Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_188_2_501_ntGboP.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 20.79 T-atoms per nm^3
Material density = 2.074 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6282 Angstrom
T1  -- O2  = 1.6236 Angstrom
T1  -- O3  = 1.6331 Angstrom
T1  -- O1  = 1.6295 Angstrom
      mean = 1.6286 Angstrom
        t1 = 0.013831  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008426  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6223 Angstrom
T2  -- O5  = 1.6160 Angstrom
T2  -- O6  = 1.6162 Angstrom
T2  -- O3  = 1.6284 Angstrom
      mean = 1.6207 Angstrom
        t1 = 0.101682  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.090104  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6160 A <--> 1.6331 A
          Mean   = 1.6247 A
          StdDev = 0.0059 A

       t1 Range  = 0.0138 <-- 0.0578 --> 0.1017
       t2 Range  = 0.0084 <-- 0.0493 --> 0.0901

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.920 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 111.036 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 107.595 deg; O1  -- O1  = 3 A
O2  -- T1  -- O3  = 109.774 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 109.055 deg; O2  -- O1  = 3 A
O3  -- T1  -- O1  = 110.404 deg; O3  -- O1  = 3 A
       107.595 deg <-- 109.464 deg --> 111.036 deg

O4  -- T2  -- O5  = 119.106 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 120.217 deg; O4  -- O6  = 3 A
O4  -- T2  -- O3  =  92.555 deg; O4  -- O3  = 2 A
O5  -- T2  -- O6  = 120.678 deg; O5  -- O6  = 3 A
O5  -- T2  -- O3  =  89.325 deg; O5  -- O3  = 2 A
O6  -- T2  -- O3  =  88.153 deg; O6  -- O3  = 2 A
       88.153 deg <-- 105.006 deg --> 120.678 deg

        O-T-O SUMMARY
          Range  = 88.1531 deg <--> 120.6777 deg
          Mean   = 105.4112 deg
          StdDev = 10.4969 deg

        O--O SUMMARY
          Range  = 2.2570 A <--> 2.8087 A
          Mean   = 2.5759 A
          StdDev = 0.1863 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 156.036 deg; T1  -- T2  = 5.8515 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.1765 A
T1  - O1  - T1  - O1  - T1  =  90.000 deg; T1  -- T1  = 4.1765 A
T2  - O2  - T1  - O3  - T1  = 110.351 deg; T2  -- T1  = 4.9262 A
T2  - O2  - T1  - O1  - T1  = 110.831 deg; T2  -- T1  = 4.9405 A
T1  - O3  - T1  - O1  - T1  =  60.000 deg; T1  -- T1  = 2.9626 A

T2  - O4  - T2  - O5  - T2  = 120.000 deg; T2  -- T2  = 5.1136 A
T2  - O4  - T2  - O6  - T2  = 120.000 deg; T2  -- T2  = 5.1276 A
T2  - O4  - T2  - O3  - T1  = 113.963 deg; T2  -- T1  = 5.0366 A
T2  - O5  - T2  - O6  - T2  = 120.000 deg; T2  -- T2  = 5.0997 A
T2  - O5  - T2  - O3  - T1  =  78.085 deg; T2  -- T1  = 3.7640 A
T2  - O6  - T2  - O3  - T1  =  78.481 deg; T2  -- T1  = 3.7901 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 156.0355 deg
          Mean   = 101.6901 deg
          StdDev = 25.6862 deg

        T--T SUMMARY
          Range  = 2.9626 A <--> 5.8515 A
          Mean   = 4.5043 A
          StdDev = 0.8004 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 130.848 deg ; T1  -- T1   2.9626 A

T1  -- O2  -- T1  = 130.068 deg ; T1  -- T1   2.9437 A

T1  -- O3  -- T2  = 137.337 deg ; T1  -- T2   3.0381 A

T2  -- O4  -- T2  = 132.382 deg ; T2  -- T2   2.9685 A

T2  -- O5  -- T2  = 130.592 deg ; T2  -- T2   2.9362 A

T2  -- O6  -- T2  = 131.948 deg ; T2  -- T2   2.9524 A


        T-O-T SUMMARY
          Range  = 130.0677° <--> 137.3368 deg
          Mean   = 132.1958 deg
          StdDev = 2.4475 deg

        T--T SUMMARY
          Range  = 2.9362 A <--> 3.0381 A
          Mean   = 2.9669 A
          StdDev = 0.0338 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O3  -- O5  = 2.2806 A
O3  -- O6  = 2.2571 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 8 15 33 62 86 109 157 208 251 305 351 408 500 577 633
TD10 = 934
Circuit symbol = 3.7_{2}.4.5.4.5
Weight = 11
Vertex symbol  = 3.10_{4}.4.5.4.5
Weight = 32

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 12 22 38 59 89 124 158 202 251 307 360 427 493 558 650
TD10 = 960
Circuit symbol = 5.6.5.6.5.9_{2}
Weight = 17
Vertex symbol  = 5.6.5.6.5.10_{2}
Weight = 26

<TD10> = 947.000
Average ring size = 5.7831