Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_167-2_1_1104_ieKo4a.cif"

There are 12 T-atoms per unit cell
There are 24 O-atoms per unit cell

Framework density = 33.33 T-atoms per nm^3
Material density = 3.326 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.9097 Angstrom
T1  -- O1  = 1.9994 Angstrom
T1  -- O2  = 1.9989 Angstrom
T1  -- O2  = 1.9092 Angstrom
T1  -- O3  = 1.6452 Angstrom
T1  -- O4  = 1.7694 Angstrom
      mean = 1.8720 Angstrom

        T-O SUMMARY
          Range  = 1.6452 A <--> 1.9994 A
          Mean   = 1.8720 A
          StdDev = 0.1281 A

       t1 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000
       t2 Range  = 13131313.0000 <-- 0.0000 --> -13131313.0000

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O1  = 141.236 deg; O1  -- O1  = 4 A
O1  -- T1  -- O2  =  86.663 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  =  82.714 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 121.543 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  89.205 deg; O1  -- O4  = 3 A
O1  -- T1  -- O2  =  78.263 deg; O1  -- O2  = 3 A
O1  -- T1  -- O2  =  86.663 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  =  95.432 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 127.982 deg; O1  -- O4  = 3 A
O2  -- T1  -- O2  = 140.514 deg; O2  -- O2  = 4 A
O2  -- T1  -- O3  =  95.001 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 128.362 deg; O2  -- O4  = 3 A
O2  -- T1  -- O3  = 122.859 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  =  89.509 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  46.091 deg; O3  -- O4  = 1 A
       46.091 deg <-- 102.136 deg --> 141.236 deg

        O-T-O SUMMARY
          Range  = 46.0913 deg <--> 141.2365 deg
          Mean   = 102.1358 deg
          StdDev = 26.1625 deg

        O--O SUMMARY
          Range  = 1.3416 A <--> 3.6877 A
          Mean   = 2.8475 A
          StdDev = 0.5712 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  =  93.193 deg ; T1  -- T1   2.8407 A
T1  -- O1  -- T1  =  86.649 deg ; T1  -- T1   2.6829 A
T1  -- O1  -- T1  = 175.654 deg ; T1  -- T1   3.8166 A
T1  -- O1  -- T1  = 175.849 deg ; T1  -- T1   3.9961 A
T1  -- O1  -- T1  =  86.649 deg ; T1  -- T1   2.6829 A
T1  -- O1  -- T1  =  93.193 deg ; T1  -- T1   2.8407 A

T1  -- O2  -- T1  =  93.221 deg ; T1  -- T1   2.8407 A
T1  -- O2  -- T1  =  86.674 deg ; T1  -- T1   2.6829 A
T1  -- O2  -- T1  = 176.609 deg ; T1  -- T1   3.9961 A
T1  -- O2  -- T1  = 176.449 deg ; T1  -- T1   3.8166 A
T1  -- O2  -- T1  =  86.674 deg ; T1  -- T1   2.6829 A
T1  -- O2  -- T1  =  93.221 deg ; T1  -- T1   2.8407 A

T1  -- O3  -- T1  = 178.821 deg ; T1  -- T1   3.2902 A

T1  -- O4  -- T1  = 180.000 deg ; T1  -- T1   3.5388 A


        T-O-T SUMMARY
          Range  = 86.6492° <--> 180.0000 deg
          Mean   = 127.3468 deg
          StdDev = 43.4133 deg

        T--T SUMMARY
          Range  = 2.6829 A <--> 3.9961 A
          Mean   = 3.1821 A
          StdDev = 0.5179 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O3  -- O4  = 1.3416 A
O3  -- O4  = 1.3416 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has only 5 neighboring T-atoms within 3.50 A, but 6 bridging O-atoms
  T1  -- T1  = 3.2902 Angstrom
  T1  -- T1  = 2.8407 Angstrom
  T1  -- T1  = 2.8407 Angstrom
  T1  -- T1  = 2.6829 Angstrom
  T1  -- T1  = 2.6829 Angstrom