Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_180_1_461_229_hR.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 33.32 T-atoms per nm^3
Material density = 3.324 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 2.0581 Angstrom
T1  -- O3  = 1.2492 Angstrom
T1  -- O4  = 1.7113 Angstrom
T1  -- O1  = 1.7523 Angstrom
      mean = 1.6927 Angstrom
        t1 = 0.182402  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.166800  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.2492 A <--> 2.0581 A
          Mean   = 1.6927 A
          StdDev = 0.2921 A

       t1 Range  = 0.1824 <-- 0.1824 --> 0.1824
       t2 Range  = 0.1668 <-- 0.1668 --> 0.1668

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O3  = 112.937 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  =  98.406 deg; O2  -- O4  = 3 A
O2  -- T1  -- O1  =  66.190 deg; O2  -- O1  = 2 A
O3  -- T1  -- O4  = 119.626 deg; O3  -- O4  = 3 A
O3  -- T1  -- O1  =  64.851 deg; O3  -- O1  = 2 A
O4  -- T1  -- O1  =  85.227 deg; O4  -- O1  = 2 A
       64.851 deg <-- 91.206 deg --> 119.626 deg

        O-T-O SUMMARY
          Range  = 64.8508 deg <--> 119.6263 deg
          Mean   = 91.2062 deg
          StdDev = 21.4660 deg

        O--O SUMMARY
          Range  = 1.6645 A <--> 2.8626 A
          Mean   = 2.3885 A
          StdDev = 0.4207 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O2  - T1  - O3  - T1  = 111.858 deg; T1  -- T1  = 3.6483 A
T1  - O2  - T1  - O4  - T1  = 104.990 deg; T1  -- T1  = 4.3933 A
T1  - O2  - T1  - O1  - T1  = 140.267 deg; T1  -- T1  = 5.1647 A
T1  - O3  - T1  - O4  - T1  = 139.812 deg; T1  -- T1  = 5.4292 A
T1  - O3  - T1  - O1  - T1  =  72.125 deg; T1  -- T1  = 3.5217 A
T1  - O4  - T1  - O1  - T1  =  89.743 deg; T1  -- T1  = 4.8244 A

        T-T-T SUMMARY
          Range  = 72.1247 deg <--> 140.2671 deg
          Mean   = 109.7990 deg
          StdDev = 25.1102 deg

        T--T SUMMARY
          Range  = 3.5217 A <--> 5.4292 A
          Mean   = 4.4969 A
          StdDev = 0.7295 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 157.030 deg ; T1  -- T1   3.4344 A

T1  -- O2  -- T1  = 173.766 deg ; T1  -- T1   4.1101 A

T1  -- O3  -- T1  = 142.388 deg ; T1  -- T1   2.3650 A

T1  -- O4  -- T1  = 167.922 deg ; T1  -- T1   3.4036 A


        T-O-T SUMMARY
          Range  = 142.3879° <--> 173.7662 deg
          Mean   = 160.2766 deg
          StdDev = 12.0739 deg

        T--T SUMMARY
          Range  = 2.3650 A <--> 4.1101 A
          Mean   = 3.3283 A
          StdDev = 0.6303 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 2.0963 A
O1  -- O2  = 2.0963 A
O1  -- O3  = 1.6645 A
O1  -- O3  = 1.6645 A
O2  -- O3  = 2.2758 A
O3  -- O3  = 2.2446 A
T1  -- T1  = 2.0337 Angstrom
T1  -- T1  = 2.3650 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 21 43 78 120 172 238 310 393 483 585 691 809 933 1069
TD10 = 1390
Circuit symbol = 4.6_{2}.4.8_{2}.6.6_{2}
Weight = 10
Vertex symbol  = 4.6_{2}.4.10_{18}.6_{2}.10_{3}
Weight = 46

<TD10> = 1390.000
Average ring size = 8.2653