Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_17_2_27747_RqMAQG.cif"

There are 8 T-atoms per unit cell
There are 16 O-atoms per unit cell

Framework density = 30.07 T-atoms per nm^3
Material density = 3.000 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6039 Angstrom
T1  -- O2  = 1.6098 Angstrom
T1  -- O3  = 1.6099 Angstrom
T1  -- O4  = 1.7960 Angstrom
      mean = 1.6549 Angstrom
        t1 = 0.094494  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.093871  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.7961 Angstrom
T2  -- O5  = 1.6039 Angstrom
T2  -- O6  = 1.6099 Angstrom
T2  -- O7  = 1.6098 Angstrom
      mean = 1.6549 Angstrom
        t1 = 0.094507  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.064885  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6039 A <--> 1.7961 A
          Mean   = 1.6549 A
          StdDev = 0.0828 A

       t1 Range  = 0.0945 <-- 0.0945 --> 0.0945
       t2 Range  = 0.0649 <-- 0.0794 --> 0.0939

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  =  95.160 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  =  95.150 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 124.924 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 116.195 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 112.058 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 112.060 deg; O3  -- O4  = 3 A
       95.150 deg <-- 109.258 deg --> 124.924 deg

O4  -- T2  -- O5  = 124.928 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 112.063 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 112.046 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  =  95.164 deg; O5  -- O6  = 2 A
O5  -- T2  -- O7  =  95.151 deg; O5  -- O7  = 2 A
O6  -- T2  -- O7  = 116.197 deg; O6  -- O7  = 3 A
       95.151 deg <-- 109.258 deg --> 124.928 deg

        O-T-O SUMMARY
          Range  = 95.1497 deg <--> 124.9282 deg
          Mean   = 111.6208 deg
          StdDev = 10.2422 deg

        O--O SUMMARY
          Range  = 2.3722 A <--> 3.0162 A
          Mean   = 2.7574 A
          StdDev = 0.2268 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  94.341 deg; T1  -- T1  = 4.7134 A
T1  - O1  - T1  - O3  - T1  =  94.341 deg; T1  -- T1  = 4.7137 A
T1  - O1  - T1  - O4  - T2  = 153.548 deg; T1  -- T2  = 6.0322 A
T1  - O2  - T1  - O3  - T1  = 116.213 deg; T1  -- T1  = 5.4667 A
T1  - O2  - T1  - O4  - T2  =  72.503 deg; T1  -- T2  = 3.6755 A
T1  - O3  - T1  - O4  - T2  =  72.499 deg; T1  -- T2  = 3.6756 A

T2  - O4  - T2  - O5  - T2  =  94.342 deg; T2  -- T2  = 4.7136 A
T2  - O4  - T2  - O6  - T1  = 153.549 deg; T2  -- T1  = 6.0322 A
T2  - O4  - T2  - O7  - T2  =  94.342 deg; T2  -- T2  = 4.7135 A
T2  - O5  - T2  - O6  - T1  =  72.499 deg; T2  -- T1  = 3.6755 A
T2  - O5  - T2  - O7  - T2  = 116.216 deg; T2  -- T2  = 5.4667 A
T1  - O6  - T2  - O7  - T2  =  72.504 deg; T1  -- T2  = 3.6756 A

        T-T-T SUMMARY
          Range  = 72.4991 deg <--> 153.5495 deg
          Mean   = 102.6489 deg
          StdDev = 30.7976 deg

        T--T SUMMARY
          Range  = 3.6755 A <--> 6.0322 A
          Mean   = 4.7443 A
          StdDev = 0.9114 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 179.988 deg ; T1  -- T1   3.2077 A

T1  -- O2  -- T1  = 178.340 deg ; T1  -- T1   3.2192 A

T1  -- O3  -- T1  = 178.380 deg ; T1  -- T1   3.2196 A

T1  -- O4  -- T2  = 179.992 deg ; T1  -- T2   3.5922 A

T2  -- O5  -- T2  = 179.957 deg ; T2  -- T2   3.2078 A

T2  -- O6  -- T2  = 178.380 deg ; T2  -- T2   3.2194 A

T2  -- O7  -- T2  = 178.332 deg ; T2  -- T2   3.2192 A


        T-O-T SUMMARY
          Range  = 178.3322° <--> 179.9919 deg
          Mean   = 179.0529 deg
          StdDev = 0.8171 deg

        T--T SUMMARY
          Range  = 3.2077 A <--> 3.5922 A
          Mean   = 3.2693 A
          StdDev = 0.1343 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 30 66 107 154 211 278 353 438 531 634 745 866 995 1134
TD10 = 1654
Circuit symbol = 6.6.6.6.6_{2}.8_{4}
Weight = 28
Vertex symbol  = 6.6.6.6.6_{2}.8_{2}
Weight = 28

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 30 66 107 154 211 278 353 438 531 634 745 866 995 1134
TD10 = 1654
Circuit symbol = 6.6.6.6.6_{2}.8_{4}
Weight = 28
Vertex symbol  = 6.6.6.6.6_{2}.8_{2}
Weight = 28

<TD10> = 1654.000
Average ring size = 6.4000