 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 115.761 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 101.458 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 105.470 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 100.187 deg; O5  -- O6  = 2 A
       100.187 deg <-- 108.701 deg --> 127.154 deg

O5  -- T3  -- O7  = 109.744 deg; O5  -- O7  = 3 A
O5  -- T3  -- O8  = 106.886 deg; O5  -- O8  = 3 A
O5  -- T3  -- O9  = 113.700 deg; O5  -- O9  = 3 A
O7  -- T3  -- O8  = 110.609 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 109.672 deg; O7  -- O9  = 3 A
O8  -- T3  -- O9  = 106.137 deg; O8  -- O9  = 3 A
       106.137 deg <-- 109.458 deg --> 113.700 deg

O6  -- T4  -- O10 = 109.241 deg; O6  -- O10 = 3 A
O6  -- T4  -- O11 = 113.046 deg; O6  -- O11 = 3 A
O6  -- T4  -- O12 = 110.293 deg; O6  -- O12 = 3 A
O10 -- T4  -- O11 = 106.631 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 108.605 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 108.877 deg; O11 -- O12 = 3 A
       106.631 deg <-- 109.449 deg --> 113.046 deg

O9  -- T5  -- O11 = 107.586 deg; O9  -- O11 = 3 A
O9  -- T5  -- O12 = 110.479 deg; O9  -- O12 = 3 A
O9  -- T5  -- O13 = 110.909 deg; O9  -- O13 = 3 A
O11 -- T5  -- O12 = 106.096 deg; O11 -- O12 = 3 A
O11 -- T5  -- O13 = 111.706 deg; O11 -- O13 = 3 A
O12 -- T5  -- O13 = 109.939 deg; O12 -- O13 = 3 A
       106.096 deg <-- 109.453 deg --> 111.706 deg

        O-T-O SUMMARY
          Range  = 49.5343 deg <--> 127.1540 deg
          Mean   = 106.3572 deg
          StdDev = 13.7002 deg

        O--O SUMMARY
          Range  = 1.3881 A <--> 3.1667 A
          Mean   = 2.5844 A
          StdDev = 0.3005 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 130.183 deg ; T1  -- T1   2.7633 A

T1  -- O2  -- T1  = 167.604 deg ; T1  -- T1   3.2189 A

T1  -- O3  -- T2  = 141.447 deg ; T1  -- T2   3.3465 A

T2  -- O4  -- T2  = 127.589 deg ; T2  -- T2   3.1313 A

T2  -- O5  -- T3  = 149.966 deg ; T2  -- T3   3.0541 A

T2  -- O6  -- T4  = 160.948 deg ; T2  -- T4   3.2483 A

T3  -- O7  -- T3  = 119.215 deg ; T3  -- T3   2.7866 A

T3  -- O8  -- T3  = 138.162 deg ; T3  -- T3   2.9513 A

T3  -- O9  -- T5  = 124.984 deg ; T3  -- T5   2.8437 A

T4  -- O10 -- T4  = 119.829 deg ; T4  -- T4   2.7782 A

T4  -- O11 -- T5  = 120.749 deg ; T4  -- T5   2.7734 A

T4  -- O12 -- T5  = 122.253 deg ; T4  -- T5   2.8254 A

T5  -- O13 -- T5  = 131.256 deg ; T5  -- T5   2.9461 A


        T-O-T SUMMARY
          Range  = 119.2151° <--> 167.6036 deg
          Mean   = 134.9372 deg
          StdDev = 15.3644 deg

        T--T SUMMARY
          Range  = 2.7633 A <--> 3.3465 A
          Mean   = 2.9744 A
          StdDev = 0.1975 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O1  = 1.8179 A
O1  -- O1  = 1.8179 A
O1  -- O3  = 1.3881 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T1  = 2.7633 Angstrom
  T1  -- T1  = 2.7633 Angstrom
  T1  -- T2  = 2.4170 Angstrom
  T1  -- T2  = 3.3465 Angstrom
  T1  -- T1  = 3.2189 Angstrom
T2  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 2.4170 Angstrom
  T2  -- T1  = 3.3465 Angstrom
  T2  -- T2  = 3.1313 Angstrom
  T2  -- T3  = 3.0541 Angstrom
  T2  -- T4  = 3.2483 Angstrom
T3  -- T3  = 2.7866 Angstrom
T4  -- T4  = 2.7782 Angstrom
T4  -- T5  = 2.7734 Angstrom
T5  -- T4  = 2.7734 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 8 17 31 50 78 112 148 174 202 252 309 376 450 514 573
TD10 = 825
Circuit symbol = 3.8.4.7_{2}.4.7_{2}
Weight = 21
Vertex symbol  = 3.8.4.7_{2}.4.7_{2}
Weight = 21

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 9 19 34 54 80 105 138 182 217 257 316 375 439 508 573
TD10 = 843
Circuit symbol = 4.7.4.7_{3}.4.8
Weight = 21
Vertex symbol  = 4.7.4.7_{3}.4.8
Weight = 21

T3 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 22 39 57 77 101 135 182 235 284 322 366 426 499 586
TD10 = 863
Circuit symbol = 4.6.4.6.6_{3}.8_{2}
Weight = 15
Vertex symbol  = 4.6.4.6.6_{2}.12_{2}
Weight = 28

T4 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 22 36 51 76 106 137 174 218 262 308 377 443 489 549
TD10 = 835
Circuit symbol = 4.6.4.6_{2}.6_{3}.7_{2}
Weight = 21
Vertex symbol  = 4.6.4.6_{2}.6_{2}.7_{2}
Weight = 21

T5 (Si): multiplicity = 12
Coordination Sequence =
    1 4 11 22 35 53 77 105 140 178 216 269 331 380 434 497 554
TD10 = 842
Circuit symbol = 4.6.6.6.6.8_{5}
Weight = 25
Vertex symbol  = 4.6.6.6.6.8_{4}
Weight = 25

<TD10> = 841.600
Average ring size = 5.7180