Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_167-2_1_764_6qtN9z.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5897 Angstrom
T1  -- O2  = 1.5792 Angstrom
T1  -- O3  = 1.8538 Angstrom
T1  -- O3  = 1.8305 Angstrom
T1  -- O3  = 2.0686 Angstrom
      mean = 1.7844 Angstrom

        T-O SUMMARY
          Range  = 1.5792 A <--> 2.0686 A
          Mean   = 1.7844 A
          StdDev = 0.1847 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 120.890 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  95.554 deg; O1  -- O3  = 3 A
O1  -- T1  -- O3  =  87.902 deg; O1  -- O3  = 2 A
O1  -- T1  -- O3  = 165.095 deg; O1  -- O3  = 4 A
O2  -- T1  -- O3  =  79.969 deg; O2  -- O3  = 2 A
O2  -- T1  -- O3  =  75.807 deg; O2  -- O3  = 2 A
O2  -- T1  -- O3  =  73.439 deg; O2  -- O3  = 2 A
O3  -- T1  -- O3  = 153.529 deg; O3  -- O3  = 4 A
O3  -- T1  -- O3  =  82.419 deg; O3  -- O3  = 3 A
O3  -- T1  -- O3  = 100.520 deg; O3  -- O3  = 3 A
       73.439 deg <-- 103.512 deg --> 165.095 deg

        O-T-O SUMMARY
          Range  = 73.4388 deg <--> 165.0948 deg
          Mean   = 102.5978 deg
          StdDev = 31.6356 deg

        O--O SUMMARY
          Range  = 2.1041 A <--> 3.6279 A
          Mean   = 2.7007 A
          StdDev = 0.5353 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  =  81.941 deg ; T1  -- T1   2.0847 A

T1  -- O2  -- T1  = 102.727 deg ; T1  -- T1   2.4672 A

T1  -- O3  -- T1  =  77.739 deg ; T1  -- T1   2.4672 A
T1  -- O3  -- T1  = 153.866 deg ; T1  -- T1   3.5889 A
T1  -- O3  -- T1  = 115.890 deg ; T1  -- T1   3.3070 A


        T-O-T SUMMARY
          Range  = 77.7385° <--> 153.8660 deg
          Mean   = 106.4324 deg
          StdDev = 27.7139 deg

        T--T SUMMARY
          Range  = 2.0847 A <--> 3.5889 A
          Mean   = 2.7830 A
          StdDev = 0.5725 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O2  -- O3  = 2.2160 A
O2  -- O3  = 2.1041 A
O2  -- O3  = 2.1041 A
O2  -- O3  = 2.2160 A

T-T-T analysis was not conducted.
T1  -- T1  = 2.4672 Angstrom
T1  -- T1  = 2.0847 Angstrom