Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_167-2_1_1744_8NyJXM.cif"

There are 6 T-atoms per unit cell
There are 12 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6340 Angstrom
T1  -- O1  = 1.9856 Angstrom
T1  -- O2  = 1.6360 Angstrom
T1  -- O1  = 1.6340 Angstrom
T1  -- O2  = 1.6360 Angstrom
      mean = 1.7051 Angstrom

        T-O SUMMARY
          Range  = 1.6340 A <--> 1.9856 A
          Mean   = 1.7051 A
          StdDev = 0.1426 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 107.383 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  =  82.968 deg; O1  -- O2  = 2 A
O1  -- T1  -- O1  = 145.234 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  =  80.312 deg; O1  -- O2  = 2 A
O1  -- T1  -- O2  = 119.112 deg; O1  -- O2  = 3 A
O1  -- T1  -- O1  = 107.383 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 119.112 deg; O1  -- O2  = 3 A
O2  -- T1  -- O1  =  80.312 deg; O2  -- O1  = 2 A
O2  -- T1  -- O2  = 121.776 deg; O2  -- O2  = 3 A
O1  -- T1  -- O2  =  82.968 deg; O1  -- O2  = 2 A
       80.312 deg <-- 104.656 deg --> 145.234 deg

        O-T-O SUMMARY
          Range  = 80.3120 deg <--> 145.2341 deg
          Mean   = 104.6561 deg
          StdDev = 21.3886 deg

        O--O SUMMARY
          Range  = 2.1087 A <--> 3.1272 A
          Mean   = 2.6630 A
          StdDev = 0.4421 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 121.980 deg ; T1  -- T1   3.1700 A
T1  -- O1  -- T1  = 116.041 deg ; T1  -- T1   2.7720 A
T1  -- O1  -- T1  = 121.980 deg ; T1  -- T1   3.1700 A

T1  -- O2  -- T1  = 180.000 deg ; T1  -- T1   3.2720 A


        T-O-T SUMMARY
          Range  = 116.0408° <--> 180.0000 deg
          Mean   = 135.0000 deg
          StdDev = 26.6549 deg

        T--T SUMMARY
          Range  = 2.7720 A <--> 3.2720 A
          Mean   = 3.0960 A
          StdDev = 0.1958 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 2.1661 A
O1  -- O2  = 2.1087 A
O1  -- O2  = 2.1087 A
O1  -- O2  = 2.1661 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 8 neighboring T-atoms within 3.50 A, but only 5 bridging O-atoms
  T1  -- T1  = 3.1700 Angstrom
  T1  -- T1  = 3.1700 Angstrom
  T1  -- T1  = 2.7720 Angstrom
  T1  -- T1  = 3.2720 Angstrom
  T1  -- T1  = 3.1700 Angstrom
  T1  -- T1  = 3.2720 Angstrom
  T1  -- T1  = 3.1700 Angstrom
  T1  -- T1  = 2.7720 Angstrom