Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_177_2_6719142_QI3dw2.cif"

There are 16 T-atoms per unit cell
There are 32 O-atoms per unit cell

Framework density = 19.04 T-atoms per nm^3
Material density = 1.899 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6114 Angstrom
T1  -- O1  = 1.6114 Angstrom
T1  -- O2  = 1.6239 Angstrom
T1  -- O3  = 1.6018 Angstrom
      mean = 1.6121 Angstrom
        t1 = 0.006621  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005379  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6174 Angstrom
T2  -- O3  = 1.6173 Angstrom
T2  -- O3  = 1.6174 Angstrom
T2  -- O4  = 1.6156 Angstrom
      mean = 1.6169 Angstrom
        t1 = 0.007330  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.005354  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6018 A <--> 1.6239 A
          Mean   = 1.6133 A
          StdDev = 0.0072 A

       t1 Range  = 0.0066 <-- 0.0070 --> 0.0073
       t2 Range  = 0.0054 <-- 0.0054 --> 0.0054

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 108.549 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 109.796 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.956 deg; O1  -- O3  = 3 A
O1  -- T1  -- O2  = 109.793 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.961 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 110.743 deg; O2  -- O3  = 3 A
       108.549 deg <-- 109.467 deg --> 110.743 deg

O3  -- T2  -- O3  = 110.390 deg; O3  -- O3  = 3 A
O3  -- T2  -- O3  = 110.386 deg; O3  -- O3  = 3 A
O3  -- T2  -- O4  = 108.537 deg; O3  -- O4  = 3 A
O3  -- T2  -- O3  = 110.390 deg; O3  -- O3  = 3 A
O3  -- T2  -- O4  = 108.538 deg; O3  -- O4  = 3 A
O3  -- T2  -- O4  = 108.537 deg; O3  -- O4  = 3 A
       108.537 deg <-- 109.463 deg --> 110.390 deg

        O-T-O SUMMARY
          Range  = 108.5371 deg <--> 110.7429 deg
          Mean   = 109.4648 deg
          StdDev = 0.8367 deg

        O--O SUMMARY
          Range  = 2.6152 A <--> 2.6560 A
          Mean   = 2.6363 A
          StdDev = 0.0169 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T2  = 115.002 deg; T1  -- T2  = 5.3289 A
T1  - O1  - T1  - O2  - T1  = 120.000 deg; T1  -- T1  = 5.5295 A
T1  - O1  - T1  - O3  - T1  =  90.002 deg; T1  -- T1  = 4.3348 A
T2  - O1  - T1  - O2  - T1  = 114.997 deg; T2  -- T1  = 5.3287 A
T2  - O1  - T1  - O3  - T1  = 122.305 deg; T2  -- T1  = 5.3071 A
T1  - O2  - T1  - O3  - T1  =  89.998 deg; T1  -- T1  = 4.3347 A

T1  - O3  - T2  - O3  - T1  =  94.105 deg; T1  -- T1  = 4.5759 A
T1  - O3  - T2  - O3  - T1  =  94.103 deg; T1  -- T1  = 4.5759 A
T1  - O3  - T2  - O4  - T2  = 122.305 deg; T1  -- T2  = 5.5683 A
T1  - O3  - T2  - O3  - T1  =  94.105 deg; T1  -- T1  = 4.5759 A
T1  - O3  - T2  - O4  - T2  = 122.306 deg; T1  -- T2  = 5.5682 A
T1  - O3  - T2  - O4  - T2  = 122.305 deg; T1  -- T2  = 5.5683 A

        T-T-T SUMMARY
          Range  = 89.9983 deg <--> 122.3062 deg
          Mean   = 108.4611 deg
          StdDev = 13.8483 deg

        T--T SUMMARY
          Range  = 4.3347 A <--> 5.5683 A
          Mean   = 5.0497 A
          StdDev = 0.4979 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 164.269 deg ; T1  -- T1   3.1925 A

T1  -- O2  -- T1  = 129.066 deg ; T1  -- T1   2.9323 A

T1  -- O3  -- T2  = 152.327 deg ; T1  -- T2   3.1257 A

T2  -- O4  -- T2  = 180.000 deg ; T2  -- T2   3.2311 A


        T-O-T SUMMARY
          Range  = 129.0657° <--> 180.0000 deg
          Mean   = 151.6985 deg
          StdDev = 16.9854 deg

        T--T SUMMARY
          Range  = 2.9323 A <--> 3.2311 A
          Mean   = 3.0983 A
          StdDev = 0.1151 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 21 39 63 88 113 145 189 240 290 338 390 452 525 605
TD10 = 913
Circuit symbol = 4.6.4.6.6_{2}.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6_{2}
Weight = 19

T2 (Si): multiplicity = 4
Coordination Sequence =
    1 4 12 25 38 55 84 121 158 193 228 274 338 406 468 529 590
TD10 = 919
Circuit symbol = 6_{2}.8_{4}.6_{2}.8_{4}.6_{2}.8_{4}
Weight = 30
Vertex symbol  = 6_{2}.8_{4}.6_{2}.8_{4}.6_{2}.8_{4}
Weight = 30

<TD10> = 914.500
Average ring size = 6.0000