Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_177_2_6005562_EnWVKh.cif"

There are 24 T-atoms per unit cell
There are 48 O-atoms per unit cell

Framework density = 19.16 T-atoms per nm^3
Material density = 1.912 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6155 Angstrom
T1  -- O2  = 1.6251 Angstrom
T1  -- O4  = 1.6212 Angstrom
T1  -- O3  = 1.6202 Angstrom
      mean = 1.6205 Angstrom
        t1 = 0.010267  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008210  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6211 Angstrom
T2  -- O4  = 1.6205 Angstrom
T2  -- O5  = 1.6197 Angstrom
T2  -- O6  = 1.6266 Angstrom
      mean = 1.6220 Angstrom
        t1 = 0.011125  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.008896  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.6155 A <--> 1.6266 A
          Mean   = 1.6213 A
          StdDev = 0.0032 A

       t1 Range  = 0.0103 <-- 0.0107 --> 0.0111
       t2 Range  = 0.0082 <-- 0.0086 --> 0.0089

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.589 deg; O1  -- O2  = 3 A
O1  -- T1  -- O4  = 108.021 deg; O1  -- O4  = 3 A
O1  -- T1  -- O3  = 110.979 deg; O1  -- O3  = 3 A
O2  -- T1  -- O4  = 111.041 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 107.796 deg; O2  -- O3  = 3 A
O4  -- T1  -- O3  = 109.431 deg; O4  -- O3  = 3 A
       107.796 deg <-- 109.476 deg --> 111.041 deg

O3  -- T2  -- O4  = 109.335 deg; O3  -- O4  = 3 A
O3  -- T2  -- O5  = 107.790 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  = 111.148 deg; O3  -- O6  = 3 A
O4  -- T2  -- O5  = 110.676 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 107.836 deg; O4  -- O6  = 3 A
O5  -- T2  -- O6  = 110.069 deg; O5  -- O6  = 3 A
       107.790 deg <-- 109.476 deg --> 111.148 deg

        O-T-O SUMMARY
          Range  = 107.7898 deg <--> 111.1481 deg
          Mean   = 109.4438 deg
          StdDev = 1.3402 deg

        O--O SUMMARY
          Range  = 2.6184 A <--> 2.6789 A
          Mean   = 2.6468 A
          StdDev = 0.0222 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T2  - O1  - T1  - O2  - T1  = 116.670 deg; T2  -- T1  = 5.2918 A
T2  - O1  - T1  - O4  - T1  = 100.513 deg; T2  -- T1  = 4.5734 A
T2  - O1  - T1  - O3  - T2  = 109.701 deg; T2  -- T2  = 4.9608 A
T1  - O2  - T1  - O4  - T1  = 141.333 deg; T1  -- T1  = 5.7538 A
T1  - O2  - T1  - O3  - T2  =  96.590 deg; T1  -- T2  = 4.6426 A
T1  - O4  - T1  - O3  - T2  =  79.484 deg; T1  -- T2  = 3.8034 A

T1  - O3  - T2  - O4  - T2  = 108.205 deg; T1  -- T2  = 4.9215 A
T1  - O3  - T2  - O5  - T2  =  79.493 deg; T1  -- T2  = 3.8034 A
T1  - O3  - T2  - O6  - T1  = 109.701 deg; T1  -- T1  = 4.9608 A
T2  - O4  - T2  - O5  - T2  = 115.372 deg; T2  -- T2  = 5.0335 A
T2  - O4  - T2  - O6  - T1  = 131.431 deg; T2  -- T1  = 5.5381 A
T2  - O5  - T2  - O6  - T1  = 100.511 deg; T2  -- T1  = 4.5734 A

        T-T-T SUMMARY
          Range  = 79.4836 deg <--> 141.3330 deg
          Mean   = 107.3102 deg
          StdDev = 18.1413 deg

        T--T SUMMARY
          Range  = 3.8034 A <--> 5.7538 A
          Mean   = 4.8113 A
          StdDev = 0.5887 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 160.265 deg ; T1  -- T1   3.1833 A

T1  -- O2  -- T1  = 127.393 deg ; T1  -- T1   2.9136 A

T1  -- O3  -- T2  = 138.760 deg ; T1  -- T2   3.0337 A

T1  -- O4  -- T2  = 138.694 deg ; T1  -- T2   3.0334 A

T2  -- O5  -- T2  = 139.802 deg ; T2  -- T2   3.0420 A

T2  -- O6  -- T2  = 127.165 deg ; T2  -- T2   2.9134 A


        T-O-T SUMMARY
          Range  = 127.1647° <--> 160.2648 deg
          Mean   = 138.6797 deg
          StdDev = 11.0861 deg

        T--T SUMMARY
          Range  = 2.9134 A <--> 3.1833 A
          Mean   = 3.0199 A
          StdDev = 0.0921 A

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 21 35 51 72 97 127 162 202 247 289 333 385 440 503
TD10 = 782
Circuit symbol = 4.6.4.6.6_{2}.8_{4}
Weight = 18
Vertex symbol  = 4.6.4.6.6.12
Weight = 25

T2 (Si): multiplicity = 12
Coordination Sequence =
    1 4 10 20 33 50 73 102 134 165 196 232 277 333 399 464 521
TD10 = 788
Circuit symbol = 4.6.4.6.6.6_{2}
Weight = 19
Vertex symbol  = 4.6.4.6.6.6
Weight = 19

<TD10> = 785.000
Average ring size = 5.3333