Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_99335652_gZ3Bzw.cif"

There are 144 T-atoms per unit cell
There are 288 O-atoms per unit cell

Framework density = 21.56 T-atoms per nm^3
Material density = 2.151 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.5829 Angstrom
T1  -- O2  = 1.6735 Angstrom
T1  -- O3  = 1.7329 Angstrom
T1  -- O4  = 1.6008 Angstrom
      mean = 1.6475 Angstrom
        t1 = 0.069972  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.043192  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.6778 Angstrom
T2  -- O5  = 1.6984 Angstrom
T2  -- O6  = 1.5631 Angstrom
T2  -- O7  = 1.6649 Angstrom
      mean = 1.6510 Angstrom
        t1 = 0.079089  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.093349  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.5521 Angstrom
T3  -- O8  = 1.5828 Angstrom
T3  -- O9  = 1.5736 Angstrom
T3  -- O10 = 1.6055 Angstrom
      mean = 1.5785 Angstrom
        t1 = 0.030435  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.029683  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.6414 Angstrom
T4  -- O11 = 1.6370 Angstrom
T4  -- O7  = 1.6414 Angstrom
T4  -- O11 = 1.6370 Angstrom
      mean = 1.6392 Angstrom
        t1 = 0.026878  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.018728  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O4  = 1.6211 Angstrom
T5  -- O4  = 1.6210 Angstrom
T5  -- O11 = 1.6385 Angstrom
T5  -- O11 = 1.6385 Angstrom
      mean = 1.6298 Angstrom
        t1 = 0.039729  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.025053  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5521 A <--> 1.7329 A
          Mean   = 1.6279 A
          StdDev = 0.0504 A

       t1 Range  = 0.0269 <-- 0.0492 --> 0.0791
       t2 Range  = 0.0187 <-- 0.0420 --> 0.0933

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 107.421 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 110.579 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  95.656 deg; O1  -- O4  = 2 A
O2  -- T1  -- O3  = 120.652 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 112.137 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 107.544 deg; O3  -- O4  = 3 A
       95.656 deg <-- 108.998 deg --> 120.652 deg

O3  -- T2  -- O5  = 122.398 deg; O3  -- O5  = 3 A
O3  -- T2  -- O6  =  92.347 deg; O3  -- O6  = 2 A
O3  -- T2  -- O7  = 111.639 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 102.074 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 114.462 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 110.259 deg; O6  -- O7  = 3 A
       92.347 deg <-- 108.863 deg --> 122.398 deg

O6  -- T3  -- O8  = 107.525 deg; O6  -- O8  = 3 A
O6  -- T3  -- O9  = 104.505 deg; O6  -- O9  = 2 A
O6  -- T3  -- O10 = 110.328 deg; O6  -- O10 = 3 A
O8  -- T3  -- O9  = 110.080 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 111.289 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 112.781 deg; O9  -- O10 = 3 A
       104.505 deg <-- 109.418 deg --> 112.781 deg

O7  -- T4  -- O11 = 105.162 deg; O7  -- O11 = 3 A
O7  -- T4  -- O7  = 112.879 deg; O7  -- O7  = 3 A
O7  -- T4  -- O11 = 110.947 deg; O7  -- O11 = 3 A
O11 -- T4  -- O7  = 110.947 deg; O11 -- O7  = 3 A
O11 -- T4  -- O11 = 111.901 deg; O11 -- O11 = 3 A
O7  -- T4  -- O11 = 105.162 deg; O7  -- O11 = 3 A
       105.162 deg <-- 109.500 deg --> 112.879 deg

O4  -- T5  -- O4  =  97.230 deg; O4  -- O4  = 2 A
O4  -- T5  -- O11 = 111.000 deg; O4  -- O11 = 3 A
O4  -- T5  -- O11 = 112.174 deg; O4  -- O11 = 3 A
O4  -- T5  -- O11 = 112.180 deg; O4  -- O11 = 3 A
O4  -- T5  -- O11 = 111.006 deg; O4  -- O11 = 3 A
O11 -- T5  -- O11 = 112.365 deg; O11 -- O11 = 3 A
       97.230 deg <-- 109.326 deg --> 112.365 deg

        O-T-O SUMMARY
          Range  = 92.3473 deg <--> 122.3980 deg
          Mean   = 109.1373 deg
          StdDev = 6.3985 deg

        O--O SUMMARY
          Range  = 2.3394 A <--> 2.9598 A
          Mean   = 2.6559 A
          StdDev = 0.1434 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T2  = 130.530 deg; T1  -- T2  = 5.7209 A
T1  - O1  - T1  - O3  - T1  =  90.000 deg; T1  -- T1  = 4.3552 A
T1  - O1  - T1  - O4  - T5  = 128.470 deg; T1  -- T5  = 5.2720 A
T2  - O2  - T1  - O3  - T1  = 117.298 deg; T2  -- T1  = 5.5046 A
T2  - O2  - T1  - O4  - T5  =  96.478 deg; T2  -- T5  = 4.5905 A
T1  - O3  - T1  - O4  - T5  =  84.174 deg; T1  -- T5  = 4.0287 A

T1  - O3  - T2  - O5  - T2  = 136.221 deg; T1  -- T2  = 5.9015 A
T1  - O3  - T2  - O6  - T3  =  86.152 deg; T1  -- T3  = 4.2461 A
T1  - O3  - T2  - O7  - T4  =  97.100 deg; T1  -- T4  = 4.8354 A
T2  - O5  - T2  - O6  - T3  =  87.033 deg; T2  -- T3  = 4.1177 A
T2  - O5  - T2  - O7  - T4  = 126.103 deg; T2  -- T4  = 5.5486 A
T3  - O6  - T2  - O7  - T4  =  90.020 deg; T3  -- T4  = 4.2955 A

