Output from "TOTOPOL", (version 1.92, 17 Jul 2017, Mike Treacy).

Report for the framework in file "public/tmp/tmp_166_5_84778879_dnGaq5.cif"

There are 162 T-atoms per unit cell
There are 324 O-atoms per unit cell

Framework density = 23.67 T-atoms per nm^3
Material density = 2.361 grams per cm^3 (excluding extra-framework material)
-------------------------------------------------------------------
-------------------------- T-O Analysis ---------------------------
-------------------------------------------------------------------
[Si] Ideal SiO distance = 1.610 Angstrom
T1  -- O1  = 1.6151 Angstrom
T1  -- O2  = 1.6097 Angstrom
T1  -- O3  = 1.5912 Angstrom
T1  -- O4  = 1.6012 Angstrom
      mean = 1.6043 Angstrom
        t1 = 0.017841  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.011064  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T2  -- O5  = 1.6152 Angstrom
T2  -- O6  = 1.5933 Angstrom
T2  -- O7  = 1.5454 Angstrom
T2  -- O4  = 1.6209 Angstrom
      mean = 1.5937 Angstrom
        t1 = 0.036551  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.022463  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T3  -- O6  = 1.6423 Angstrom
T3  -- O8  = 1.6240 Angstrom
T3  -- O9  = 1.6436 Angstrom
T3  -- O10 = 1.6267 Angstrom
      mean = 1.6341 Angstrom
        t1 = 0.026715  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.014609  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T4  -- O10 = 1.6377 Angstrom
T4  -- O11 = 1.7244 Angstrom
T4  -- O12 = 1.7182 Angstrom
T4  -- O13 = 1.6731 Angstrom
      mean = 1.6883 Angstrom
        t1 = 0.066408  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.030462  (0.0 is a perfect tetrahedron)

[Si] Ideal SiO distance = 1.610 Angstrom
T5  -- O7  = 1.6070 Angstrom
T5  -- O13 = 1.6367 Angstrom
T5  -- O7  = 1.6070 Angstrom
T5  -- O13 = 1.6367 Angstrom
      mean = 1.6218 Angstrom
        t1 = 0.036740  (0.0 is a perfect SiO4 tetrahedron)
        t2 = 0.043895  (0.0 is a perfect tetrahedron)

        T-O SUMMARY
          Range  = 1.5454 A <--> 1.7244 A
          Mean   = 1.6292 A
          StdDev = 0.0417 A

       t1 Range  = 0.0178 <-- 0.0369 --> 0.0664
       t2 Range  = 0.0111 <-- 0.0245 --> 0.0439

-------------------------------------------------------------------
------------------------- O-T-O Analysis --------------------------
-------------------------------------------------------------------
O1  -- T1  -- O2  = 109.437 deg; O1  -- O2  = 3 A
O1  -- T1  -- O3  = 109.523 deg; O1  -- O3  = 3 A
O1  -- T1  -- O4  = 113.815 deg; O1  -- O4  = 3 A
O2  -- T1  -- O3  = 110.106 deg; O2  -- O3  = 3 A
O2  -- T1  -- O4  = 108.543 deg; O2  -- O4  = 3 A
O3  -- T1  -- O4  = 105.327 deg; O3  -- O4  = 3 A
       105.327 deg <-- 109.459 deg --> 113.815 deg

O5  -- T2  -- O6  = 111.596 deg; O5  -- O6  = 3 A
O5  -- T2  -- O7  = 111.427 deg; O5  -- O7  = 3 A
O5  -- T2  -- O4  = 111.230 deg; O5  -- O4  = 3 A
O6  -- T2  -- O7  = 101.738 deg; O6  -- O7  = 2 A
O6  -- T2  -- O4  = 114.316 deg; O6  -- O4  = 3 A
O7  -- T2  -- O4  = 106.009 deg; O7  -- O4  = 3 A
       101.738 deg <-- 109.386 deg --> 114.316 deg

O6  -- T3  -- O8  = 113.263 deg; O6  -- O8  = 3 A
O6  -- T3  -- O9  = 107.435 deg; O6  -- O9  = 3 A
O6  -- T3  -- O10 = 106.128 deg; O6  -- O10 = 3 A
O8  -- T3  -- O9  = 107.913 deg; O8  -- O9  = 3 A
O8  -- T3  -- O10 = 106.788 deg; O8  -- O10 = 3 A
O9  -- T3  -- O10 = 115.492 deg; O9  -- O10 = 3 A
       106.128 deg <-- 109.503 deg --> 115.492 deg

