Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_189_5_10372702_fJ0IZE.cif"

There are 54 T-atoms per unit cell
There are 108 O-atoms per unit cell

Framework density = 21.47 T-atoms per nm^3
Material density = 2.142 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6224 Angstrom
T1  -- O2  = 1.7737 Angstrom
T1  -- O3  = 1.5008 Angstrom
T1  -- O4  = 1.7071 Angstrom
      mean = 1.6510 Angstrom
        t1 = 0.113968  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.078635  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.4795 Angstrom
T2  -- O4  = 1.7413 Angstrom
T2  -- O5  = 1.5684 Angstrom
T2  -- O6  = 1.6293 Angstrom
      mean = 1.6046 Angstrom
        t1 = 0.055582  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.039059  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6605 Angstrom
T3  -- O7  = 1.7545 Angstrom
T3  -- O8  = 1.4794 Angstrom
T3  -- O9  = 1.6755 Angstrom
      mean = 1.6425 Angstrom
        t1 = 0.156787  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.100328  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O8  = 1.3958 Angstrom
T4  -- O9  = 1.7377 Angstrom
T4  -- O10 = 1.6069 Angstrom
T4  -- O11 = 1.6269 Angstrom
      mean = 1.5918 Angstrom
        t1 = 0.118636  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.127965  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O11 = 1.5884 Angstrom
T5  -- O11 = 1.5884 Angstrom
T5  -- O12 = 1.5146 Angstrom
T5  -- O12 = 1.5222 Angstrom
      mean = 1.5534 Angstrom
        t1 = 0.084443  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.056792  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.3958 A <--> 1.7737 A
          Mean   = 1.6148 A
          StdDev = 0.1058 A

       t1 Range  = 0.0556 <-- 0.1059 --> 0.1568
       t2 Range  = 0.0391 <-- 0.0806 --> 0.1280

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.176 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 107.754 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 109.871 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 113.100 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 129.060 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  84.213 deg; O3  -- O4  = 2 A
       84.213 deg <-- 108.862 deg --> 129.060 deg

O3  -- T2  -- O4  =  99.608 deg; O3  -- O4  = 2 A
O3  -- T2  -- O5  = 112.274 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 129.210 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 115.436 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  =  95.280 deg; O4  -- O6  = 2 A
O5  -- T2  -- O6  = 104.075 deg; O5  -- O6  = 3 A
       95.280 deg <-- 109.314 deg --> 129.210 deg

O6  -- T3  -- O7  = 114.777 deg; O6  -- O7  = 3 A
O6  -- T3  -- O8  = 116.327 deg; O6  -- O8  = 3 A
O6  -- T3  -- O9  = 107.481 deg; O6  -- O9  = 3 A
O7  -- T3  -- O8  =  97.012 deg; O7  -- O8  = 2 A
O7  -- T3  -- O9  = 136.634 deg; O7  -- O9  = 3 A
O8  -- T3  -- O9  =  71.669 deg; O8  -- O9  = 2 A
       71.669 deg <-- 107.317 deg --> 136.634 deg

O8  -- T4  -- O9  = 127.621 deg; O8  -- O9  = 3 A
O8  -- T4  -- O10 =  86.675 deg; O8  -- O10 = 2 A
O8  -- T4  -- O11 = 119.565 deg; O8  -- O11 = 3 A
O9  -- T4  -- O10 =  86.565 deg; O9  -- O10 = 2 A
O9  -- T4  -- O11 = 112.539 deg; O9  -- O11 = 3 A
O10 -- T4  -- O11 =  92.007 deg; O10 -- O11 = 2 A
       86.565 deg <-- 104.162 deg --> 127.621 deg

O11 -- T5  -- O11 = 134.850 deg; O11 -- O11 = 3 A
O11 -- T5  -- O12 = 102.032 deg; O11 -- O12 = 2 A
O11 -- T5  -- O12 = 100.737 deg; O11 -- O12 = 2 A
O11 -- T5  -- O12 = 102.032 deg; O11 -- O12 = 2 A
O11 -- T5  -- O12 = 100.737 deg; O11 -- O12 = 2 A
O12 -- T5  -- O12 = 118.081 deg; O12 -- O12 = 3 A
       100.737 deg <-- 109.745 deg --> 134.850 deg

