Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_189_5_13188456_PWpMOq.cif"

There are 48 T-atoms per unit cell
There are 96 O-atoms per unit cell

Framework density = 20.92 T-atoms per nm^3
Material density = 2.087 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6236 Angstrom
T1  -- O1  = 1.6234 Angstrom
T1  -- O2  = 1.6141 Angstrom
T1  -- O3  = 1.6012 Angstrom
      mean = 1.6156 Angstrom
        t1 = 0.004012  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002791  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6128 Angstrom
T2  -- O4  = 1.6236 Angstrom
T2  -- O5  = 1.6208 Angstrom
T2  -- O6  = 1.6146 Angstrom
      mean = 1.6180 Angstrom
        t1 = 0.005838  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001966  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6145 Angstrom
T3  -- O7  = 1.6270 Angstrom
T3  -- O7  = 1.6273 Angstrom
T3  -- O8  = 1.6028 Angstrom
      mean = 1.6179 Angstrom
        t1 = 0.007179  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.004760  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O3  = 1.6156 Angstrom
T4  -- O9  = 1.6243 Angstrom
T4  -- O10 = 1.6175 Angstrom
T4  -- O3  = 1.6156 Angstrom
      mean = 1.6182 Angstrom
        t1 = 0.006997  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003214  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O8  = 1.6151 Angstrom
T5  -- O8  = 1.6151 Angstrom
T5  -- O11 = 1.6258 Angstrom
T5  -- O12 = 1.6204 Angstrom
      mean = 1.6191 Angstrom
        t1 = 0.007693  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.003491  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6012 A <--> 1.6273 A
          Mean   = 1.6175 A
          StdDev = 0.0076 A

       t1 Range  = 0.0040 <-- 0.0063 --> 0.0077
       t2 Range  = 0.0020 <-- 0.0032 --> 0.0048

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 108.510 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 109.770 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.030 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 108.948 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.483 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 110.069 deg; O2  -- O3  = 3 A
       108.510 deg <-- 109.468 deg --> 110.069 deg

O2  -- T2  -- O4  = 109.260 deg; O2  -- O4  = 3 A
O2  -- T2  -- O5  = 109.515 deg; O2  -- O5  = 3 A
O2  -- T2  -- O6  = 109.175 deg; O2  -- O6  = 3 A
O4  -- T2  -- O5  = 109.961 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.174 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 109.737 deg; O5  -- O6  = 3 A
       109.174 deg <-- 109.471 deg --> 109.961 deg

O6  -- T3  -- O7  = 110.187 deg; O6  -- O7  = 3 A
O6  -- T3  -- O7  = 110.042 deg; O6  -- O7  = 3 A
O6  -- T3  -- O8  = 109.177 deg; O6  -- O8  = 3 A
O7  -- T3  -- O7  = 108.211 deg; O7  -- O7  = 3 A
O7  -- T3  -- O8  = 108.936 deg; O7  -- O8  = 3 A
O7  -- T3  -- O8  = 110.270 deg; O7  -- O8  = 3 A
       108.211 deg <-- 109.471 deg --> 110.270 deg

O3  -- T4  -- O9  = 108.322 deg; O3  -- O9  = 3 A
O3  -- T4  -- O10 = 109.905 deg; O3  -- O10 = 3 A
O3  -- T4  -- O3  = 109.910 deg; O3  -- O3  = 3 A
O9  -- T4  -- O10 = 110.445 deg; O9  -- O10 = 3 A
O9  -- T4  -- O3  = 108.322 deg; O9  -- O3  = 3 A
O10 -- T4  -- O3  = 109.905 deg; O10 -- O3  = 3 A
       108.322 deg <-- 109.468 deg --> 110.445 deg

O8  -- T5  -- O8  = 108.119 deg; O8  -- O8  = 3 A
O8  -- T5  -- O11 = 109.630 deg; O8  -- O11 = 3 A
O8  -- T5  -- O12 = 109.684 deg; O8  -- O12 = 3 A
O8  -- T5  -- O11 = 109.630 deg; O8  -- O11 = 3 A
O8  -- T5  -- O12 = 109.684 deg; O8  -- O12 = 3 A
O11 -- T5  -- O12 = 110.064 deg; O11 -- O12 = 3 A
       108.119 deg <-- 109.469 deg --> 110.064 deg

        O-T-O SUMMARY
          Range  = 108.1189 deg <--> 110.4445 deg
          Mean   = 109.4184 deg
          StdDev = 0.6343 deg

        O--O SUMMARY
          Range  = 2.6153 A <--> 2.6627 A
          Mean   = 2.6404 A
          StdDev = 0.0107 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T1  =  60.000 deg; T1  -- T1  = 2.9423 A
T1  - O1  - T1  - O2  - T2  = 112.712 deg; T1  -- T2  = 5.0698 A
T1  - O1  - T1  - O3  - T4  = 115.070 deg; T1  -- T4  = 5.1338 A
T1  - O1  - T1  - O2  - T2  = 123.957 deg; T1  -- T2  = 5.3755 A
T1  - O1  - T1  - O3  - T4  = 126.714 deg; T1  -- T4  = 5.4382 A
T2  - O2  - T1  - O3  - T4  = 107.164 deg; T2  -- T4  = 5.0593 A

