Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_167-2_1_132_OqD4Nx.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 14.07 T-atoms per nm^3
Material density = 1.404 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6512 Angstrom
T1  -- O1  = 1.5822 Angstrom
T1  -- O2  = 1.6392 Angstrom
T1  -- O3  = 1.6229 Angstrom
      mean = 1.6239 Angstrom
        t1 = 0.090981  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.091254  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5822 A <--> 1.6512 A
          Mean   = 1.6239 A
          StdDev = 0.0264 A

       t1 Range  = 0.0910 <-- 0.0910 --> 0.0910
       t2 Range  = 0.0913 <-- 0.0913 --> 0.0913

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 101.744 deg; O1  -- O1  = 3 A
O1  -- T1  -- O2  = 125.847 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  96.646 deg; O1  -- O3  = 2 A
O1  -- T1  -- O2  =  89.699 deg; O1  -- O2  = 2 A
O1  -- T1  -- O3  = 122.308 deg; O1  -- O3  = 3 A
O2  -- T1  -- O3  = 121.229 deg; O2  -- O3  = 3 A
       89.699 deg <-- 109.579 deg --> 125.847 deg

        O-T-O SUMMARY
          Range  = 89.6995 deg <--> 125.8472 deg
          Mean   = 108.5197 deg
          StdDev = 14.3295 deg

        O--O SUMMARY
          Range  = 2.2722 A <--> 2.9298 A
          Mean   = 2.6154 A
          StdDev = 0.2429 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O1  - T1  =  60.000 deg; T1  -- T1  = 2.7977 A
T1  - O1  - T1  - O2  - T1  =  93.162 deg; T1  -- T1  = 4.3949 A
T1  - O1  - T1  - O3  - T1  = 125.992 deg; T1  -- T1  = 5.3885 A
T1  - O1  - T1  - O2  - T1  =  73.664 deg; T1  -- T1  = 3.6358 A
T1  - O1  - T1  - O3  - T1  = 150.682 deg; T1  -- T1  = 5.8480 A
T1  - O2  - T1  - O3  - T1  = 129.203 deg; T1  -- T1  = 5.8578 A

        T-T-T SUMMARY
          Range  = 60.0000 deg <--> 150.6817 deg
          Mean   = 103.2911 deg
          StdDev = 33.1470 deg

        T--T SUMMARY
          Range  = 2.7977 A <--> 5.8578 A
          Mean   = 4.5443 A
          StdDev = 1.1508 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 119.808 deg ; T1  -- T1   2.7977 A

T1  -- O2  -- T1  = 162.144 deg ; T1  -- T1   3.2386 A

T1  -- O3  -- T1  = 180.000 deg ; T1  -- T1   3.2459 A


        T-O-T SUMMARY
          Range  = 119.8078° <--> 180.0000 deg
          Mean   = 153.9838 deg
          StdDev = 25.5997 deg

        T--T SUMMARY
          Range  = 2.7977 A <--> 3.2459 A
          Mean   = 3.0941 A
          StdDev = 0.2125 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O1  -- O2  = 2.2722 A
T1  -- T1  = 2.7977 Angstrom
T1  -- T1  = 2.7977 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 12
Coordination Sequence =
    1 4 8 16 32 49 70 101 135 166 212 262 305 359 427 489 550
TD10 = 794
Circuit symbol = 3.9_{3}.4.9_{2}.4.9_{3}
Weight = 31
Vertex symbol  = 3.9_{3}.4.9_{2}.4.9_{3}
Weight = 31

<TD10> = 794.000
Average ring size = 6.3871