Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_86151252_0nVhjQ.cif"

There are 162 T-atoms per unit cell
There are 324 O-atoms per unit cell

Framework density = 24.46 T-atoms per nm^3
Material density = 2.440 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6072 Angstrom
T1  -- O2  = 1.6447 Angstrom
T1  -- O3  = 1.4494 Angstrom
T1  -- O4  = 1.6514 Angstrom
      mean = 1.5882 Angstrom
        t1 = 0.079351  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.055979  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O3  = 1.4455 Angstrom
T2  -- O5  = 1.6036 Angstrom
T2  -- O6  = 1.6178 Angstrom
T2  -- O7  = 1.7218 Angstrom
      mean = 1.5972 Angstrom
        t1 = 0.040947  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.042614  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O4  = 1.6646 Angstrom
T3  -- O8  = 1.6762 Angstrom
T3  -- O9  = 1.6489 Angstrom
T3  -- O10 = 1.5976 Angstrom
      mean = 1.6468 Angstrom
        t1 = 0.048460  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.032223  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O9  = 1.6870 Angstrom
T4  -- O10 = 1.5934 Angstrom
T4  -- O11 = 1.6199 Angstrom
T4  -- O12 = 1.6861 Angstrom
      mean = 1.6466 Angstrom
        t1 = 0.047173  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.026008  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O7  = 1.6686 Angstrom
T5  -- O12 = 1.6307 Angstrom
T5  -- O7  = 1.6686 Angstrom
T5  -- O12 = 1.6307 Angstrom
      mean = 1.6496 Angstrom
        t1 = 0.058172  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.052439  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.4455 A <--> 1.7218 A
          Mean   = 1.6230 A
          StdDev = 0.0709 A

       t1 Range  = 0.0409 <-- 0.0548 --> 0.0794
       t2 Range  = 0.0260 <-- 0.0419 --> 0.0560

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 111.776 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 108.239 deg; O1  -- O3  = 2 A
O1  -- T1  -- O4  = 111.878 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 101.258 deg; O2  -- O3  = 2 A
O2  -- T1  -- O4  = 124.003 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  =  96.654 deg; O3  -- O4  = 2 A
       96.654 deg <-- 108.968 deg --> 124.003 deg

O3  -- T2  -- O5  = 109.342 deg; O3  -- O5  = 2 A
O3  -- T2  -- O6  = 107.305 deg; O3  -- O6  = 2 A
O3  -- T2  -- O7  = 108.691 deg; O3  -- O7  = 3 A
O5  -- T2  -- O6  = 111.454 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 111.344 deg; O5  -- O7  = 3 A
O6  -- T2  -- O7  = 108.583 deg; O6  -- O7  = 3 A
       107.305 deg <-- 109.453 deg --> 111.454 deg

O4  -- T3  -- O8  = 118.935 deg; O4  -- O8  = 3 A
O4  -- T3  -- O9  = 103.944 deg; O4  -- O9  = 3 A
O4  -- T3  -- O10 = 104.975 deg; O4  -- O10 = 3 A
O8  -- T3  -- O9  = 115.269 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 104.635 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 108.324 deg; O9  -- O10 = 3 A
       103.944 deg <-- 109.347 deg --> 118.935 deg

O9  -- T4  -- O10 = 105.762 deg; O9  -- O10 = 3 A
O9  -- T4  -- O11 = 108.362 deg; O9  -- O11 = 3 A
O9  -- T4  -- O12 = 119.408 deg; O9  -- O12 = 3 A
O10 -- T4  -- O11 = 106.933 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 105.527 deg; O10 -- O12 = 3 A
O11 -- T4  -- O12 = 110.091 deg; O11 -- O12 = 3 A
       105.527 deg <-- 109.347 deg --> 119.408 deg

O7  -- T5  -- O12 = 103.914 deg; O7  -- O12 = 3 A
O7  -- T5  -- O7  = 117.694 deg; O7  -- O7  = 3 A
O7  -- T5  -- O12 = 116.071 deg; O7  -- O12 = 3 A
O12 -- T5  -- O7  = 116.071 deg; O12 -- O7  = 3 A
O12 -- T5  -- O12 =  97.831 deg; O12 -- O12 = 2 A
O7  -- T5  -- O12 = 103.914 deg; O7  -- O12 = 3 A
       97.831 deg <-- 109.249 deg --> 117.694 deg

