Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_182_2_2063_zEjuX9.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 19.97 T-atoms per nm^3
Material density = 1.993 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6253 Angstrom
T1  -- O2  = 1.6239 Angstrom
T1  -- O3  = 1.6222 Angstrom
T1  -- O1  = 1.6253 Angstrom
      mean = 1.6242 Angstrom
        t1 = 0.009474  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002597  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6222 Angstrom
T2  -- O5  = 1.6213 Angstrom
T2  -- O6  = 1.6211 Angstrom
T2  -- O4  = 1.6214 Angstrom
      mean = 1.6215 Angstrom
        t1 = 0.007144  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000399  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6211 A <--> 1.6253 A
          Mean   = 1.6228 A
          StdDev = 0.0017 A

       t1 Range  = 0.0071 <-- 0.0083 --> 0.0095
       t2 Range  = 0.0004 <-- 0.0015 --> 0.0026

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.341 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.834 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 108.207 deg; O1  -- O1  = 3 A
O2  -- T1  -- O3  = 110.264 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 109.335 deg; O2  -- O1  = 3 A
O3  -- T1  -- O1  = 109.826 deg; O3  -- O1  = 3 A
       108.207 deg <-- 109.468 deg --> 110.264 deg

O3  -- T2  -- O5  = 109.373 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 109.545 deg; O3  -- O6  = 3 A
O3  -- T2  -- O4  = 109.436 deg; O3  -- O4  = 3 A
O5  -- T2  -- O6  = 109.469 deg; O5  -- O6  = 3 A
O5  -- T2  -- O4  = 109.500 deg; O5  -- O4  = 3 A
O6  -- T2  -- O4  = 109.504 deg; O6  -- O4  = 3 A
       109.373 deg <-- 109.471 deg --> 109.545 deg

        O-T-O SUMMARY
          Range  = 108.2068 deg <--> 110.2642 deg
          Mean   = 109.4664 deg
          StdDev = 0.4936 deg

        O--O SUMMARY
          Range  = 2.6332 A <--> 2.6633 A
          Mean   = 2.6503 A
          StdDev = 0.0075 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 109.089 deg; T2  -- T1  = 4.8496 A
T2  - O1  - T1  - O3  - T1  = 109.092 deg; T2  -- T1  = 4.8496 A
T2  - O1  - T1  - O1  - T1  = 157.811 deg; T2  -- T1  = 5.8277 A
T1  - O2  - T1  - O3  - T1  =  60.000 deg; T1  -- T1  = 2.9472 A
T1  - O2  - T1  - O1  - T1  =  89.999 deg; T1  -- T1  = 4.1575 A
T1  - O3  - T1  - O1  - T1  =  90.001 deg; T1  -- T1  = 4.1576 A

T2  - O3  - T2  - O5  - T2  = 108.067 deg; T2  -- T2  = 4.9128 A
T2  - O3  - T2  - O6  - T1  =  98.796 deg; T2  -- T1  = 4.5871 A
T2  - O3  - T2  - O4  - T2  = 108.070 deg; T2  -- T2  = 4.9136 A
T2  - O5  - T2  - O6  - T1  = 133.033 deg; T2  -- T1  = 5.5404 A
T2  - O5  - T2  - O4  - T2  = 108.067 deg; T2  -- T2  = 4.9128 A
T1  - O6  - T2  - O4  - T2  =  98.794 deg; T1  -- T2  = 4.5871 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 157.8111 deg
          Mean   = 104.8451 deg
          StdDev = 23.5384 deg

        T--T SUMMARY
          Range  = 2.9472 A <--> 5.8277 A
          Mean   = 4.6403 A
          StdDev = 0.7217 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 130.095 deg ; T1  -- T1   2.9472 A

T1  -- O2  -- T1  = 129.085 deg ; T1  -- T1   2.9324 A

T1  -- O3  -- T2  = 135.821 deg ; T1  -- T2   3.0062 A

T2  -- O4  -- T2  = 138.799 deg ; T2  -- T2   3.0354 A

T2  -- O5  -- T2  = 138.819 deg ; T2  -- T2   3.0354 A

T2  -- O6  -- T2  = 138.769 deg ; T2  -- T2   3.0346 A


        T-O-T SUMMARY
          Range  = 129.0854° <--> 138.8188 deg
          Mean   = 135.2313 deg
          StdDev = 4.1646 deg

        T--T SUMMARY
          Range  = 2.9324 A <--> 3.0354 A
          Mean   = 2.9985 A
          StdDev = 0.0433 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 8 15 33 62 86 109 157 208 251 305 351 408 500 577 633
TD10 = 934
Circuit symbol = 3.7_{2}.4.5.4.5
Weight = 11
Vertex symbol  = 3.10_{4}.4.5.4.5
Weight = 32

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 12 22 38 59 89 124 158 202 251 307 360 427 493 558 650
TD10 = 960
Circuit symbol = 5.6.5.6.5.9_{2}
Weight = 17
Vertex symbol  = 5.6.5.6.5.10_{2}
Weight = 26

<TD10> = 947.000
Average ring size = 5.7831