Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_189_5_10646093_xECvHt.cif"

There are 54 T-atoms per unit cell
There are 108 O-atoms per unit cell

Framework density = 20.40 T-atoms per nm^3
Material density = 2.036 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6356 Angstrom
T1  -- O2  = 1.5669 Angstrom
T1  -- O3  = 1.5186 Angstrom
T1  -- O4  = 1.7459 Angstrom
      mean = 1.6168 Angstrom
        t1 = 0.045467  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.039811  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.5137 Angstrom
T2  -- O4  = 1.7197 Angstrom
T2  -- O5  = 1.7729 Angstrom
T2  -- O6  = 1.6206 Angstrom
      mean = 1.6567 Angstrom
        t1 = 0.105541  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.064228  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6658 Angstrom
T3  -- O7  = 1.5759 Angstrom
T3  -- O8  = 1.5566 Angstrom
T3  -- O9  = 1.6393 Angstrom
      mean = 1.6094 Angstrom
        t1 = 0.041462  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.026662  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O8  = 1.5839 Angstrom
T4  -- O9  = 1.6484 Angstrom
T4  -- O10 = 1.6038 Angstrom
T4  -- O11 = 1.6067 Angstrom
      mean = 1.6107 Angstrom
        t1 = 0.025141  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.022459  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O11 = 1.6034 Angstrom
T5  -- O11 = 1.6034 Angstrom
T5  -- O12 = 1.5828 Angstrom
T5  -- O12 = 1.5837 Angstrom
      mean = 1.5933 Angstrom
        t1 = 0.034097  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.022337  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5137 A <--> 1.7729 A
          Mean   = 1.6201 A
          StdDev = 0.0695 A

       t1 Range  = 0.0251 <-- 0.0503 --> 0.1055
       t2 Range  = 0.0223 <-- 0.0351 --> 0.0642

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 106.674 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 121.215 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 112.711 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 105.169 deg; O2  -- O3  = 2 A
O2  -- T1  -- O4  = 104.590 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 105.093 deg; O3  -- O4  = 3 A
       104.590 deg <-- 109.242 deg --> 121.215 deg

O3  -- T2  -- O4  =  94.056 deg; O3  -- O4  = 2 A
O3  -- T2  -- O5  = 109.169 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  =  96.286 deg; O3  -- O6  = 2 A
O4  -- T2  -- O5  = 127.711 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 111.363 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 111.696 deg; O5  -- O6  = 3 A
       94.056 deg <-- 108.380 deg --> 127.711 deg

O6  -- T3  -- O7  = 107.465 deg; O6  -- O7  = 3 A
O6  -- T3  -- O8  = 107.886 deg; O6  -- O8  = 3 A
O6  -- T3  -- O9  = 119.388 deg; O6  -- O9  = 3 A
O7  -- T3  -- O8  = 106.244 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 108.697 deg; O7  -- O9  = 3 A
O8  -- T3  -- O9  = 106.456 deg; O8  -- O9  = 3 A
       106.244 deg <-- 109.356 deg --> 119.388 deg

O8  -- T4  -- O9  = 112.695 deg; O8  -- O9  = 3 A
O8  -- T4  -- O10 = 107.045 deg; O8  -- O10 = 3 A
O8  -- T4  -- O11 = 105.320 deg; O8  -- O11 = 3 A
O9  -- T4  -- O10 = 108.031 deg; O9  -- O10 = 3 A
O9  -- T4  -- O11 = 113.784 deg; O9  -- O11 = 3 A
O10 -- T4  -- O11 = 109.751 deg; O10 -- O11 = 3 A
       105.320 deg <-- 109.438 deg --> 113.784 deg

O11 -- T5  -- O11 = 120.048 deg; O11 -- O11 = 3 A
O11 -- T5  -- O12 = 107.150 deg; O11 -- O12 = 3 A
O11 -- T5  -- O12 = 105.421 deg; O11 -- O12 = 3 A
O11 -- T5  -- O12 = 107.150 deg; O11 -- O12 = 3 A
O11 -- T5  -- O12 = 105.421 deg; O11 -- O12 = 3 A
O12 -- T5  -- O12 = 111.675 deg; O12 -- O12 = 3 A
       105.421 deg <-- 109.478 deg --> 120.048 deg

        O-T-O SUMMARY
          Range  = 94.0559 deg <--> 127.7107 deg
          Mean   = 109.1788 deg
          StdDev = 6.7082 deg

        O--O SUMMARY
          Range  = 2.3356 A <--> 3.1353 A
          Mean   = 2.6354 A
          StdDev = 0.1545 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  = 120.394 deg; T2  -- T2  = 5.0143 A
T2  - O1  - T1  - O3  - T1  =  93.403 deg; T2  -- T1  = 4.1103 A
T2  - O1  - T1  - O4  - T1  = 120.535 deg; T2  -- T1  = 4.6315 A
T2  - O2  - T1  - O3  - T1  = 111.083 deg; T2  -- T1  = 5.2401 A
T2  - O2  - T1  - O4  - T1  = 113.155 deg; T2  -- T1  = 5.0679 A
T1  - O3  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.1926 A

T1  - O3  - T2  - O4  - T1  =  76.027 deg; T1  -- T1  = 3.5961 A
T1  - O3  - T2  - O5  - T3  = 109.069 deg; T1  -- T3  = 4.4682 A
T1  - O3  - T2  - O6  - T2  =  86.597 deg; T1  -- T2  = 4.1103 A
T1  - O4  - T2  - O5  - T3  = 113.940 deg; T1  -- T3  = 5.2096 A
T1  - O4  - T2  - O6  - T2  = 155.874 deg; T1  -- T2  = 6.5062 A
T3  - O5  - T2  - O6  - T2  =  87.335 deg; T3  -- T2  = 4.4075 A