T2  - O6  - T3  - O8  - T3  = 141.831 deg; T2  -- T3  = 5.3096 A
T2  - O6  - T3  - O9  - T3  =  92.967 deg; T2  -- T3  = 4.1177 A
T2  - O6  - T3  - O10 - T3  = 109.787 deg; T2  -- T3  = 4.7155 A
T3  - O8  - T3  - O9  - T3  = 120.000 deg; T3  -- T3  = 4.7392 A
T3  - O8  - T3  - O10 - T3  =  90.588 deg; T3  -- T3  = 3.9528 A
T3  - O9  - T3  - O10 - T3  =  89.412 deg; T3  -- T3  = 3.9528 A

T2  - O7  - T4  - O11 - T5  =  86.710 deg; T2  -- T5  = 4.3941 A
T2  - O7  - T4  - O7  - T2  = 118.588 deg; T2  -- T2  = 5.4296 A
T2  - O7  - T4  - O11 - T5  = 133.206 deg; T2  -- T5  = 5.8739 A
T5  - O11 - T4  - O7  - T2  = 133.206 deg; T5  -- T2  = 5.8739 A
T5  - O11 - T4  - O11 - T5  = 104.215 deg; T5  -- T5  = 5.1177 A
T2  - O7  - T4  - O11 - T5  =  86.712 deg; T2  -- T5  = 4.3942 A

T1  - O4  - T5  - O4  - T4  = 128.786 deg; T1  -- T4  = 5.4956 A
T1  - O4  - T5  - O11 - T4  =  83.852 deg; T1  -- T4  = 4.0805 A
T1  - O4  - T5  - O11 - T1  = 132.988 deg; T1  -- T1  = 5.2247 A
T4  - O4  - T5  - O11 - T4  =  98.771 deg; T4  -- T4  = 4.9228 A
T4  - O4  - T5  - O11 - T1  =  83.850 deg; T4  -- T1  = 4.0805 A
T4  - O11 - T5  - O11 - T1  = 128.782 deg; T4  -- T1  = 5.4956 A

        T-T-T SUMMARY
          Range  = 83.8496 deg <--> 141.8309 deg
          Mean   = 107.8058 deg
          StdDev = 19.9019 deg

        T--T SUMMARY
          Range  = 3.9528 A <--> 5.9015 A
          Mean   = 4.8716 A
          StdDev = 0.6390 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 169.514 deg ; T1  -- T1   3.1526 A

T1  -- O2  -- T1  = 127.727 deg ; T1  -- T1   3.0048 A

T1  -- O3  -- T2  = 149.761 deg ; T1  -- T2   3.2926 A

T1  -- O4  -- T5  = 124.304 deg ; T1  -- T5   2.8488 A

T2  -- O5  -- T2  = 129.065 deg ; T2  -- T2   3.0668 A

T2  -- O6  -- T3  = 138.287 deg ; T2  -- T3   2.9111 A

T2  -- O7  -- T4  = 145.484 deg ; T2  -- T4   3.1575 A

T3  -- O8  -- T3  = 128.633 deg ; T3  -- T3   2.8528 A

T3  -- O9  -- T3  = 118.658 deg ; T3  -- T3   2.7068 A

T3  -- O10 -- T3  = 118.915 deg ; T3  -- T3   2.7654 A

T4  -- O11 -- T5  = 163.725 deg ; T4  -- T5   3.2425 A


        T-O-T SUMMARY
          Range  = 118.6582° <--> 169.5140 deg
          Mean   = 136.4010 deg
          StdDev = 16.0290 deg

        T--T SUMMARY
          Range  = 2.7068 A <--> 3.2926 A
          Mean   = 2.9886 A
          StdDev = 0.1853 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T3  -- T3  = 2.7068 Angstrom
T3  -- T3  = 2.7654 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 24 44 72 100 133 182 235 289 347 413 496 582 666 761
TD10 = 1095
Circuit symbol = 4.6.5.7_{2}.5_{2}.6
Weight = 14
Vertex symbol  = 4.8.5.8_{2}.5_{2}.6
Weight = 26

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 23 38 64 101 140 180 224 282 347 419 490 563 656 754
TD10 = 1068
Circuit symbol = 4.5.5.8_{2}.6.7_{2}
Weight = 19
Vertex symbol  = 4.5.5.8.6.8_{2}
Weight = 26

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 16 27 46 77 119 166 211 257 314 385 465 541 619 704
TD10 = 933
Circuit symbol = 4.4.4.6.5.6_{2}
Weight = 16
Vertex symbol  = 4.4.4.6.5.6
Weight = 16

T4 (Si): multiplicity = 18
Coordination Sequence =
    1 4 12 22 42 63 94 137 180 226 282 348 418 498 566 644 750
TD10 = 1063
Circuit symbol = 5.5.5.5.8_{4}.8_{4}
Weight = 27
Vertex symbol  = 5.5.5.5.8.8
Weight = 21

T5 (Si): multiplicity = 18
Coordination Sequence =
    1 4 12 24 46 69 94 135 174 226 290 338 414 488 554 659 758
TD10 = 1075
Circuit symbol = 5.5.5.5.6_{2}.8_{4}
Weight = 21
Vertex symbol  = 5.5.5.5.8_{2}.10_{3}
Weight = 30

<TD10> = 1041.250
Average ring size = 5.6250