Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_182_2_216087_gxavUt.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 16.56 T-atoms per nm^3
Material density = 1.652 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6197 Angstrom
T1  -- O2  = 1.6154 Angstrom
T1  -- O4  = 1.6207 Angstrom
T1  -- O3  = 1.6187 Angstrom
      mean = 1.6186 Angstrom
        t1 = 0.005535  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000957  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6188 Angstrom
T2  -- O5  = 1.6155 Angstrom
T2  -- O6  = 1.6195 Angstrom
T2  -- O4  = 1.6208 Angstrom
      mean = 1.6186 Angstrom
        t1 = 0.005539  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.001826  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6154 A <--> 1.6208 A
          Mean   = 1.6186 A
          StdDev = 0.0020 A

       t1 Range  = 0.0055 <-- 0.0055 --> 0.0055
       t2 Range  = 0.0010 <-- 0.0014 --> 0.0018

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.501 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 109.417 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 109.024 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 109.435 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 109.775 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 109.675 deg; O4  -- O3  = 3 A
       109.024 deg <-- 109.471 deg --> 109.775 deg

O3  -- T2  -- O5  = 109.767 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.013 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 109.667 deg; O3  -- O4  = 3 A
O5  -- T2  -- O6  = 109.492 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 109.449 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 109.438 deg; O6  -- O4  = 3 A
       109.013 deg <-- 109.471 deg --> 109.767 deg

        O-T-O SUMMARY
          Range  = 109.0130 deg <--> 109.7747 deg
          Mean   = 109.4687 deg
          StdDev = 0.2488 deg

        O--O SUMMARY
          Range  = 2.6365 A <--> 2.6483 A
          Mean   = 2.6433 A
          StdDev = 0.0038 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  98.385 deg; T1  -- T1  = 4.7820 A
T1  - O1  - T1  - O4  - T2  = 138.755 deg; T1  -- T2  = 5.7638 A
T1  - O1  - T1  - O3  - T2  = 119.749 deg; T1  -- T2  = 5.3074 A
T1  - O2  - T1  - O4  - T2  =  90.001 deg; T1  -- T2  = 4.4512 A
T1  - O2  - T1  - O3  - T2  = 118.396 deg; T1  -- T2  = 5.3869 A
T2  - O4  - T1  - O3  - T2  =  90.003 deg; T2  -- T2  = 4.3222 A

T2  - O3  - T2  - O5  - T2  =  98.374 deg; T2  -- T2  = 4.7814 A
T2  - O3  - T2  - O6  - T1  =  89.999 deg; T2  -- T1  = 4.4512 A
T2  - O3  - T2  - O4  - T1  = 118.406 deg; T2  -- T1  = 5.3872 A
T2  - O5  - T2  - O6  - T1  = 138.741 deg; T2  -- T1  = 5.7633 A
T2  - O5  - T2  - O4  - T1  = 119.770 deg; T2  -- T1  = 5.3077 A
T1  - O6  - T2  - O4  - T1  =  89.997 deg; T1  -- T1  = 4.3220 A

        T-T-T SUMMARY
          Range  = 89.9968 deg <--> 138.7547 deg
          Mean   = 108.3647 deg
          StdDev = 17.5038 deg

        T--T SUMMARY
          Range  = 4.3220 A <--> 5.7638 A
          Mean   = 4.9776 A
          StdDev = 0.5199 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 145.205 deg ; T1  -- T1   3.0911 A

T1  -- O2  -- T1  = 173.437 deg ; T1  -- T1   3.2256 A

T1  -- O3  -- T2  = 142.681 deg ; T1  -- T2   3.0673 A

T1  -- O4  -- T2  = 139.899 deg ; T1  -- T2   3.0450 A

T2  -- O5  -- T2  = 173.445 deg ; T2  -- T2   3.2256 A

T2  -- O6  -- T2  = 145.202 deg ; T2  -- T2   3.0909 A


        T-O-T SUMMARY
          Range  = 139.8988° <--> 173.4450 deg
          Mean   = 153.3115 deg
          StdDev = 14.4461 deg

        T--T SUMMARY
          Range  = 3.0450 A <--> 3.2256 A
          Mean   = 3.1243 A
          StdDev = 0.0739 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 33 50 72 98 128 160 196 238 283 332 384 440 502
TD10 = 772
Circuit symbol = 4.6.4.6_{2}.6_{2}.8_{6}
Weight = 21
Vertex symbol  = 4.6.4.6_{2}.6.8_{2}
Weight = 21

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 33 50 72 98 128 160 196 238 283 332 384 440 502
TD10 = 772
Circuit symbol = 4.6.4.6_{2}.6_{2}.8_{6}
Weight = 21
Vertex symbol  = 4.6.4.6_{2}.6.8_{2}
Weight = 21

<TD10> = 772.000
Average ring size = 5.6471