Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_99219636_a6whuP.cif"

There are 144 T-atoms per unit cell
There are 288 O-atoms per unit cell

Framework density = 23.29 T-atoms per nm^3
Material density = 2.324 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.7123 Angstrom
T1  -- O2  = 1.6636 Angstrom
T1  -- O3  = 1.7397 Angstrom
T1  -- O4  = 1.5998 Angstrom
      mean = 1.6789 Angstrom
        t1 = 0.079452  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.088734  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6011 Angstrom
T2  -- O5  = 1.5981 Angstrom
T2  -- O6  = 1.6011 Angstrom
T2  -- O7  = 1.5458 Angstrom
      mean = 1.5866 Angstrom
        t1 = 0.022659  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.012259  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O8  = 1.6156 Angstrom
T3  -- O9  = 1.6735 Angstrom
T3  -- O10 = 1.6564 Angstrom
T3  -- O11 = 1.7438 Angstrom
      mean = 1.6723 Angstrom
        t1 = 0.050414  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.027528  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O10 = 1.6302 Angstrom
T4  -- O12 = 1.5415 Angstrom
T4  -- O10 = 1.6302 Angstrom
T4  -- O12 = 1.5415 Angstrom
      mean = 1.5859 Angstrom
        t1 = 0.058970  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.084213  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O7  = 1.5875 Angstrom
T5  -- O7  = 1.5874 Angstrom
T5  -- O11 = 1.6198 Angstrom
T5  -- O11 = 1.6197 Angstrom
      mean = 1.6036 Angstrom
        t1 = 0.066976  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.060642  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5415 A <--> 1.7438 A
          Mean   = 1.6331 A
          StdDev = 0.0592 A

       t1 Range  = 0.0227 <-- 0.0557 --> 0.0795
       t2 Range  = 0.0123 <-- 0.0547 --> 0.0887

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.784 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 125.047 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  =  99.530 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 113.534 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 105.312 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 101.366 deg; O3  -- O4  = 3 A
       99.530 deg <-- 108.929 deg --> 125.047 deg

O4  -- T2  -- O5  = 110.125 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 109.310 deg; O4  -- O6  = 3 A
O4  -- T2  -- O7  = 112.477 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 110.988 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 107.613 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 106.274 deg; O6  -- O7  = 3 A
       106.274 deg <-- 109.464 deg --> 112.477 deg

O8  -- T3  -- O9  = 106.828 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 108.046 deg; O8  -- O10 = 3 A
O8  -- T3  -- O11 = 107.588 deg; O8  -- O11 = 3 A
O9  -- T3  -- O10 = 109.396 deg; O9  -- O10 = 3 A
O9  -- T3  -- O11 = 115.932 deg; O9  -- O11 = 3 A
O10 -- T3  -- O11 = 108.775 deg; O10 -- O11 = 3 A
       106.828 deg <-- 109.427 deg --> 115.932 deg

O10 -- T4  -- O12 = 106.397 deg; O10 -- O12 = 3 A
O10 -- T4  -- O10 = 124.954 deg; O10 -- O10 = 3 A
O10 -- T4  -- O12 = 107.078 deg; O10 -- O12 = 3 A
O12 -- T4  -- O10 = 107.078 deg; O12 -- O10 = 3 A
O12 -- T4  -- O12 = 102.901 deg; O12 -- O12 = 2 A
O10 -- T4  -- O12 = 106.397 deg; O10 -- O12 = 3 A
       102.901 deg <-- 109.134 deg --> 124.954 deg

O7  -- T5  -- O7  = 117.867 deg; O7  -- O7  = 3 A
O7  -- T5  -- O11 =  98.606 deg; O7  -- O11 = 2 A
O7  -- T5  -- O11 = 106.675 deg; O7  -- O11 = 3 A
O7  -- T5  -- O11 = 106.681 deg; O7  -- O11 = 3 A
O7  -- T5  -- O11 =  98.616 deg; O7  -- O11 = 2 A
O11 -- T5  -- O11 = 129.931 deg; O11 -- O11 = 3 A
       98.606 deg <-- 109.730 deg --> 129.931 deg

        O-T-O SUMMARY
          Range  = 98.6064 deg <--> 129.9313 deg
          Mean   = 109.1134 deg
          StdDev = 7.2456 deg

        O--O SUMMARY
          Range  = 2.4111 A <--> 3.0626 A
          Mean   = 2.6395 A
          StdDev = 0.1451 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  90.000 deg; T1  -- T1  = 4.5631 A
T1  - O1  - T1  - O3  - T1  = 150.000 deg; T1  -- T1  = 6.3935 A
T1  - O1  - T1  - O4  - T2  =  97.763 deg; T1  -- T2  = 4.9652 A
T1  - O2  - T1  - O3  - T1  = 120.000 deg; T1  -- T1  = 5.4439 A
T1  - O2  - T1  - O4  - T2  =  86.320 deg; T1  -- T2  = 4.2800 A
T1  - O3  - T1  - O4  - T2  =  85.130 deg; T1  -- T2  = 4.3491 A

T1  - O4  - T2  - O5  - T2  =  93.680 deg; T1  -- T2  = 4.2800 A
T1  - O4  - T2  - O6  - T2  =  94.870 deg; T1  -- T2  = 4.3491 A
T1  - O4  - T2  - O7  - T5  = 121.110 deg; T1  -- T5  = 5.3414 A
T2  - O5  - T2  - O6  - T2  = 120.000 deg; T2  -- T2  = 4.6170 A
T2  - O5  - T2  - O7  - T5  = 120.321 deg; T2  -- T5  = 4.8396 A
T2  - O6  - T2  - O7  - T5  = 104.701 deg; T2  -- T5  = 4.4512 A

