Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_181_1_856_2oURcc.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.5615 Angstrom
T1  -- O3  = 1.5149 Angstrom
T1  -- O4  = 1.8839 Angstrom
T1  -- O1  = 1.9722 Angstrom
T1  -- O4  = 1.8839 Angstrom
      mean = 1.7633 Angstrom

        T-O SUMMARY
          Range  = 1.5149 A <--> 1.9722 A
          Mean   = 1.7633 A
          StdDev = 0.1888 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O3  = 120.089 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  =  70.431 deg; O2  -- O4  = 2 A
O2  -- T1  -- O1  =  86.235 deg; O2  -- O1  = 2 A
O2  -- T1  -- O4  =  70.431 deg; O2  -- O4  = 2 A
O3  -- T1  -- O4  =  81.448 deg; O3  -- O4  = 2 A
O3  -- T1  -- O1  = 105.150 deg; O3  -- O1  = 3 A
O3  -- T1  -- O4  = 146.468 deg; O3  -- O4  = 3 A
O4  -- T1  -- O1  = 155.524 deg; O4  -- O1  = 4 A
O4  -- T1  -- O4  =  72.361 deg; O4  -- O4  = 2 A
O1  -- T1  -- O4  = 107.362 deg; O1  -- O4  = 3 A
       70.431 deg <-- 101.550 deg --> 155.524 deg

        O-T-O SUMMARY
          Range  = 70.4308 deg <--> 155.5241 deg
          Mean   = 101.5498 deg
          StdDev = 29.8278 deg

        O--O SUMMARY
          Range  = 2.0042 A <--> 3.7686 A
          Mean   = 2.6482 A
          StdDev = 0.5597 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 171.218 deg ; T1  -- T1   3.9328 A

T1  -- O2  -- T1  = 112.158 deg ; T1  -- T1   2.5914 A

T1  -- O3  -- T1  = 121.644 deg ; T1  -- T1   2.6453 A

T1  -- O4  -- T1  =  49.982 deg ; T1  -- T1   1.5918 A
T1  -- O4  -- T1  =  86.907 deg ; T1  -- T1   2.5914 A
T1  -- O4  -- T1  = 107.639 deg ; T1  -- T1   3.0413 A
T1  -- O4  -- T1  = 107.639 deg ; T1  -- T1   3.0413 A
T1  -- O4  -- T1  =  86.907 deg ; T1  -- T1   2.5914 A
T1  -- O4  -- T1  =  49.982 deg ; T1  -- T1   1.5918 A


        T-O-T SUMMARY
          Range  = 49.9821° <--> 171.2181 deg
          Mean   = 99.3417 deg
          StdDev = 35.3581 deg

        T--T SUMMARY
          Range  = 1.5918 A <--> 3.9328 A
          Mean   = 2.6243 A
          StdDev = 0.6860 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O2  -- O4  = 2.0042 A
O2  -- O4  = 2.0042 A
O3  -- O4  = 2.2350 A
O3  -- O4  = 2.2349 A
O4  -- O4  = 2.2243 A

T-T-T analysis was not conducted.
T1  -- T1  = 1.5918 Angstrom
T1  -- T1  = 2.5914 Angstrom
T1  -- T1  = 2.6453 Angstrom