        O-T-O SUMMARY
          Range  = 71.6689 deg <--> 136.6342 deg
          Mean   = 107.6817 deg
          StdDev = 15.3818 deg

        O--O SUMMARY
          Range  = 1.8538 A <--> 3.1874 A
          Mean   = 2.5781 A
          StdDev = 0.2929 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 156.624 deg ; T1  -- T1   3.1775 A

T1  -- O2  -- T1  = 149.299 deg ; T1  -- T1   3.4208 A

T1  -- O3  -- T2  = 125.725 deg ; T1  -- T2   2.6523 A

T1  -- O4  -- T2  = 132.270 deg ; T1  -- T2   3.1536 A

T2  -- O5  -- T2  = 123.446 deg ; T2  -- T2   2.7624 A

T2  -- O6  -- T3  = 137.416 deg ; T2  -- T3   3.0653 A

T3  -- O7  -- T3  = 136.510 deg ; T3  -- T3   3.2592 A

T3  -- O8  -- T4  = 119.338 deg ; T3  -- T4   2.4820 A

T3  -- O9  -- T4  = 140.828 deg ; T3  -- T4   3.2158 A

T4  -- O10 -- T4  = 156.223 deg ; T4  -- T4   3.1449 A

T4  -- O11 -- T5  = 142.635 deg ; T4  -- T5   3.0459 A

T5  -- O12 -- T5  = 121.919 deg ; T5  -- T5   2.6550 A


        T-O-T SUMMARY
          Range  = 119.3376° <--> 156.6236 deg
          Mean   = 137.5020 deg
          StdDev = 12.2339 deg

        T--T SUMMARY
          Range  = 2.4820 A <--> 3.4208 A
          Mean   = 3.0180 A
          StdDev = 0.2768 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O3  -- O4  = 2.1564 A
O8  -- O9  = 1.8538 A
O8  -- O10 = 2.0665 A
O9  -- O10 = 2.2951 A

T-T-T analysis was not conducted.
T1  -- T2  = 2.6523 Angstrom

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T2  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 2.6523 Angstrom
  T2  -- T1  = 3.1536 Angstrom
  T2  -- T2  = 3.4899 Angstrom
  T2  -- T2  = 3.4898 Angstrom
  T2  -- T2  = 2.7624 Angstrom
  T2  -- T3  = 3.0653 Angstrom
T3  -- T4  = 2.4820 Angstrom
T4  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T3  = 2.4820 Angstrom
  T4  -- T3  = 3.2158 Angstrom
  T4  -- T4  = 3.1586 Angstrom
  T4  -- T4  = 3.1586 Angstrom
  T4  -- T5  = 3.0459 Angstrom
  T4  -- T4  = 3.1449 Angstrom
T5  -- T5  = 2.6550 Angstrom
T5  -- T5  = 2.6550 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 33 50 73 99 129 164 202 247 298 350 398 453 522
TD10 = 785
Circuit symbol = 4.6.4.6_{2}.6_{2}.8_{6}
Weight = 21
Vertex symbol  = 4.6.4.6_{2}.6.8_{2}
Weight = 21

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 33 50 72 99 130 164 202 247 293 343 404 458 511
TD10 = 785
Circuit symbol = 4.6.4.6_{2}.6_{2}.8_{6}
Weight = 21
Vertex symbol  = 4.6.4.6_{2}.6.8_{2}
Weight = 21

T3 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 33 50 73 100 131 166 205 244 290 347 396 451 525
TD10 = 793
Circuit symbol = 4.5.4.6.6_{2}.7
Weight = 15
Vertex symbol  = 4.5.4.6.6.10
Weight = 21

T4 (Si): multiplicity = 12
Coordination Sequence =
    1 4 11 20 33 52 73 102 135 165 200 247 294 335 394 461 517
TD10 = 796
Circuit symbol = 4.5.5.8_{5}.6.6_{2}
Weight = 21
Vertex symbol  = 4.5.5.8_{2}.6.6_{2}
Weight = 21

T5 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 17 32 52 70 107 132 160 204 240 284 345 396 446 516
TD10 = 789
Circuit symbol = 3.6.5.5.5.5
Weight = 16
Vertex symbol  = 3.6.5.5.5.5
Weight = 16

<TD10> = 789.667
Average ring size = 5.4848