O10 -- T4  -- O11 = 110.334 deg; O10 -- O11 = 3 A
O10 -- T4  -- O12 = 107.577 deg; O10 -- O12 = 3 A
O10 -- T4  -- O13 =  99.877 deg; O10 -- O13 = 3 A
O11 -- T4  -- O12 = 118.716 deg; O11 -- O12 = 3 A
O11 -- T4  -- O13 = 108.425 deg; O11 -- O13 = 3 A
O12 -- T4  -- O13 = 110.273 deg; O12 -- O13 = 3 A
       99.877 deg <-- 109.200 deg --> 118.716 deg

O7  -- T5  -- O13 = 106.544 deg; O7  -- O13 = 3 A
O7  -- T5  -- O7  = 101.387 deg; O7  -- O7  = 2 A
O7  -- T5  -- O13 = 112.168 deg; O7  -- O13 = 3 A
O13 -- T5  -- O7  = 112.168 deg; O13 -- O7  = 3 A
O13 -- T5  -- O13 = 116.990 deg; O13 -- O13 = 3 A
O7  -- T5  -- O13 = 106.544 deg; O7  -- O13 = 3 A
       101.387 deg <-- 109.300 deg --> 116.990 deg

        O-T-O SUMMARY
          Range  = 99.8770 deg <--> 118.7158 deg
          Mean   = 109.2087 deg
          StdDev = 4.3116 deg

        O--O SUMMARY
          Range  = 2.4349 A <--> 2.9619 A
          Mean   = 2.6526 A
          StdDev = 0.0985 A

-------------------------------------------------------------------
------------------------- T-T-T Analysis --------------------------
-------------------------------------------------------------------
T1  - O1  - T1  - O2  - T1  =  89.871 deg; T1  -- T1  = 4.1760 A
T1  - O1  - T1  - O3  - T1  =  90.129 deg; T1  -- T1  = 4.1760 A
T1  - O1  - T1  - O4  - T2  = 149.115 deg; T1  -- T2  = 5.8788 A
T1  - O2  - T1  - O3  - T1  = 120.000 deg; T1  -- T1  = 4.7689 A
T1  - O2  - T1  - O4  - T2  =  91.600 deg; T1  -- T2  = 4.1026 A
T1  - O3  - T1  - O4  - T2  = 115.407 deg; T1  -- T2  = 4.8239 A

T2  - O5  - T2  - O6  - T3  = 122.936 deg; T2  -- T3  = 5.0257 A
T2  - O5  - T2  - O7  - T5  = 128.073 deg; T2  -- T5  = 5.0821 A
T2  - O5  - T2  - O4  - T1  =  88.400 deg; T2  -- T1  = 4.1026 A
T3  - O6  - T2  - O7  - T5  =  95.127 deg; T3  -- T5  = 4.0745 A
T3  - O6  - T2  - O4  - T1  = 126.698 deg; T3  -- T1  = 5.1426 A
T5  - O7  - T2  - O4  - T1  =  95.740 deg; T5  -- T1  = 4.2191 A

T2  - O6  - T3  - O8  - T3  = 112.723 deg; T2  -- T3  = 5.0366 A
T2  - O6  - T3  - O9  - T3  = 117.587 deg; T2  -- T3  = 4.6973 A
T2  - O6  - T3  - O10 - T4  =  79.533 deg; T2  -- T4  = 3.7334 A
T3  - O8  - T3  - O9  - T3  =  90.000 deg; T3  -- T3  = 4.2217 A
T3  - O8  - T3  - O10 - T4  =  86.827 deg; T3  -- T4  = 4.3206 A
T3  - O9  - T3  - O10 - T4  = 162.322 deg; T3  -- T4  = 5.6644 A

T3  - O10 - T4  - O11 - T4  =  83.639 deg; T3  -- T4  = 4.3206 A
T3  - O10 - T4  - O12 - T4  = 115.899 deg; T3  -- T4  = 5.3824 A
T3  - O10 - T4  - O13 - T5  =  91.321 deg; T3  -- T5  = 4.3092 A
T4  - O11 - T4  - O12 - T4  = 138.552 deg; T4  -- T4  = 6.3066 A
T4  - O11 - T4  - O13 - T5  =  84.655 deg; T4  -- T5  = 4.3351 A
T4  - O12 - T4  - O13 - T5  = 127.823 deg; T4  -- T5  = 5.6626 A

T2  - O7  - T5  - O13 - T4  = 108.709 deg; T2  -- T4  = 4.6477 A
T2  - O7  - T5  - O7  - T2  = 103.853 deg; T2  -- T2  = 4.2921 A
T2  - O7  - T5  - O13 - T4  =  97.245 deg; T2  -- T4  = 4.2928 A
T4  - O13 - T5  - O7  - T2  =  97.245 deg; T4  -- T2  = 4.2928 A
T4  - O13 - T5  - O13 - T4  = 137.513 deg; T4  -- T4  = 5.5737 A
T2  - O7  - T5  - O13 - T4  = 108.709 deg; T2  -- T4  = 4.6477 A