T3  - O8  - T3  - O9  - T4  =  90.385 deg; T3  -- T4  = 4.2295 A
T3  - O8  - T3  - O10 - T5  = 117.918 deg; T3  -- T5  = 4.9550 A
T3  - O8  - T3  - O11 - T3  = 120.000 deg; T3  -- T3  = 5.3943 A
T4  - O9  - T3  - O10 - T5  = 139.366 deg; T4  -- T5  = 5.3687 A
T4  - O9  - T3  - O11 - T3  =  88.352 deg; T4  -- T3  = 4.3044 A
T5  - O10 - T3  - O11 - T3  =  99.930 deg; T5  -- T3  = 4.5959 A

T3  - O10 - T4  - O12 - T4  =  91.648 deg; T3  -- T4  = 4.3044 A
T3  - O10 - T4  - O10 - T4  =  89.615 deg; T3  -- T4  = 4.2295 A
T3  - O10 - T4  - O12 - T3  = 177.474 deg; T3  -- T3  = 5.9028 A
T4  - O12 - T4  - O10 - T4  = 120.000 deg; T4  -- T4  = 5.2805 A
T4  - O12 - T4  - O12 - T3  =  89.615 deg; T4  -- T3  = 4.2295 A
T4  - O10 - T4  - O12 - T3  =  91.648 deg; T4  -- T3  = 4.3044 A

T2  - O7  - T5  - O7  - T2  = 150.597 deg; T2  -- T2  = 5.6720 A
T2  - O7  - T5  - O11 - T3  =  87.005 deg; T2  -- T3  = 3.9286 A
T2  - O7  - T5  - O11 - T3  =  87.974 deg; T2  -- T3  = 3.9633 A
T2  - O7  - T5  - O11 - T3  =  87.976 deg; T2  -- T3  = 3.9633 A
T2  - O7  - T5  - O11 - T3  =  87.010 deg; T2  -- T3  = 3.9286 A
T3  - O11 - T5  - O11 - T3  = 160.139 deg; T3  -- T3  = 5.4615 A

        T-T-T SUMMARY
          Range  = 85.1302 deg <--> 177.4736 deg
          Mean   = 108.5389 deg
          StdDev = 25.1431 deg

        T--T SUMMARY
          Range  = 3.9286 A <--> 6.3935 A
          Mean   = 4.7093 A
          StdDev = 0.6205 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 163.500 deg ; T1  -- T1   3.3891 A

T1  -- O2  -- T1  = 133.363 deg ; T1  -- T1   3.0555 A

T1  -- O3  -- T1  = 136.341 deg ; T1  -- T1   3.2298 A

T1  -- O4  -- T2  = 176.724 deg ; T1  -- T2   3.1997 A

T2  -- O5  -- T2  = 111.673 deg ; T2  -- T2   2.6447 A

T2  -- O6  -- T2  = 114.061 deg ; T2  -- T2   2.6865 A

T2  -- O7  -- T5  = 138.699 deg ; T2  -- T5   2.9321 A

T3  -- O8  -- T3  = 137.243 deg ; T3  -- T3   3.0090 A

T3  -- O9  -- T3  = 148.150 deg ; T3  -- T3   3.2186 A

T3  -- O10 -- T4  = 127.853 deg ; T3  -- T4   2.9521 A

T3  -- O11 -- T5  = 110.967 deg ; T3  -- T5   2.7723 A

T4  -- O12 -- T4  = 162.898 deg ; T4  -- T4   3.0487 A


        T-O-T SUMMARY
          Range  = 110.9670° <--> 176.7243 deg
          Mean   = 137.3933 deg
          StdDev = 20.2057 deg

        T--T SUMMARY
          Range  = 2.6447 A <--> 3.3891 A
          Mean   = 3.0099 A
          StdDev = 0.2245 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T2  -- T2  = 2.6447 Angstrom
T2  -- T2  = 2.6865 Angstrom
T3  -- T5  = 2.7723 Angstrom
T5  -- T3  = 2.7723 Angstrom
T5  -- T3  = 2.7722 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 18 35 61 92 124 161 209 267 329 391 457 534 622 714
TD10 = 981
Circuit symbol = 4.4.4.8_{2}.6.6_{2}
Weight = 11
Vertex symbol  = 4.4.4.10_{2}.6.9
Weight = 23

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 20 36 57 80 109 148 196 248 301 361 434 519 608 695
TD10 = 909
Circuit symbol = 4.6.4.6_{3}.6_{2}.8_{4}
Weight = 19
Vertex symbol  = 4.6.4.6_{3}.6.9
Weight = 24

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 19 33 52 76 105 142 184 228 276 333 403 481 563 650
TD10 = 854
Circuit symbol = 4.6.4.6_{3}.6_{2}.8_{4}
Weight = 19
Vertex symbol  = 4.6.4.6_{3}.6.9
Weight = 24

T4 (Si): multiplicity = 18
Coordination Sequence =
    1 4 8 15 28 48 72 99 132 174 218 264 322 393 468 541 620
TD10 = 799
Circuit symbol = 4.4.4.4.6_{2}.6_{3}
Weight = 12
Vertex symbol  = 4.4.4.4.6.9
Weight = 18

T5 (Si): multiplicity = 18
Coordination Sequence =
    1 4 12 23 34 50 76 112 148 189 238 287 342 418 506 595 680
TD10 = 887
Circuit symbol = 6.6.6.6.6_{2}.6_{2}
Weight = 16
Vertex symbol  = 6.6.6.6.6_{2}.6_{2}
Weight = 16

<TD10> = 896.750
Average ring size = 5.5328