Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_93003785_p1FOzR.cif"

There are 162 T-atoms per unit cell
There are 324 O-atoms per unit cell

Framework density = 16.73 T-atoms per nm^3
Material density = 1.669 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6164 Angstrom
T1  -- O2  = 1.6481 Angstrom
T1  -- O3  = 1.6321 Angstrom
T1  -- O4  = 1.6760 Angstrom
      mean = 1.6432 Angstrom
        t1 = 0.025725  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.015786  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O4  = 1.6455 Angstrom
T2  -- O5  = 1.6612 Angstrom
T2  -- O6  = 1.6016 Angstrom
T2  -- O7  = 1.6864 Angstrom
      mean = 1.6487 Angstrom
        t1 = 0.049503  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.053774  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.5870 Angstrom
T3  -- O8  = 1.5966 Angstrom
T3  -- O9  = 1.5881 Angstrom
T3  -- O10 = 1.5709 Angstrom
      mean = 1.5857 Angstrom
        t1 = 0.026565  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.019377  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O7  = 1.7106 Angstrom
T4  -- O10 = 1.5985 Angstrom
T4  -- O11 = 1.6739 Angstrom
T4  -- O12 = 1.6770 Angstrom
      mean = 1.6650 Angstrom
        t1 = 0.189189  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.228234  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O12 = 1.6044 Angstrom
T5  -- O12 = 1.6046 Angstrom
T5  -- O13 = 1.6262 Angstrom
T5  -- O13 = 1.6262 Angstrom
      mean = 1.6154 Angstrom
        t1 = 0.058051  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.037373  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5709 A <--> 1.7106 A
          Mean   = 1.6334 A
          StdDev = 0.0396 A

       t1 Range  = 0.0257 <-- 0.0698 --> 0.1892
       t2 Range  = 0.0158 <-- 0.0709 --> 0.2282

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 108.748 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.112 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 107.884 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.368 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 112.046 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 109.568 deg; O3  -- O4  = 3 A
       107.884 deg <-- 109.454 deg --> 112.046 deg

O4  -- T2  -- O5  = 109.764 deg; O4  -- O5  = 3 A
O4  -- T2  -- O6  = 100.143 deg; O4  -- O6  = 2 A
O4  -- T2  -- O7  = 112.616 deg; O4  -- O7  = 3 A
O5  -- T2  -- O6  = 105.046 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 116.454 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 111.340 deg; O6  -- O7  = 3 A
       100.143 deg <-- 109.227 deg --> 116.454 deg

O6  -- T3  -- O8  = 109.783 deg; O6  -- O8  = 3 A
O6  -- T3  -- O9  = 112.738 deg; O6  -- O9  = 3 A
O6  -- T3  -- O10 = 102.946 deg; O6  -- O10 = 2 A
O8  -- T3  -- O9  = 110.159 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 111.869 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 109.188 deg; O9  -- O10 = 3 A
       102.946 deg <-- 109.447 deg --> 112.738 deg

O7  -- T4  -- O10 =  65.911 deg; O7  -- O10 = 2 A
O7  -- T4  -- O11 = 136.635 deg; O7  -- O11 = 3 A
O7  -- T4  -- O12 =  85.698 deg; O7  -- O12 = 2 A
O10 -- T4  -- O11 =  77.651 deg; O10 -- O11 = 2 A
O10 -- T4  -- O12 = 114.300 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 =  88.751 deg; O11 -- O12 = 2 A
       65.911 deg <-- 94.825 deg --> 136.635 deg

O12 -- T5  -- O12 =  91.166 deg; O12 -- O12 = 2 A
O12 -- T5  -- O13 = 110.569 deg; O12 -- O13 = 3 A
O12 -- T5  -- O13 = 114.963 deg; O12 -- O13 = 3 A
O12 -- T5  -- O13 = 114.950 deg; O12 -- O13 = 3 A
O12 -- T5  -- O13 = 110.562 deg; O12 -- O13 = 3 A
O13 -- T5  -- O13 = 112.938 deg; O13 -- O13 = 3 A
       91.166 deg <-- 109.191 deg --> 114.963 deg

        O-T-O SUMMARY
          Range  = 65.9114 deg <--> 136.6354 deg
          Mean   = 106.0983 deg
          StdDev = 13.4847 deg

