Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_178a_1_250_WktRvT.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O2  = 1.8751 Angstrom
T1  -- O3  = 1.8474 Angstrom
T1  -- O1  = 1.7384 Angstrom
T1  -- O1  = 1.7150 Angstrom
T1  -- O1  = 1.4227 Angstrom
T1  -- O1  = 1.9236 Angstrom
      mean = 1.7537 Angstrom

        T-O SUMMARY
          Range  = 1.4227 A <--> 1.9236 A
          Mean   = 1.7537 A
          StdDev = 0.1663 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O2  -- T1  -- O3  =  91.076 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  =  71.956 deg; O2  -- O1  = 2 A
O2  -- T1  -- O1  =  95.962 deg; O2  -- O1  = 3 A
O2  -- T1  -- O1  = 109.311 deg; O2  -- O1  = 3 A
O2  -- T1  -- O1  = 126.830 deg; O2  -- O1  = 3 A
O3  -- T1  -- O1  = 115.505 deg; O3  -- O1  = 3 A
O3  -- T1  -- O1  = 122.688 deg; O3  -- O1  = 3 A
O3  -- T1  -- O1  = 112.810 deg; O3  -- O1  = 3 A
O3  -- T1  -- O1  = 115.405 deg; O3  -- O1  = 3 A
O1  -- T1  -- O1  =  24.844 deg; O1  -- O1  = 1 A
O1  -- T1  -- O1  = 131.646 deg; O1  -- O1  = 3 A
O1  -- T1  -- O1  = 124.551 deg; O1  -- O1  = 3 A
O1  -- T1  -- O1  = 117.852 deg; O1  -- O1  = 3 A
O1  -- T1  -- O1  = 104.855 deg; O1  -- O1  = 3 A
O1  -- T1  -- O1  =  19.105 deg; O1  -- O1  = 1 A
       19.105 deg <-- 98.960 deg --> 131.646 deg

        O-T-O SUMMARY
          Range  = 19.1050 deg <--> 131.6465 deg
          Mean   = 99.2317 deg
          StdDev = 34.2747 deg

        O--O SUMMARY
          Range  = 0.7432 A <--> 3.3972 A
          Mean   = 2.5862 A
          StdDev = 0.7982 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  =  37.230 deg ; T1  -- T1   1.1820 A
T1  -- O1  -- T1  = 149.130 deg ; T1  -- T1   3.3288 A
T1  -- O1  -- T1  = 158.185 deg ; T1  -- T1   3.1045 A
T1  -- O1  -- T1  = 117.013 deg ; T1  -- T1   3.1045 A
T1  -- O1  -- T1  = 159.837 deg ; T1  -- T1   3.2958 A
T1  -- O1  -- T1  =  43.014 deg ; T1  -- T1   1.1820 A

T1  -- O2  -- T1  = 141.369 deg ; T1  -- T1   3.5392 A

T1  -- O3  -- T1  = 163.458 deg ; T1  -- T1   3.6565 A


        T-O-T SUMMARY
          Range  = 37.2300° <--> 163.4579 deg
          Mean   = 121.1544 deg
          StdDev = 49.0089 deg

        T--T SUMMARY
          Range  = 1.1820 A <--> 3.6565 A
          Mean   = 2.7992 A
          StdDev = 0.9554 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O1  = 0.7432 A
O1  -- O2  = 2.1257 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has only 5 neighboring T-atoms within 3.50 A, but 6 bridging O-atoms
  T1  -- T1  = 3.3288 Angstrom
  T1  -- T1  = 3.1045 Angstrom
  T1  -- T1  = 1.1820 Angstrom
  T1  -- T1  = 3.1045 Angstrom
  T1  -- T1  = 3.2958 Angstrom