Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_177_2_7410040_XQhhXL.cif"

There are 18 T-atoms per unit cell
There are 36 O-atoms per unit cell

Framework density = 18.70 T-atoms per nm^3
Material density = 1.866 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6176 Angstrom
T1  -- O2  = 1.6157 Angstrom
T1  -- O3  = 1.6142 Angstrom
T1  -- O1  = 1.6176 Angstrom
      mean = 1.6163 Angstrom
        t1 = 0.004048  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.000832  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6197 Angstrom
T2  -- O3  = 1.6197 Angstrom
T2  -- O4  = 1.6245 Angstrom
T2  -- O4  = 1.6245 Angstrom
      mean = 1.6221 Angstrom
        t1 = 0.008531  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.002648  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6142 A <--> 1.6245 A
          Mean   = 1.6182 A
          StdDev = 0.0033 A

       t1 Range  = 0.0040 <-- 0.0063 --> 0.0085
       t2 Range  = 0.0008 <-- 0.0017 --> 0.0026

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.659 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.402 deg; O1  -- O3  = 3 A
O1  -- T1  -- O1  = 109.360 deg; O1  -- O1  = 3 A
O2  -- T1  -- O3  = 109.331 deg; O2  -- O3  = 3 A
O2  -- T1  -- O1  = 109.671 deg; O2  -- O1  = 3 A
O3  -- T1  -- O1  = 109.402 deg; O3  -- O1  = 3 A
       109.331 deg <-- 109.471 deg --> 109.671 deg

O3  -- T2  -- O3  = 111.038 deg; O3  -- O3  = 3 A
O3  -- T2  -- O4  = 109.379 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 109.367 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 109.367 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 109.379 deg; O3  -- O4  = 3 A
O4  -- T2  -- O4  = 108.262 deg; O4  -- O4  = 3 A
       108.262 deg <-- 109.465 deg --> 111.038 deg

        O-T-O SUMMARY
          Range  = 108.2621 deg <--> 111.0377 deg
          Mean   = 109.5207 deg
          StdDev = 0.5386 deg

        O--O SUMMARY
          Range  = 2.6328 A <--> 2.6703 A
          Mean   = 2.6445 A
          StdDev = 0.0093 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 112.764 deg; T1  -- T2  = 5.1499 A
T1  - O1  - T1  - O3  - T1  = 120.000 deg; T1  -- T1  = 5.3342 A
T1  - O1  - T1  - O1  - T1  =  89.996 deg; T1  -- T1  = 4.4589 A
T2  - O2  - T1  - O3  - T1  = 112.772 deg; T2  -- T1  = 5.1501 A
T2  - O2  - T1  - O1  - T1  = 129.286 deg; T2  -- T1  = 5.7197 A
T1  - O3  - T1  - O1  - T1  =  90.004 deg; T1  -- T1  = 4.4592 A

T1  - O3  - T2  - O3  - T1  =  78.572 deg; T1  -- T1  = 3.9315 A
T1  - O3  - T2  - O4  - T2  = 132.089 deg; T1  -- T2  = 5.5470 A
T1  - O3  - T2  - O4  - T2  = 132.092 deg; T1  -- T2  = 5.5470 A
T1  - O3  - T2  - O4  - T2  = 132.092 deg; T1  -- T2  = 5.5470 A
T1  - O3  - T2  - O4  - T2  = 132.089 deg; T1  -- T2  = 5.5470 A
T2  - O4  - T2  - O4  - T2  =  60.000 deg; T2  -- T2  = 2.9650 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 132.0918 deg
          Mean   = 112.3265 deg
          StdDev = 21.7779 deg

        T--T SUMMARY
          Range  = 2.9650 A <--> 5.7197 A
          Mean   = 5.0325 A
          StdDev = 0.7039 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 144.332 deg ; T1  -- T1   3.0797 A

T1  -- O2  -- T1  = 172.670 deg ; T1  -- T1   3.2247 A

T1  -- O3  -- T2  = 147.477 deg ; T1  -- T2   3.1045 A

T2  -- O4  -- T2  = 131.738 deg ; T2  -- T2   2.9650 A


        T-O-T SUMMARY
          Range  = 131.7379° <--> 172.6701 deg
          Mean   = 151.5282 deg
          StdDev = 14.4256 deg

        T--T SUMMARY
          Range  = 2.9650 A <--> 3.2247 A
          Mean   = 3.1118 A
          StdDev = 0.0849 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 21 38 62 89 114 143 184 238 294 340 383 441 523 612
TD10 = 904
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 24
Vertex symbol  = 4.6.4.6.6.8_{2}
Weight = 24

T2 (Si): multiplicity = 6
Coordination Sequence =
    1 4 10 24 40 54 80 120 156 196 228 266 330 410 472 524 576
TD10 = 913
Circuit symbol = 3.6_{2}.8_{3}.8_{3}.8_{3}.8_{3}
Weight = 33
Vertex symbol  = 3.6_{2}.8_{3}.8_{3}.8_{3}.8_{3}
Weight = 33

<TD10> = 907.000
Average ring size = 6.2143