Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_189_5_10438396_zwWFkz.cif"

There are 54 T-atoms per unit cell
There are 108 O-atoms per unit cell

Framework density = 20.42 T-atoms per nm^3
Material density = 2.037 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6402 Angstrom
T1  -- O2  = 1.5719 Angstrom
T1  -- O3  = 1.5307 Angstrom
T1  -- O4  = 1.7497 Angstrom
      mean = 1.6231 Angstrom
        t1 = 0.044430  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.038502  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.5265 Angstrom
T2  -- O4  = 1.7243 Angstrom
T2  -- O5  = 1.7693 Angstrom
T2  -- O6  = 1.6302 Angstrom
      mean = 1.6626 Angstrom
        t1 = 0.101910  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.061030  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6653 Angstrom
T3  -- O7  = 1.6161 Angstrom
T3  -- O8  = 1.5806 Angstrom
T3  -- O9  = 1.6299 Angstrom
      mean = 1.6230 Angstrom
        t1 = 0.032399  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.020120  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O8  = 1.5805 Angstrom
T4  -- O9  = 1.6354 Angstrom
T4  -- O10 = 1.5876 Angstrom
T4  -- O11 = 1.6249 Angstrom
      mean = 1.6071 Angstrom
        t1 = 0.026015  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.036913  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O11 = 1.6079 Angstrom
T5  -- O11 = 1.6079 Angstrom
T5  -- O12 = 1.5679 Angstrom
T5  -- O12 = 1.5615 Angstrom
      mean = 1.5863 Angstrom
        t1 = 0.050688  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.041223  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5265 A <--> 1.7693 A
          Mean   = 1.6242 A
          StdDev = 0.0664 A

       t1 Range  = 0.0260 <-- 0.0511 --> 0.1019
       t2 Range  = 0.0201 <-- 0.0396 --> 0.0610

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 106.782 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 120.673 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 112.112 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 104.813 deg; O2  -- O3  = 2 A
O2  -- T1  -- O4  = 103.757 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 107.179 deg; O3  -- O4  = 3 A
       103.757 deg <-- 109.219 deg --> 120.673 deg

O3  -- T2  -- O4  =  93.063 deg; O3  -- O4  = 2 A
O3  -- T2  -- O5  = 109.031 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  =  99.412 deg; O3  -- O6  = 2 A
O4  -- T2  -- O5  = 127.946 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 112.268 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 109.720 deg; O5  -- O6  = 3 A
       93.063 deg <-- 108.573 deg --> 127.946 deg

O6  -- T3  -- O7  = 109.333 deg; O6  -- O7  = 3 A
O6  -- T3  -- O8  = 110.291 deg; O6  -- O8  = 3 A
O6  -- T3  -- O9  = 115.510 deg; O6  -- O9  = 3 A
O7  -- T3  -- O8  = 108.726 deg; O7  -- O8  = 3 A
O7  -- T3  -- O9  = 109.674 deg; O7  -- O9  = 3 A
O8  -- T3  -- O9  = 103.007 deg; O8  -- O9  = 3 A
       103.007 deg <-- 109.424 deg --> 115.510 deg

O8  -- T4  -- O9  = 113.452 deg; O8  -- O9  = 3 A
O8  -- T4  -- O10 = 103.372 deg; O8  -- O10 = 2 A
O8  -- T4  -- O11 = 111.037 deg; O8  -- O11 = 3 A
O9  -- T4  -- O10 = 107.867 deg; O9  -- O10 = 3 A
O9  -- T4  -- O11 = 110.934 deg; O9  -- O11 = 3 A
O10 -- T4  -- O11 = 109.833 deg; O10 -- O11 = 3 A
       103.372 deg <-- 109.416 deg --> 113.452 deg

O11 -- T5  -- O11 = 124.314 deg; O11 -- O11 = 3 A
O11 -- T5  -- O12 = 102.270 deg; O11 -- O12 = 2 A
O11 -- T5  -- O12 = 107.312 deg; O11 -- O12 = 3 A
O11 -- T5  -- O12 = 102.270 deg; O11 -- O12 = 2 A
O11 -- T5  -- O12 = 107.312 deg; O11 -- O12 = 3 A
O12 -- T5  -- O12 = 113.354 deg; O12 -- O12 = 3 A
       102.270 deg <-- 109.472 deg --> 124.314 deg

        O-T-O SUMMARY
          Range  = 93.0627 deg <--> 127.9460 deg
          Mean   = 109.1916 deg
          StdDev = 6.9432 deg

        O--O SUMMARY
          Range  = 2.3632 A <--> 3.1394 A
          Mean   = 2.6405 A
          StdDev = 0.1540 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  =  92.699 deg; T1  -- T2  = 4.1113 A
T1  - O1  - T1  - O3  - T2  = 110.791 deg; T1  -- T2  = 5.2772 A
T1  - O1  - T1  - O4  - T1  =  90.000 deg; T1  -- T1  = 4.2142 A
T2  - O2  - T1  - O3  - T2  = 124.019 deg; T2  -- T2  = 5.1531 A
T2  - O2  - T1  - O4  - T1  = 118.625 deg; T2  -- T1  = 4.6156 A
T2  - O3  - T1  - O4  - T1  = 111.650 deg; T2  -- T1  = 5.0701 A

T1  - O3  - T2  - O4  - T1  =  76.091 deg; T1  -- T1  = 3.6370 A
T1  - O3  - T2  - O5  - T2  =  87.301 deg; T1  -- T2  = 4.1113 A
T1  - O3  - T2  - O6  - T3  = 109.499 deg; T1  -- T3  = 4.4950 A
T1  - O4  - T2  - O5  - T2  = 157.132 deg; T1  -- T2  = 6.5170 A
T1  - O4  - T2  - O6  - T3  = 113.555 deg; T1  -- T3  = 5.2332 A
T2  - O5  - T2  - O6  - T3  =  86.594 deg; T2  -- T3  = 4.3458 A