        O--O SUMMARY
          Range  = 1.8025 A <--> 3.1450 A
          Mean   = 2.5912 A
          StdDev = 0.2515 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 160.205 deg ; T1  -- T1   3.1847 A

T1  -- O2  -- T1  = 146.261 deg ; T1  -- T1   3.1545 A

T1  -- O3  -- T1  = 146.976 deg ; T1  -- T1   3.1295 A

T1  -- O4  -- T2  = 124.598 deg ; T1  -- T2   2.9409 A

T2  -- O5  -- T2  = 135.473 deg ; T2  -- T2   3.0748 A

T2  -- O6  -- T3  = 140.598 deg ; T2  -- T3   3.0020 A

T2  -- O7  -- T4  = 162.114 deg ; T2  -- T4   3.3557 A

T3  -- O8  -- T3  = 127.311 deg ; T3  -- T3   2.8615 A

T3  -- O9  -- T3  = 112.042 deg ; T3  -- T3   2.6338 A

T3  -- O10 -- T4  = 120.402 deg ; T3  -- T4   2.7503 A

T4  -- O11 -- T4  = 159.015 deg ; T4  -- T4   3.2916 A

T4  -- O12 -- T5  = 113.112 deg ; T4  -- T5   2.7384 A

T5  -- O13 -- T5  = 118.313 deg ; T5  -- T5   2.7923 A


        T-O-T SUMMARY
          Range  = 112.0425° <--> 162.1143 deg
          Mean   = 136.5811 deg
          StdDev = 17.3248 deg

        T--T SUMMARY
          Range  = 2.6338 A <--> 3.3557 A
          Mean   = 3.0011 A
          StdDev = 0.2195 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

SOME OXYGEN ATOMS ARE TOO CLOSE TO EACH OTHER
O7  -- O10 = 1.8025 A
O10 -- O11 = 2.0524 A
O12 -- O12 = 2.2921 A

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T2  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T2  -- T1  = 2.9409 Angstrom
  T2  -- T2  = 3.0748 Angstrom
  T2  -- T3  = 3.0020 Angstrom
  T2  -- T4  = 2.9543 Angstrom
  T2  -- T4  = 3.3557 Angstrom
T3  -- T3  = 2.6338 Angstrom
T3  -- T4  = 2.7503 Angstrom
T4  has 6 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T2  = 2.9543 Angstrom
  T4  -- T2  = 3.3557 Angstrom
  T4  -- T3  = 2.7503 Angstrom
  T4  -- T4  = 2.2947 Angstrom
  T4  -- T4  = 3.2916 Angstrom
  T4  -- T5  = 2.7384 Angstrom
T5  -- T4  = 2.7384 Angstrom
T5  -- T4  = 2.7384 Angstrom
T5  -- T5  = 2.7923 Angstrom
T5  -- T5  = 2.7923 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 17 28 43 64 90 118 144 170 202 243 294 352 409 461
TD10 = 688
Circuit symbol = 4.4.4.6.6.6_{2}
Weight = 14
Vertex symbol  = 4.4.4.6.6.12
Weight = 23

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 18 28 43 62 86 113 143 177 209 247 295 347 403 458
TD10 = 685
Circuit symbol = 4.5.4.8_{2}.6.6_{2}
Weight = 17
Vertex symbol  = 4.5.4.8.6.6
Weight = 17

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 18 27 40 61 89 119 146 170 199 239 296 359 417 465
TD10 = 685
Circuit symbol = 4.4.5.6.6.6
Weight = 18
Vertex symbol  = 4.4.5.6.6.6
Weight = 18

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 19 30 44 60 82 111 143 177 213 252 294 343 396 450
TD10 = 681
Circuit symbol = 4.5.4.6_{2}.5.7
Weight = 13
Vertex symbol  = 4.5.4.6.5.12_{2}
Weight = 28

T5 (Si): multiplicity = 18
Coordination Sequence =
    1 4 10 19 30 43 58 78 104 138 178 219 258 293 328 374 438
TD10 = 663
Circuit symbol = 4.4.5_{2}.6.7_{3}.7_{3}
Weight = 16
Vertex symbol  = 4.4.5_{2}.6.8.8
Weight = 22

<TD10> = 682.333
Average ring size = 5.2615