        T-T-T SUMMARY
          Range  = 79.5333 deg <--> 162.3217 deg
          Mean   = 108.8355 deg
          StdDev = 20.9102 deg

        T--T SUMMARY
          Range  = 3.7334 A <--> 6.3066 A
          Mean   = 4.7086 A
          StdDev = 0.6057 A

-------------------------------------------------------------------
------------------------- T-O-T Analysis --------------------------
-------------------------------------------------------------------
T1  -- O1  -- T1  = 152.845 deg ; T1  -- T1   3.1398 A

T1  -- O2  -- T1  = 118.061 deg ; T1  -- T1   2.7604 A

T1  -- O3  -- T1  = 119.299 deg ; T1  -- T1   2.7463 A

T1  -- O4  -- T2  = 133.373 deg ; T1  -- T2   2.9590 A

T2  -- O5  -- T2  = 129.821 deg ; T2  -- T2   2.9256 A

T2  -- O6  -- T3  = 119.444 deg ; T2  -- T3   2.7944 A

T2  -- O7  -- T5  = 119.700 deg ; T2  -- T5   2.7261 A

T3  -- O8  -- T3  = 178.785 deg ; T3  -- T3   3.2477 A

T3  -- O9  -- T3  = 110.276 deg ; T3  -- T3   2.6972 A

T3  -- O10 -- T4  = 136.781 deg ; T3  -- T4   3.0350 A

T4  -- O11 -- T4  = 167.935 deg ; T4  -- T4   3.4297 A

T4  -- O12 -- T4  = 149.228 deg ; T4  -- T4   3.3130 A

T4  -- O13 -- T5  = 129.215 deg ; T4  -- T5   2.9900 A


        T-O-T SUMMARY
          Range  = 110.2756° <--> 178.7855 deg
          Mean   = 135.7510 deg
          StdDev = 20.0260 deg

        T--T SUMMARY
          Range  = 2.6972 A <--> 3.4297 A
          Mean   = 2.9819 A
          StdDev = 0.2321 A

-------------------------------------------------------------------
------------------------ *** WARNINGS *** -------------------------
-------------------------------------------------------------------
T1  -- T1  = 2.7604 Angstrom
T1  -- T1  = 2.7463 Angstrom
T2  -- T3  = 2.7944 Angstrom
T2  -- T5  = 2.7261 Angstrom
T3  -- T2  = 2.7944 Angstrom
T3  -- T3  = 2.6972 Angstrom
T5  -- T2  = 2.7261 Angstrom
T5  -- T2  = 2.7261 Angstrom

-------------------------------------------------------------------
---------------------- Topological Analysis -----------------------
-------------------------------------------------------------------
T1 (Si): multiplicity = 36
Coordination Sequence =
    1 4 9 18 33 54 85 127 179 228 274 331 411 505 596 688 783
TD10 = 1012
Circuit symbol = 4.4.4.6.6.6_{2}
Weight = 14
Vertex symbol  = 4.4.4.6.6.8
Weight = 19

T2 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 22 38 62 94 136 179 230 293 360 429 506 600 692 784
TD10 = 1070
Circuit symbol = 4.5_{2}.6.6.6.8_{3}
Weight = 24
Vertex symbol  = 4.5_{2}.6.6.6.8_{2}
Weight = 24

T3 (Si): multiplicity = 36
Coordination Sequence =
    1 4 10 20 39 68 99 134 178 232 298 366 434 514 601 693 791
TD10 = 1083
Circuit symbol = 4.5.4.6.5.6
Weight = 11
Vertex symbol  = 4.5.4.6.5.8
Weight = 16

T4 (Si): multiplicity = 36
Coordination Sequence =
    1 4 11 25 47 76 113 151 198 256 314 380 453 535 625 713 813
TD10 = 1196
Circuit symbol = 4.8_{3}.5.6.5.7
Weight = 22
Vertex symbol  = 4.8_{3}.5.6.5.8
Weight = 26

T5 (Si): multiplicity = 18
Coordination Sequence =
    1 4 12 25 42 64 104 139 190 238 306 366 438 527 614 703 798
TD10 = 1125
Circuit symbol = 5_{2}.5_{2}.6.8_{2}.8_{4}.8_{4}
Weight = 40
Vertex symbol  = 5_{2}.5_{2}.6.8_{2}.8_{4}.8_{4}
Weight = 40

<TD10> = 1094.111
Average ring size = 5.7028