T2  - O6  - T3  - O7  - T3  =  93.406 deg; T2  -- T3  = 4.3458 A
T2  - O6  - T3  - O8  - T4  = 107.273 deg; T2  -- T4  = 4.6769 A
T2  - O6  - T3  - O9  - T4  = 121.819 deg; T2  -- T4  = 5.1012 A
T3  - O7  - T3  - O8  - T4  = 152.917 deg; T3  -- T4  = 5.6894 A
T3  - O7  - T3  - O9  - T4  =  87.420 deg; T3  -- T4  = 4.0658 A
T4  - O8  - T3  - O9  - T4  =  95.903 deg; T4  -- T4  = 4.2464 A

T3  - O8  - T4  - O9  - T3  = 114.979 deg; T3  -- T3  = 4.8223 A
T3  - O8  - T4  - O10 - T5  = 114.342 deg; T3  -- T5  = 4.9477 A
T3  - O8  - T4  - O11 - T4  = 130.294 deg; T3  -- T4  = 5.0754 A
T3  - O9  - T4  - O10 - T5  =  94.722 deg; T3  -- T5  = 4.3541 A
T3  - O9  - T4  - O11 - T4  =  92.580 deg; T3  -- T4  = 4.0658 A
T5  - O10 - T4  - O11 - T4  = 102.751 deg; T5  -- T4  = 4.5285 A

T4  - O11 - T5  - O11 - T4  = 137.135 deg; T4  -- T4  = 5.6643 A
T4  - O11 - T5  - O12 - T5  = 109.679 deg; T4  -- T5  = 4.7756 A
T4  - O11 - T5  - O12 - T5  =  92.610 deg; T4  -- T5  = 4.2250 A
T4  - O11 - T5  - O12 - T5  = 109.679 deg; T4  -- T5  = 4.7756 A
T4  - O11 - T5  - O12 - T5  =  92.610 deg; T4  -- T5  = 4.2250 A
T5  - O12 - T5  - O12 - T5  =  60.000 deg; T5  -- T5  = 2.7963 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 157.1316 deg
          Mean   = 107.3008 deg
          StdDev = 20.0883 deg

        T--T SUMMARY
          Range  = 2.7963 A <--> 6.5170 A
          Mean   = 4.6796 A
          StdDev = 0.6484 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 119.342 deg ; T1  -- T1   2.8314 A

T1  -- O2  -- T1  = 166.324 deg ; T1  -- T1   3.1214 A

T1  -- O3  -- T2  = 111.890 deg ; T1  -- T2   2.5329 A

T1  -- O4  -- T2  = 142.430 deg ; T1  -- T2   3.2890 A

T2  -- O5  -- T2  = 143.431 deg ; T2  -- T2   3.3599 A

T2  -- O6  -- T3  = 128.086 deg ; T2  -- T3   2.9631 A

T3  -- O7  -- T3  = 137.056 deg ; T3  -- T3   3.0078 A

T3  -- O8  -- T4  = 128.244 deg ; T3  -- T4   2.8441 A

T3  -- O9  -- T4  = 123.344 deg ; T3  -- T4   2.8743 A

T4  -- O10 -- T4  = 119.948 deg ; T4  -- T4   2.7491 A

T4  -- O11 -- T5  = 140.489 deg ; T4  -- T5   3.0425 A

T5  -- O12 -- T5  = 126.646 deg ; T5  -- T5   2.7963 A


        T-O-T SUMMARY
          Range  = 111.8898° <--> 166.3241 deg
          Mean   = 132.5136 deg
          StdDev = 14.3189 deg

        T--T SUMMARY
          Range  = 2.5329 A <--> 3.3599 A
          Mean   = 2.9577 A
          StdDev = 0.2256 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T2  = 2.5329 Angstrom
T2  -- T1  = 2.5329 Angstrom
T4  -- T4  = 2.7491 Angstrom
T5  -- T5  = 2.7963 Angstrom
T5  -- T5  = 2.7963 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 33 50 73 99 129 164 202 247 298 350 398 453 522
TD10 = 785
Circuit symbol = 4.6.4.6_{2}.6_{2}.8_{6}
Weight = 21
Vertex symbol  = 4.6.4.6_{2}.6.8_{2}
Weight = 21

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 33 50 72 99 130 164 202 247 293 343 404 458 511
TD10 = 785
Circuit symbol = 4.6.4.6_{2}.6_{2}.8_{6}
Weight = 21
Vertex symbol  = 4.6.4.6_{2}.6.8_{2}
Weight = 21

T3 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 33 50 73 100 131 166 205 244 290 347 396 451 525
TD10 = 793
Circuit symbol = 4.5.4.6.6_{2}.7
Weight = 15
Vertex symbol  = 4.5.4.6.6.10
Weight = 21

T4 (Si): multiplicity = 12
Coordination Sequence =
    1 4 11 20 33 52 73 102 135 165 200 247 294 335 394 461 517
TD10 = 796
Circuit symbol = 4.5.5.8_{5}.6.6_{2}
Weight = 21
Vertex symbol  = 4.5.5.8_{2}.6.6_{2}
Weight = 21

T5 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 17 32 52 70 107 132 160 204 240 284 345 396 446 516
TD10 = 789
Circuit symbol = 3.6.5.5.5.5
Weight = 16
Vertex symbol  = 3.6.5.5.5.5
Weight = 16

<TD10> = 789.667
Average ring size = 5.4848