        O-T-O SUMMARY
          Range  = 96.6539 deg <--> 124.0030 deg
          Mean   = 109.1922 deg
          StdDev = 6.2973 deg

        O--O SUMMARY
          Range  = 2.3200 A <--> 2.9125 A
          Mean   = 2.6486 A
          StdDev = 0.1495 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 163.000 deg ; T1  -- T1   3.1789 A

T1  -- O2  -- T1  = 125.348 deg ; T1  -- T1   2.9222 A

T1  -- O3  -- T2  = 161.180 deg ; T1  -- T2   2.8559 A

T1  -- O4  -- T3  = 122.238 deg ; T1  -- T3   2.9035 A

T2  -- O5  -- T2  = 119.945 deg ; T2  -- T2   2.7767 A

T2  -- O6  -- T2  = 116.184 deg ; T2  -- T2   2.7465 A

T2  -- O7  -- T5  = 161.000 deg ; T2  -- T5   3.3439 A

T3  -- O8  -- T3  = 150.052 deg ; T3  -- T3   3.2385 A

T3  -- O9  -- T4  = 131.845 deg ; T3  -- T4   3.0458 A

T3  -- O10 -- T4  = 134.575 deg ; T3  -- T4   2.9436 A

T4  -- O11 -- T4  = 130.091 deg ; T4  -- T4   2.9373 A

T4  -- O12 -- T5  = 144.427 deg ; T4  -- T5   3.1583 A


        T-O-T SUMMARY
          Range  = 116.1837° <--> 163.0005 deg
          Mean   = 138.3238 deg
          StdDev = 16.3469 deg

        T--T SUMMARY
          Range  = 2.7465 A <--> 3.3439 A
          Mean   = 3.0043 A
          StdDev = 0.1808 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------

T-T-T analysis was not conducted.

SOME T-ATOM DISTANCES ARE OUTSIDE THE NORMAL RANGE
T1  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T1  -- T1  = 3.1789 Angstrom
  T1  -- T1  = 2.9222 Angstrom
  T1  -- T2  = 2.8559 Angstrom
  T1  -- T3  = 2.9035 Angstrom
  T1  -- T4  = 3.3607 Angstrom
T2  -- T2  = 2.7767 Angstrom
T2  -- T2  = 2.7465 Angstrom
T3  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T3  -- T1  = 2.9035 Angstrom
  T3  -- T3  = 3.2385 Angstrom
  T3  -- T4  = 3.0458 Angstrom
  T3  -- T4  = 2.9436 Angstrom
  T3  -- T3  = 3.3858 Angstrom
T4  has 5 neighboring T-atoms within 3.50 A, but only 4 bridging O-atoms
  T4  -- T3  = 3.0458 Angstrom
  T4  -- T3  = 2.9436 Angstrom
  T4  -- T4  = 2.9373 Angstrom
  T4  -- T5  = 3.1583 Angstrom
  T4  -- T1  = 3.3607 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 18 29 46 70 100 132 171 216 258 302 362 438 508 569
TD10 = 797
Circuit symbol = 4.5.4.5_{2}.6_{2}.7_{3}
Weight = 11
Vertex symbol  = 4.5.4.5_{2}.10_{2}.*
Weight = 19

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 21 31 43 63 96 135 169 202 247 306 367 423 486 565
TD10 = 776
Circuit symbol = 4.6_{2}.5.6.6.6_{2}
Weight = 21
Vertex symbol  = 4.6_{2}.5.6.6.6_{2}
Weight = 21

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 18 35 58 77 103 142 187 230 272 322 383 450 522 599
TD10 = 865
Circuit symbol = 4.5.4.6.5_{2}.6
Weight = 12
Vertex symbol  = 4.5.4.6.5_{2}.10
Weight = 19

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 20 34 53 80 109 137 176 223 276 327 381 450 515 577
TD10 = 847
Circuit symbol = 4.6.4.6_{2}.5.6
Weight = 14
Vertex symbol  = 4.6_{2}.4.10_{3}.5.12
Weight = 34

T5 (Si): multiplicity = 18
Coordination Sequence =
    1 4 12 20 30 48 72 104 136 166 210 258 314 376 430 492 572
TD10 = 803
Circuit symbol = 5.5.6.6.6_{2}.9_{4}
Weight = 19
Vertex symbol  = 5.5.6.6.6_{2}.10_{3}
Weight = 32

<TD10> = 819.222
Average ring size = 5.7105