Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_181_1_834_T2GRJ7.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.9972 Angstrom
T1  -- O2  = 1.7817 Angstrom
T1  -- O3  = 1.7355 Angstrom
T1  -- O1  = 1.7788 Angstrom
T1  -- O1  = 2.0229 Angstrom
      mean = 1.8632 Angstrom

        T-O SUMMARY
          Range  = 1.7355 A <--> 2.0229 A
          Mean   = 1.8632 A
          StdDev = 0.1223 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 118.941 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 100.563 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  =  73.214 deg; O1  -- O1  = 2 A
O1  -- T1  -- O1  = 124.071 deg; O1  -- O1  = 4 A
O2  -- T1  -- O3  =  79.032 deg; O2  -- O3  = 2 A
O2  -- T1  -- O1  =  82.535 deg; O2  -- O1  = 2 A
O2  -- T1  -- O1  = 106.662 deg; O2  -- O1  = 3 A
O3  -- T1  -- O1  = 154.427 deg; O3  -- O1  = 3 A
O3  -- T1  -- O1  = 119.188 deg; O3  -- O1  = 3 A
O1  -- T1  -- O1  =  83.033 deg; O1  -- O1  = 3 A
       73.214 deg <-- 104.167 deg --> 154.427 deg

        O-T-O SUMMARY
          Range  = 73.2135 deg <--> 154.4267 deg
          Mean   = 105.4894 deg
          StdDev = 24.2931 deg

        O--O SUMMARY
          Range  = 2.2382 A <--> 3.5507 A
          Mean   = 2.9119 A
          StdDev = 0.4660 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  =  78.108 deg ; T1  -- T1   2.3851 A
T1  -- O1  -- T1  = 111.859 deg ; T1  -- T1   3.3301 A
T1  -- O1  -- T1  =  59.936 deg ; T1  -- T1   1.9107 A

T1  -- O2  -- T1  = 141.654 deg ; T1  -- T1   3.3657 A

T1  -- O3  -- T1  = 120.078 deg ; T1  -- T1   3.0071 A


        T-O-T SUMMARY
          Range  = 59.9360° <--> 141.6537 deg
          Mean   = 102.3269 deg
          StdDev = 29.6971 deg

        T--T SUMMARY
          Range  = 1.9107 A <--> 3.3657 A
          Mean   = 2.7997 A
          StdDev = 0.5717 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O1  = 2.2585 A
O2  -- O3  = 2.2382 A
O2  -- O3  = 2.2383 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 7 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 1.9107 Angstrom
  T1  -- T1  = 3.3657 Angstrom
  T1  -- T1  = 2.3851 Angstrom
  T1  -- T1  = 3.3301 Angstrom
  T1  -- T1  = 3.0071 Angstrom
  T1  -- T1  = 3.1190 Angstrom
  T1  -- T1  = 3.3301 Angstrom