Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_180a_1_1685_uvTrhP.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.9192 Angstrom
T1  -- O2  = 1.7313 Angstrom
T1  -- O3  = 2.0135 Angstrom
T1  -- O3  = 1.9397 Angstrom
T1  -- O4  = 1.6247 Angstrom
      mean = 1.8457 Angstrom

        T-O SUMMARY
          Range  = 1.6247 A <--> 2.0135 A
          Mean   = 1.8457 A
          StdDev = 0.1457 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  =  90.508 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  72.246 deg; O1  -- O3  = 2 A
O1  -- T1  -- O3  = 135.241 deg; O1  -- O3  = 4 A
O1  -- T1  -- O4  = 129.588 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 153.985 deg; O2  -- O3  = 4 A
O2  -- T1  -- O3  = 132.567 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  =  84.069 deg; O2  -- O4  = 2 A
O3  -- T1  -- O3  =  70.141 deg; O3  -- O3  = 2 A
O3  -- T1  -- O4  =  92.012 deg; O3  -- O4  = 3 A
O3  -- T1  -- O4  =  75.270 deg; O3  -- O4  = 2 A
       70.141 deg <-- 103.563 deg --> 153.985 deg

        O-T-O SUMMARY
          Range  = 70.1411 deg <--> 153.9852 deg
          Mean   = 103.5628 deg
          StdDev = 29.6531 deg

        O--O SUMMARY
          Range  = 2.1908 A <--> 3.6492 A
          Mean   = 2.8047 A
          StdDev = 0.5568 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 160.840 deg ; T1  -- T1   3.7849 A

T1  -- O2  -- T1  = 131.738 deg ; T1  -- T1   3.1600 A

T1  -- O3  -- T1  =  54.156 deg ; T1  -- T1   1.8007 A
T1  -- O3  -- T1  = 137.706 deg ; T1  -- T1   3.6871 A
T1  -- O3  -- T1  = 146.876 deg ; T1  -- T1   3.8599 A
T1  -- O3  -- T1  = 148.631 deg ; T1  -- T1   3.7350 A
T1  -- O3  -- T1  = 137.706 deg ; T1  -- T1   3.6871 A
T1  -- O3  -- T1  =  54.156 deg ; T1  -- T1   1.8007 A

T1  -- O4  -- T1  = 179.676 deg ; T1  -- T1   3.2494 A


        T-O-T SUMMARY
          Range  = 54.1563° <--> 179.6757 deg
          Mean   = 127.9428 deg
          StdDev = 41.8796 deg

        T--T SUMMARY
          Range  = 1.8007 A <--> 3.8599 A
          Mean   = 3.1961 A
          StdDev = 0.7824 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O2  -- O4  = 2.2485 A
O2  -- O4  = 2.2485 A
O3  -- O3  = 2.2722 A
O3  -- O4  = 2.1908 A
O3  -- O3  = 2.2722 A
O3  -- O4  = 2.1908 A

T-T-T analysis was not conducted.
T1  -- T1  = 1.8007 Angstrom