Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_182_2_273571_VLgLYu.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 22.39 T-atoms per nm^3
Material density = 2.234 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6156 Angstrom
T1  -- O2  = 1.6212 Angstrom
T1  -- O2  = 1.6212 Angstrom
T1  -- O2  = 1.6212 Angstrom
      mean = 1.6198 Angstrom
        t1 = 0.006133  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000780  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O2  = 1.6212 Angstrom
T2  -- O2  = 1.6212 Angstrom
T2  -- O2  = 1.6212 Angstrom
T2  -- O3  = 1.6156 Angstrom
      mean = 1.6198 Angstrom
        t1 = 0.006145  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000785  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6156 A <--> 1.6212 A
          Mean   = 1.6198 A
          StdDev = 0.0025 A

       t1 Range  = 0.0061 <-- 0.0061 --> 0.0061
       t2 Range  = 0.0008 <-- 0.0008 --> 0.0008

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.470 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 109.470 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  = 109.470 deg; O1  -- O2  = 3 A
O2  -- T1  -- O2  = 109.472 deg; O2  -- O2  = 3 A
O2  -- T1  -- O2  = 109.472 deg; O2  -- O2  = 3 A
O2  -- T1  -- O2  = 109.472 deg; O2  -- O2  = 3 A
       109.470 deg <-- 109.471 deg --> 109.472 deg

O2  -- T2  -- O2  = 109.471 deg; O2  -- O2  = 3 A
O2  -- T2  -- O2  = 109.474 deg; O2  -- O2  = 3 A
O2  -- T2  -- O3  = 109.470 deg; O2  -- O3  = 3 A
O2  -- T2  -- O2  = 109.473 deg; O2  -- O2  = 3 A
O2  -- T2  -- O3  = 109.470 deg; O2  -- O3  = 3 A
O2  -- T2  -- O3  = 109.470 deg; O2  -- O3  = 3 A
       109.470 deg <-- 109.471 deg --> 109.474 deg

        O-T-O SUMMARY
          Range  = 109.4695 deg <--> 109.4737 deg
          Mean   = 109.4712 deg
          StdDev = 0.0014 deg

        O--O SUMMARY
          Range  = 2.6428 A <--> 2.6474 A
          Mean   = 2.6451 A
          StdDev = 0.0023 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T2  = 107.958 deg; T2  -- T2  = 4.8905 A
T2  - O1  - T1  - O2  - T2  = 107.959 deg; T2  -- T2  = 4.8905 A
T2  - O1  - T1  - O2  - T1  = 110.945 deg; T2  -- T1  = 5.1541 A
T2  - O2  - T1  - O2  - T2  = 107.959 deg; T2  -- T2  = 4.8905 A
T2  - O2  - T1  - O2  - T1  = 110.945 deg; T2  -- T1  = 5.1541 A
T2  - O2  - T1  - O2  - T1  = 110.945 deg; T2  -- T1  = 5.1540 A

T1  - O2  - T2  - O2  - T2  = 110.945 deg; T1  -- T2  = 5.1541 A
T1  - O2  - T2  - O2  - T1  = 107.959 deg; T1  -- T1  = 4.8905 A
T1  - O2  - T2  - O3  - T1  = 107.958 deg; T1  -- T1  = 4.8905 A
T2  - O2  - T2  - O2  - T1  = 110.945 deg; T2  -- T1  = 5.1540 A
T2  - O2  - T2  - O3  - T1  = 110.945 deg; T2  -- T1  = 5.1541 A
T1  - O2  - T2  - O3  - T1  = 107.959 deg; T1  -- T1  = 4.8905 A

        T-T-T SUMMARY
          Range  = 107.9578 deg <--> 110.9448 deg
          Mean   = 109.4516 deg
          StdDev = 1.4983 deg

        T--T SUMMARY
          Range  = 4.8905 A <--> 5.1541 A
          Mean   = 5.0223 A
          StdDev = 0.1322 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 180.000 deg ; T1  -- T1   3.2311 A

T1  -- O2  -- T2  = 137.635 deg ; T1  -- T2   3.0233 A

T2  -- O3  -- T2  = 180.000 deg ; T2  -- T2   3.2311 A


        T-O-T SUMMARY
          Range  = 137.6353° <--> 180.0000 deg
          Mean   = 165.8784 deg
          StdDev = 20.8590 deg

        T--T SUMMARY
          Range  = 3.0233 A <--> 3.2311 A
          Mean   = 3.1619 A
          StdDev = 0.1023 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 25 44 67 96 130 170 214 264 319 380 445 516 592 674
TD10 = 1027
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 27

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 24 42 66 96 130 170 214 264 318 378 444 516 592 674
TD10 = 1023
Circuit symbol = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29
Vertex symbol  = 6_{2}.6_{2}.6_{2}.6_{2}.6_{2}.6_{2}
Weight = 29

<TD10> = 1025.000
Average ring size = 6.0000