T2  - O6  - T3  - O7  - T4  = 109.426 deg; T2  -- T4  = 4.5684 A
T2  - O6  - T3  - O8  - T4  = 124.618 deg; T2  -- T4  = 5.2709 A
T2  - O6  - T3  - O9  - T3  =  92.665 deg; T2  -- T3  = 4.4075 A
T4  - O7  - T3  - O8  - T4  = 100.631 deg; T4  -- T4  = 4.3310 A
T4  - O7  - T3  - O9  - T3  = 145.375 deg; T4  -- T3  = 5.4993 A
T4  - O8  - T3  - O9  - T3  =  87.151 deg; T4  -- T3  = 4.2192 A

T3  - O8  - T4  - O9  - T3  = 106.355 deg; T3  -- T3  = 4.5038 A
T3  - O8  - T4  - O10 - T4  = 135.540 deg; T3  -- T4  = 5.0557 A
T3  - O8  - T4  - O11 - T5  = 113.814 deg; T3  -- T5  = 4.7677 A
T3  - O9  - T4  - O10 - T4  =  92.849 deg; T3  -- T4  = 4.2192 A
T3  - O9  - T4  - O11 - T5  =  98.674 deg; T3  -- T5  = 4.5856 A
T4  - O10 - T4  - O11 - T5  = 101.928 deg; T4  -- T5  = 4.5743 A

T4  - O11 - T5  - O11 - T4  = 143.731 deg; T4  -- T4  = 5.8058 A
T4  - O11 - T5  - O12 - T5  =  98.285 deg; T4  -- T5  = 4.4679 A
T4  - O11 - T5  - O12 - T5  = 108.118 deg; T4  -- T5  = 4.7820 A
T4  - O11 - T5  - O12 - T5  =  98.285 deg; T4  -- T5  = 4.4679 A
T4  - O11 - T5  - O12 - T5  = 108.118 deg; T4  -- T5  = 4.7820 A
T5  - O12 - T5  - O12 - T5  =  60.000 deg; T5  -- T5  = 2.8500 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 155.8744 deg
          Mean   = 107.3371 deg
          StdDev = 19.6762 deg

        T--T SUMMARY
          Range  = 2.8500 A <--> 6.5062 A
          Mean   = 4.6821 A
          StdDev = 0.6230 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 118.849 deg ; T1  -- T1   2.8164 A

T1  -- O2  -- T1  = 164.661 deg ; T1  -- T1   3.1057 A

T1  -- O3  -- T2  = 112.036 deg ; T1  -- T2   2.5145 A

T1  -- O4  -- T2  = 139.250 deg ; T1  -- T2   3.2488 A

T2  -- O5  -- T2  = 147.511 deg ; T2  -- T2   3.4042 A

T2  -- O6  -- T3  = 128.670 deg ; T2  -- T3   2.9623 A

T3  -- O7  -- T3  = 166.159 deg ; T3  -- T3   3.1288 A

T3  -- O8  -- T4  = 113.698 deg ; T3  -- T4   2.6294 A

T3  -- O9  -- T4  = 130.892 deg ; T3  -- T4   2.9904 A

T4  -- O10 -- T4  = 123.952 deg ; T4  -- T4   2.8316 A

T4  -- O11 -- T5  = 144.191 deg ; T4  -- T5   3.0546 A

T5  -- O12 -- T5  = 128.325 deg ; T5  -- T5   2.8500 A


        T-O-T SUMMARY
          Range  = 112.0358° <--> 166.1592 deg
          Mean   = 135.1332 deg
          StdDev = 17.6407 deg

        T--T SUMMARY
          Range  = 2.5145 A <--> 3.4042 A
          Mean   = 2.9662 A
          StdDev = 0.2460 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.5145 Angstrom
T2  -- T1  = 2.5145 Angstrom
T3  -- T4  = 2.6294 Angstrom
T4  -- T3  = 2.6294 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 33 50 73 99 129 164 202 247 298 350 398 453 522
TD10 = 785
Circuit symbol = 4.6.4.6_{2}.6_{2}.8_{6}
Weight = 21
Vertex symbol  = 4.6.4.6_{2}.6.8_{2}
Weight = 21

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 33 50 72 99 130 164 202 247 293 343 404 458 511
TD10 = 785
Circuit symbol = 4.6.4.6_{2}.6_{2}.8_{6}
Weight = 21
Vertex symbol  = 4.6.4.6_{2}.6.8_{2}
Weight = 21

T3 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 33 50 73 100 131 166 205 244 290 347 396 451 525
TD10 = 793
Circuit symbol = 4.5.4.6.6_{2}.7
Weight = 15
Vertex symbol  = 4.5.4.6.6.10
Weight = 21

T4 (Si): multiplicity = 12
Coordination Sequence =
    1 4 11 20 33 52 73 102 135 165 200 247 294 335 394 461 517
TD10 = 796
Circuit symbol = 4.5.5.8_{5}.6.6_{2}
Weight = 21
Vertex symbol  = 4.5.5.8_{2}.6.6_{2}
Weight = 21

T5 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 17 32 52 70 107 132 160 204 240 284 345 396 446 516
TD10 = 789
Circuit symbol = 3.6.5.5.5.5
Weight = 16
Vertex symbol  = 3.6.5.5.5.5
Weight = 16

<TD10> = 789.667
Average ring size = 5.4848