T1  - O2  - T2  - O4  - T2  = 102.491 deg; T1  -- T2  = 4.7749 A
T1  - O2  - T2  - O5  - T3  = 111.410 deg; T1  -- T3  = 5.2181 A
T1  - O2  - T2  - O6  - T2  = 110.516 deg; T1  -- T2  = 5.1566 A
T2  - O4  - T2  - O5  - T3  = 104.230 deg; T2  -- T3  = 4.8518 A
T2  - O4  - T2  - O6  - T2  = 120.000 deg; T2  -- T2  = 5.2873 A
T3  - O5  - T2  - O6  - T2  = 107.971 deg; T3  -- T2  = 5.0954 A

T2  - O6  - T3  - O7  - T3  = 115.544 deg; T2  -- T3  = 5.1844 A
T2  - O6  - T3  - O7  - T3  = 121.261 deg; T2  -- T3  = 5.3407 A
T2  - O6  - T3  - O8  - T5  = 114.854 deg; T2  -- T5  = 5.3647 A
T3  - O7  - T3  - O7  - T3  =  60.000 deg; T3  -- T3  = 2.9571 A
T3  - O7  - T3  - O8  - T5  = 113.643 deg; T3  -- T5  = 5.1515 A
T3  - O7  - T3  - O8  - T5  = 119.245 deg; T3  -- T5  = 5.3096 A

T1  - O3  - T4  - O9  - T4  = 104.089 deg; T1  -- T4  = 4.6945 A
T1  - O3  - T4  - O10 - T4  = 111.552 deg; T1  -- T4  = 5.1002 A
T1  - O3  - T4  - O3  - T1  = 104.103 deg; T1  -- T1  = 4.9538 A
T4  - O9  - T4  - O10 - T4  = 120.000 deg; T4  -- T4  = 5.0534 A
T4  - O9  - T4  - O3  - T1  = 104.089 deg; T4  -- T1  = 4.6945 A
T4  - O10 - T4  - O3  - T1  = 111.552 deg; T4  -- T1  = 5.1002 A

T3  - O8  - T5  - O8  - T3  = 117.202 deg; T3  -- T3  = 5.4557 A
T3  - O8  - T5  - O11 - T5  = 103.049 deg; T3  -- T5  = 4.9221 A
T3  - O8  - T5  - O12 - T5  = 107.082 deg; T3  -- T5  = 5.1505 A
T3  - O8  - T5  - O11 - T5  = 103.049 deg; T3  -- T5  = 4.9221 A
T3  - O8  - T5  - O12 - T5  = 107.082 deg; T3  -- T5  = 5.1505 A
T5  - O11 - T5  - O12 - T5  = 120.000 deg; T5  -- T5  = 5.4552 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 126.7142 deg
          Mean   = 108.1255 deg
          StdDev = 14.9040 deg

        T--T SUMMARY
          Range  = 2.9423 A <--> 5.4557 A
          Mean   = 4.9663 A
          StdDev = 0.5952 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 129.956 deg ; T1  -- T1   2.9423 A

T1  -- O2  -- T2  = 154.296 deg ; T1  -- T2   3.1461 A

T1  -- O3  -- T4  = 155.088 deg ; T1  -- T4   3.1411 A

T2  -- O4  -- T2  = 132.773 deg ; T2  -- T2   2.9754 A

T2  -- O5  -- T2  = 149.732 deg ; T2  -- T2   3.1293 A

T2  -- O6  -- T3  = 158.058 deg ; T2  -- T3   3.1701 A

T3  -- O7  -- T3  = 130.645 deg ; T3  -- T3   2.9571 A

T3  -- O8  -- T5  = 166.585 deg ; T3  -- T5   3.1959 A

T4  -- O9  -- T4  = 119.552 deg ; T4  -- T4   2.8070 A

T4  -- O10 -- T4  = 138.663 deg ; T4  -- T4   3.0267 A

T5  -- O11 -- T5  = 143.804 deg ; T5  -- T5   3.0908 A

T5  -- O12 -- T5  = 163.675 deg ; T5  -- T5   3.2080 A


        T-O-T SUMMARY
          Range  = 119.5522° <--> 166.5851 deg
          Mean   = 145.9980 deg
          StdDev = 13.9792 deg

        T--T SUMMARY
          Range  = 2.8070 A <--> 3.2080 A
          Mean   = 3.0723 A
          StdDev = 0.1116 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 24 44 64 100 122 164 214 264 322 362 432 512 600 672
TD10 = 1011
Circuit symbol = 3.6_{2}.6.6.6.6
Weight = 21
Vertex symbol  = 3.6_{2}.6.6.6.6
Weight = 21

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 12 25 42 66 94 131 170 208 258 312 382 447 502 578 658
TD10 = 1011
Circuit symbol = 6.6.6.6.6.6_{2}
Weight = 24
Vertex symbol  = 6.6.6.6.6.6_{2}
Weight = 24

T3 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 24 44 64 100 122 164 214 264 322 362 432 512 600 672
TD10 = 1011
Circuit symbol = 3.6_{2}.6.6.6.6
Weight = 21
Vertex symbol  = 3.6_{2}.6.6.6.6
Weight = 21

T4 (Si): multiplicity = 6
Coordination Sequence =
    1 4 12 25 42 66 94 131 170 208 258 312 382 447 502 578 658
TD10 = 1011
Circuit symbol = 6.6.6.6.6.6_{2}
Weight = 24
Vertex symbol  = 6.6.6.6.6.6_{2}
Weight = 24

T5 (Si): multiplicity = 6
Coordination Sequence =
    1 4 12 25 42 66 94 131 170 208 258 312 382 447 502 578 658
TD10 = 1011
Circuit symbol = 6.6.6.6.6.6_{2}
Weight = 24
Vertex symbol  = 6.6.6.6.6.6_{2}
Weight = 24

<TD10> = 1011.000
Average ring size = 5.6000